Effects of Si on the stability of retained austenite and temper embrittlement of ultrahigh strength steels

Abstract

Effects of silicon (Si) content on the stability of retained austenite and temper embrittlement of ultrahigh strength steels were investigated using X-ray diffraction (XRD), transmission electron microscopy (TEM), and other experimental methods. The results show that Si can suppress temper embrittlement, improve temper resistance, and hinder the decomposition of retained austenite. Reversed austenite appears gradually with the increase of Si content during tempering. Si has a significant effect on enhancing carbon (C) partitioning and improving the stability of retained austenite. Si and C atoms are mutually exclusive in lath bainite, while they attract each other in austenite. ɛ-carbides are found in 1.8wt% Si steel tempered at 250°C, and they get coarsened obviously when tempered at 400°C, leading to temper embrittlement. Not ɛ-carbides but acicular or lath carbides lead to temper embrittlement in 0.4wt% Si steel, which can be inferred as cementites and composite compounds. Temper embrittlement is closely related to the decomposition of retained austenite and the formation of reversed austenite.

Keywords

silicon / ultrahigh strength steel / retained austenite / temper embrittlement / reversed austenite

References

[1] Garrison W.M., Maloney J.L. Lanthanum additions and the toughness of ultra-high strength steels and the determination of appropriate lanthanum additions. Mater. Sci. Eng. A, 2005, 403, 299.

[2] Li J., Guo F., Li Z., Wang J.L., Yan M.G. Influence of sizes of inclusions and voids on fracture toughness of ultra-high strength steel AerMet100. J. Iron Steel Res. Int., 2007, 14, 254.

[3] Pancholi V., Krishnan M., Samajdar I.S., et al. Self-accommodation in the bainitic microstructure of ultra-high-strength steel. Acta Mater., 2008, 56(9): 2037.

[4] Fan C.G., Dong H., Shi J., et al. Microstructure and mechanical properties of 2200 MPa grade ultra-high strength low alloy steels. Ordnance Mater. Sci. Eng., 2006, 29(2): 31.

[5] Wang L.D., Ding F.C., Wang B.M., et al. Influence of super-fine substructure on toughness of low-alloying ultra-high strength structure steel. Acta Metall. Sin., 2009, 45(3): 292.

[6] Gao K., Wang L.D., Zhu M., et al. Refinement of grain and enhancement of impact toughness for low-alloying ultra-high strength bainite steels. Acta Metall. Sin., 2007, 43(3): 315.

[7] Scott C.P., Drillet J. A study of the carbon distribution in retained austenite. Scripta Mater., 2007, 56, 489.

[8] Yaso M., Morito S., Ohba T., et al. Microstructure of martensite in Fe-C-Cr steel. Mater. Sci. Eng. A, 2008, 481–482, 770.

[9] Huang W.G., Fang H.S., Zheng Y.K. Effect of silicon content on the microstructure and properties in Mn-B air-cooled bainitic steel. Trans. Met. Heat Treat., 1997, 18(1): 8.

[10] Leem D.S., Lee Y.D., Jun J.H., et al. Amount of retained austenite at room temperature after reverse transformation of martensite to austenite in an Fe-13%Cr-7%Ni-3%Si martensite stainless steel. Scripta Mater., 2001, 45, 767.

[11] Zhou Y., Wu G.H. Analysis Methods in Materials Science, 2007 Harbin, Harbin Institute of Technology Press, 95.

[12] Xu Z.Y. Martensitic Transformation and Martensite, 1999 Beijing, Science Press, 84.

[13] Xu Z.Y. Thermodynamics of Materials, 2005 Beijing, Science Press, 305.

[14] Shi L. Thermodynamics of Alloys, 1992 Beijing, China Machine Press, 389.

[15] Shi D.K. Materials Science, 1999 Beijing, China Machine Press, 389.

[16] Cui Z.Q. Metallurgy and Heat Treatment, 1997 Beijing, China Machine Press, 286.