Selective interfacial bonding and thermal conductivity of diamond/Cu-alloy composites prepared by HPHT technique

Abstract

Cu-based and Cu-alloy-based diamond composites were made by high-pressure-high-temperature (HPHT) sintering with the aim of maximizing the thermal conductivity of the composites. Improvements in interfacial bonding strength and thermo-physical properties of the composites were achieved using an atomized copper alloy with minor additions of Co, Cr, B, and Ti. The thermal conductivity (TC) obtained exhibited as high as 688 W·m⁻¹·K⁻¹, but also as low as 325 W·m⁻¹·K⁻¹. A large variation in TC can be rationalized by the discrepancy of diamond-matrix interfacial bonding. It was found from fractography that preferential bonding between diamond and the Cu-alloy matrix occurred only on the diamond {100} faces. EDS analysis and Raman spectra suggested that selective interfacial bonding may be attributed to amorphous carbon increasing the wettability between diamond and the Cu-alloy matrix. Amorphous carbon was found to significantly affect the TC of the composite by interface modification.

Keywords

metallic matrix composites / diamonds / copper alloys / interfacial bonding / thermal conductivity

References

[1] Zweben C. Thermal materials solve power electronics challenges. Power Electron. Technol., 2006, 40, 40.

[2] Chen H., Jia C.C., Chu K., Liang X.B., Liu Z.F., Guo H. Research on increasing thermal conductivity of diamond/copper composites by improving interface condition. Powder Metall. Technol., 2010, 28(2): 143.

[3] Schubert T., Ciupiński Zieliński W., Michalski A., Weiβgärber T., Kieback B. Interfacial characterization of Cu/diamond composites prepared by powder metallurgy for heat sink applications. Scripta Mater., 2008, 58(4): 263

[4] Schubert T., Trindade B., Weiβgärber T., Kieback B. Interfacial design of Cu-based composites prepared by powder metallurgy for heat sink applications. Mater. Sci. Eng. A, 2008, 475(1–2): 39

[5] Weber L., Tavangar R. On the influence of active element content on the thermal conductivity and thermal expansion of Cu-X (X=Cr, B) diamond composites. Scripta Mater., 2007, 57(11): 988

[6] Xia Y., Song Y.Q., Lin C.G., Cui S., Fang Z.Z. Effect of carbide formers on microstructure and thermal conductivity of diamond-Cu composites for heat sink materials. Trans. Nonferrous Met. Soc. China, 2009, 19(5): 1161

[7] Yin F.Z., Guo H., Zhang X.M., Fan Y.M., Zhang Y.Z. Effect of Ti on microstructure and properties of diamond/copper composites. Acta Mater. Compos. Sin., 2010, 27(3): 138.

[8] Wang Y., Alsmeyer D.C., McCreery R.L. Raman spectroscopy of carbon materials: structural basis of observed spectra. Chem. Mater., 1990, 2(5): 557

[9] Robertson J., O’Reilly E.P. Electronic and atomic structure of amorphous carbon. Phys. Rev. B, 1987, 35(6): 2946

[10] Hasselman D.P.H., Johnson L.F. Effective thermal conductivity of composites with interfacial thermal barrier resistance. J. Compos. Mater., 1987, 21(6): 508

[11] Chu K., Liu Z.F., Jia C.C., Chen H., Liang X.B., Gao W.J., Tian W.H., Guo H. Thermal conductivity of SPS consolidated Cu/diamond composites with Cr-coated diamond particles. J. Alloys Compd., 2009, 490(1–2): 453.

[12] Ruch P.W., Beffort O., Kleiner S., Weber L., Uggowitzer P.J. Selective interfacial bonding in Al(Si)-diamond composites and its effect on thermal conductivity. Compos. Sci. Technol., 2006, 66, 2677