Effect of magnesium and nickel coatings on the wetting behavior of alumina toughened zirconia by molten Al-Mg alloy

Abstract

The wettability of alumina toughened zirconia (ZTA) by Al-Mg alloy was investigated using the sessile drop technique. The effects of nickel coating, magnesium content, nitrogen atmosphere, and processing temperature on the contact angle between the molten alloy and the substrate were determined. Likewise, the effect of these factors on the wetting properties was studied. The results showed that the nickel coating on the ceramic substrate caused a significant reduction in solid/liquid surface energy and the contact angle decreased obviously. The presence of magnesium in the molten aluminum alloy in nitrogen atmosphere reduced the contact angle effectively. The presence of magnesium in the alloy must be at a minimum amount of 2wt%–3wt%. Moreover, it was suggested that some chemical reactions in the Al-Mg-N system led to the production of Mg₃N₂ and AlN compositions. These compositions improved the wetting properties of the systems by reducing the surface energy of the molten. It was shown that increasing the temperature is also an effective factor for the enhancement of wetting properties.

Keywords

wetting / coatings / alumina / zirconia / ceramic materials / composite materials

References

[1] Nakashima K., Matsumoto H., Mori K. Effect of additional elements Ni and Cr on wetting characteristics of liquid Cu on zirconia ceramics. Acta Mater., 2000, 48, 4677

[2] Yu Z.Q., Wu G.H., Sun D.L., Jiang L.T. Coating of Y₂O₃ additive on Al₂O₃ powder and its effect on the wetting behavior in the system Al₂O_3p/Al. Mater. Lett., 2003, 57, 3111

[3] Pech-Canul M.I., Katz R.N., Makhlouf M.M. Optimum parameters for wetting silicon carbide by aluminum alloys. Metall. Mater. Trans. A, 2000, 31, 565

[4] Nogi K. The role of wettability in metal-ceramic joining. Scripta Mater., 2010, 62, 945

[5] Sang K., Weiler L., Aulbach E. Wetting and pressureless infiltration in the CuTi/Al₂O₃ system under poor vacuum. Ceram. Int., 2010, 36, 719

[6] Durov A.V., Naidich Y.V., Kostyuk B.D. Investigation of interaction of metal melts and zirconia. J. Mater. Sci., 2005, 40, 2173

[7] Konopka K., Szafran M. Fabrication of Al₂O₃-Al composites by infiltration method and their characteristic. J. Mater. Process. Technol., 2006, 175, 266

[8] Bahraini M., Molina J.M., Kida M., Weber L., Narciso J., Mortensen A. Measuring and tailoring capillary forces during liquid metal infiltration. Curr. Opin. Solid State Mater. Sci., 2005, 9, 196

[9] Liu G.W., Muolo M.L., Valenza F., Passerone A. Survey on wetting of SiC by molten metals. Ceram. Int., 2010, 36, 1177

[10] Michauda V., Mortensen A. On measuring wettability in infiltration processing. Scripta Mater., 2007, 56, 859

[11] Bahraini M., Minghetti T., Zoellig M., Schubert J., Berroth K., Schelle C., Graule T., Kuebler J. Activated pressureless infiltration of metal-matrix composites with graded activator content. Compos. Part A, 2009, 40, 1566

[12] Ouyang Q.B., Zhou W.M., Zhang G.D., Zhang D. Wettability at Al-Mg/ceramic interfaces. Key Eng. Mater., 2006, 313, 159

[13] Chen J., Gu M., Pan F. Reactive wetting of a metal/ceramic system. J. Mater. Res., 2002, 17, 911

[14] Kalogeropoulou S., Rado C., Eustathopoulos N. Mechanisms of reactive wetting: The wetting to non-wetting case. Scripta Mater., 1999, 41, 723

[15] Witting D., Glauche A., Aneziris C.G., Minghetti T., Schelle C., Graule T., Kuebler J. Activated pressureless melt infiltration of zirconia-based metal matrix composites. Mater. Sci. Eng. A, 2008, 488, 580

[16] Kennedy A.R., Brapton B. The reactive wetting and incorporation of B4C particles into molten aluminum. Scripta Mater., 2001, 44, 1077

[17] Aghajanian M.K., MacMillan N.H., Kennedy C.R., Luszcz S.J., Roy R. Properties and microstructures of Lanxide® Al₂O₃-Al ceramic composite materials. J. Mater. Sci., 1989, 24, 658

[18] Sharifi H., Divandari M., Khavandi A., Idris M.H. Effect of Al powder and silica sol on the structure and mechanical properties of Al₂O₃-ZrO₂ foams. Acta Metall. Sin. Engl. Lett., 2010, 23, 241.

[19] Aghajanian M.K., Rocazella M.A., Burke J.T., Keck S.D. The fabrication of metal matrix composites by a pressureless infiltration technique. J. Mater. Sci., 1991, 26, 447

[20] Corbin S.F., Zhao-jie X., Henein H., Apte P.S. Functionally graded metal/ceramic composites by tape casting, lamination and infiltration. Mater. Sci. Eng. A, 1999, 262, 192