Electro-deoxidation of V₂O₃ in molten CaCl₂-NaCl-CaO

Abstract

The electro-deoxidation of V₂O₃ precursors was studied. Experiments were carried out with a two-terminal electrochemical cell, which was comprised of a molten electrolyte of CaCl₂ and NaCl with additions of CaO, a cathode of compact V₂O₃, and a graphite anode under the potential of 3.0 V at 1173 K. The phase constitution and composition as well as the morphology of the samples were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM). 3 g of V₂O₃ could be converted to vanadium metal powder within the processing time of 8 h. The kinetic pathway was investigated by analyzing the product phase in samples prepared at different reduction stages. CaO added in the reduction path of V₂O₃ formed the intermediate product CaV₂O₄.

Keywords

vanadous oxide / electro-deoxidation / vanadium / molten salt / electrochemical cells

References

[1] Suzuki R.O., Ishikawa H. Direct reduction of vanadium oxide in molten CaCl₂. ECS Trans., 2007, 3, 347.

[2] Ono K., Suzuki R.O. A new concept of sponge titanium production by calciothermic reduction of titanium dioxide in molten calcium chloride. JOM, 2002, 54, 59

[3] Suzuki R.O., Tatemoto K., Kitagawa H. Direct synthesis of the hydrogen storage V-Ti alloy powder from the oxides by calcium Co-reduction. J. Alloys Compd., 2004, 385, 173

[4] Baba M., Ono Y., Suzuki R.O. Tantalum and niobium powder preparation from their oxides by calciothermic reduction in the molten CaCl₂. J. Phys. Chem. Solids, 2004, 66, 466

[5] D.J. Fray, T.W. Farthing, and Z. Chen, Removal of Oxygen from Metal Oxides and Solid Solutions by Electrolysis in a Fused Salt, World Patent, Appl.9964638, 1999.

[6] Chen G.Z., Fray D.J., Farthing T.W. Direct electrochemical reduction of titanium dioxide to titanium in molten calcium chloride. Nature, 2000, 407, 361

[7] Fray D.J. Emerging molten salt technologies for metals production. JOM, 2001, 53, 26

[8] Chen G.Z., Gordo E., Fray D.J. Direct electrolytic preparation of chromium powder. Metall. Mater. Trans. B, 2004, 35, 223

[9] Yan X.Y., Fray D.J. Using electro-deoxidation to synthesize niobium sponge from solid Nb2O5 in alkali-alkaline-earth metal chloride melts. J. Mater. Res., 2003, 18, 346

[10] Pistorius P.C., Fray D.J. Formation of silicon by electro-deoxidation, and implications for titanium metal production. J. S. Afr. Inst. Min. Metall., 2006, 106, 31.

[11] Peng J.J., Chen H.L., Jin X.B., Wang T., Wang D.H., Chen G.Z. Phase-tuneable fabrication of consolidated (α+β)-TiZr alloys for biomedical applications through molten salt electrolysis of solid oxides. Chem. Mater., 2009, 21, 5187

[12] Jiao S.Q., Zhang L.L., Zhu H.M., Fray D.J. Production of NiTi shape memory alloys via electro-deoxidation utilizing an inert anode. Electrochim. Acta, 2010, 55, 7016

[13] Yan X.Y., Fray D.J. Synthesis of niobium aluminides by electro-deoxidation of oxides. J. Alloys Compd., 2009, 486, 154

[14] Chen G.Z., Fray D.J. Voltammetric studies of the oxygen-titanium binary system in molten calcium chloride. J. Electrochem. Soc., 2002, 149, E455

[15] Wang S.L., Li Y.J. Reaction mechanism of direct electro-reduction of titanium dioxide in molten calcium chloride. J. Electroanal. Chem., 2004, 571, 37

[16] Wang S.L., Wang W., Li S.C., Cao S.H. Cathodic behavior of molten CaCl₂-CaO and CaCl₂-NaCl-CaO. Int. J. Miner. Metall. Mater., 2010, 17(6): 791

[17] Schwandt C., Fray D.J. Determination of the kinetic pathway in the electrochemical reduction of titanium dioxide in molten calcium chloride. Electrochim. Acta, 2005, 51, 66

[18] Alexander D.T.L., Schwandt C., Fray D.J. Microstructural kinetics of phase transformations during electrochemical reduction of titanium dioxide in molten calcium. Acta Mater., 2006, 54, 2933

[19] Xiao W., Jin X.B., Deng Y., Wang D.H., Hu X.H., Chen G.Z. Electrochemically driven three-phase interlines into insulator compounds: electroreduction of solid SiO₂ in molten CaCl₂. Chem. Phys. Chem., 2006, 7, 1750

[20] Wang D.H., Qiu G.H., Jin X.B., Hu X.H., Chen G.Z. Electrochemical metallization of solid terbium oxide. Angew. Chem. Int. Ed., 2006, 45, 2384

[21] Schwandt C., Alexander D.T.L., Fray D.J. The electro-deoxidation of porous titanium dioxide precursors in molten calcium chloride under cathodic potential control. Electrochim. Acta, 2009, 54, 3819

[22] Kubaschewski O., Alcock C.B., Spencer P.J. Materials Thermochemistry, 1993, Oxford, Pergamon, 46.

[23] Maeda M., Mclean A. Dissolution of carbon dioxide in CaO-CaCl₂ melts. Iron Steel Maker, 1986, 13, 61.