Effects of submicron diamonds on the growth of copper in Cu-diamond co-deposition

Abstract

Submicron diamonds were co-deposited on aluminum substrates with copper from the acid copper sulfate electrolyte by electrolyte-suspension co-deposition. After submicron diamonds were added to the electrolyte, the shape of copper grains transformed from oval or round to polyhedron, the growth mode of copper grains transformed from columnar growth to gradual change in size, and the preferred orientation of copper grains transformed from (220) to (200). Analyzing the variation of cathodic overpotential, it was found that the cathodic overpotential tended to remain unchanged when copper plane (220) grew in the process of electrodepositing pure copper, while it tended to decrease with time when copper plane (200) grew in the process of co-deposition. It was inferred that copper plane (200) was propitious to the deposition of submicron diamonds.

Keywords

composite coatings / copper / diamond / co-deposition / gradient materials / grain growth

References

[1] Schubert T., Trindade B., Weißgärber T., Kieback B. Interfacial design of Cu-based composites prepared by powder metallurgy for heat sink applications. Mater. Sci. Eng. A, 2008, 475(1–2): 39

[2] Ruch P.W., Beffort O., Kleiner S., Weber L., Uggowitzer P.J. Selective interfacial bonding in Al(Si)-diamond composites and its effect on thermal conductivity. Compos. Sci. Technol., 2006, 66(15): 2677

[3] Ekimov E.A., Suetin N.V., Popovich A.F., Ralchenko V.G. Thermal conductivity of diamond composites sintered under high pressures. Diamond Relat. Mater., 2008, 17(4–5): 838

[4] Battabyal M., Beffort O., Kleiner S., Vaucher S., Rohr L. Heat transport across the metal-diamond interface. Diamond Relat. Mater., 2008, 17(7–10): 1438

[5] Shao W.Z., Ivanov V.V., Zhen L., Cui Y.S., Wang Y. A study on graphitization of diamond in copper-diamond composite materials. Mater. Lett., 2004, 58(1–2): 146

[6] Medeliene V., Stankevıc V., Bikulčius G. The influence of artificial diamond additions on the formation and properties of an electroplated copper metal matrix coating. Surf. Coat. Technol., 2003, 168(2–3): 161

[7] Li Y.D., Zhao A.Q., Wang B.A., Li J.W., Wu F.H. Matrix microstructure deteriorations resulting from diamond incorporation in electroplated metal-diamond composites. Surf. Coat. Technol., 2008, 202(8): 1357

[8] Pushpavanam M., Manikandan H., Ramanathan K. Preparation and characterization of nickel-cobalt-diamond electro-composites by sediment co-deposition. Surf. Coat. Technol., 2007, 201(14): 6372

[9] Shrestha N.K., Takebe T., Saji T. Effect of particle size on the co-deposition of diamond with nickel in presence of a redox-active surfactant and mechanical property of the coatings. Diamond Relat. Mater., 2006, 15(10): 1570

[10] Liao Q., Zhu L.Q., Liu H.C., Li W.P. Mechanical properties of electroformed copper layers with gradient microstructure. Int. J. Miner. Metall. Mater., 2010, 17(1): 69

[11] Xu X.Q., Zhu L.Q., Li W.P., Liu H.C. A variable hydrophobic surface improves corrosion resistance of electroplating copper coating. Appl. Surf. Sci., 2011, 257(13): 5524

[12] Matsushima H., Bund A., Plieth W., Kikuchi S., Fukunaka Y. Copper electrodeposition in a magnetic field. Electrochim. Acta, 2007, 53(1): 161

[13] El-Sherik A.M., Erb U. Synthesis of bulk nanocrystalline nickel by pulsed electrodeposition. J. Mater. Sci., 1995, 30(22): 5743

[14] El-Sherik A.M., Erb U., Page J. Microstructural evolution in pulse plated nickel electrodeposits. Surf. Coat. Technol., 1997, 88(1–3): 70