Activation pretreatment of limonitic laterite ores by alkali-roasting using NaOH

Abstract

Activation pretreatment of Cr-containing limonitic laterite ores by NaOH roasting to remove Cr, Al, and Si, as well as its effect on Ni and Co extraction in the subsequent pressure acid leaching process was investigated. Characterization results of X-ray diffraction (XRD) and scanning electron microscopy/X-ray energy dispersive spectroscopy (SEM/XEDS) show that goethite is the major Ni-bearing mineral, and chromite is the minor one. Experimental results show that the leaching rates of Cr, Al, and Si are 95.6wt%, 83.8wt%, and 40.1wt%, respectively, under the optimal alkali-roasting conditions. Compared with the direct pressure acid leaching of laterite ores, the leaching rates of Ni and Co increase from 80.1wt% to 96.9wt% and 70.2wt% to 95.1wt% after pretreatment, respectively. Meanwhile, the grade of acid leaching iron residues increases from 54.4wt% to 62.5wt%, and these residues with low Cr content are more suitable raw materials for iron making.

Keywords

laterite ores / sodium hydroxide / roasting / activation / pretreatment / pressure acid leaching

References

[1] Landers M., Gilkes R.J., Wells M. Dissolution kinetics of dehydroxylated nickeliferous goethite from limonitic lateritic nickel ore. Appl. Clay Sci., 2009, 42, 615

[2] Luo W., Feng Q.M., Ou L.M., Zhang G.F., Chen Y. Kinetics of saprolitic laterite leaching by sulphuric acid at atmospheric pressure. Miner. Eng., 2010, 23, 458

[3] Loveday B.K. The use of oxygen in high pressure acid leaching of nickel laterites. Miner. Eng., 2008, 21, 533

[4] Brand N.W., Butt C.R.M., Elias M. Nickel laterites: classification and features. AGSO J. Aust. Geol. Geophys., 1998, 17, 81.

[5] Swamy Y.V., Kar B.B., Mohanty J.K. Physico-chemical characterization and sulphatization roasting of low-grade nickeliferous laterites. Hydrometallurgy, 2003, 69, 89

[6] Deepatana A., Tang J.A., Valix M. Comparative study of chelating ion exchange resins for metal recovery from bioleaching of nickel laterite ores. Miner. Eng., 2006, 19, 1280

[7] Kotzé I.J. Pilot plant production of ferronickel from nickel oxide ores and dusts in a DC arc furnace. Miner. Eng., 2002, 15, 1017

[8] Valix M., Cheung W.H. Study of phase transformation of laterite ores at high temperature. Miner. Eng., 2002, 15, 607

[9] Whittington B.I., McDonald R.G., Johnson J.A., Muir D.M. Pressure acid leaching of Bulong nickel laterite ore: Part I. Effect of water quality. Hydrometallurgy, 2003, 70, 31

[10] McDonald R.G., Whittington B.I. Atmospheric acid leaching of nickel laterites review: Part I. Sulphuric acid technologies. Hydrometallurgy, 2008, 91, 35

[11] Owada S., Harada T. Mineralogical properties and fundamental mineral processing behaviour of the chromite contained in laterite leach residue. Int. J. Miner. Process., 1987, 19, 77

[12] Stamboliadis E., Alevizos G., Zafiratos J. Leaching residue of nickeliferous laterites as a source of iron concentrate. Miner. Eng., 2004, 17, 245

[13] S.T. Dong, C.Y. Wang, T. Qi, et al., A Treatment Processing for the Limonitic Nickeliferous Laterite Ores by Alkali-acid Circulation, Chinese Patent, Appl.0910180397.6, 2009.

[14] T. Qi, J.K. Qu, S.T. Dong, et al., A Clean Production Technology for Low-grade Nickeliferous Laterite Ores by Alkali-roasting Method Using Sodium Hydroxide, Chinese Patent, Appl.0910082369.0, 2009.

[15] J.K. Qu, T. Qi, S.T. Dong, et al., A Method for Chrome Oxide Preparation from Nickeliferous Laterite Ores, Chinese Patent, Appl.0910223300.5, 2009.

[16] Guo Q., Qu J.K., Han B.B., Wei G.Y., Qi T. Thermodynamic analysis and experimental study on alkali-roasting treatment of limonitic laterite ore with sodium carbonate. Chin. J. Process Eng., 2011, 11(1): 72.