Effect of moisture on the aging behavior of asphalt binder

Abstract

The moisture aging effect and mechanism of asphalt binder during the in-service life of pavement were investigated by laboratory simulating tests. Pressure aging vessel (PAV) test simulating the long-term aging of binder during the in-service life of pavement was modified to capture the long-term moisture aging effect of binder. Penetration grade tests including penetration test, soften point test, and ductility test as well as Superpave™ performance grade tests including viscosity test, dynamic shear rheometer test, and bending beam rheometer test were conducted to fully evaluate the moisture aging effect of binder. Fourier transform infrared spectroscopy test and Gel-permeation chromatography test were applied to provide a fundamental understanding of the moisture aging mechanism of binder. The results indicate that moisture condition can accelerate the aging of asphalt binder and shorten the service life of asphalt binder. The modified PAV test with moisture condition can well characterize the moisture aging properties of asphalt binder.

Keywords

pavement / asphalt / aging / moisture

References

[1] ASTM D2872-04. Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test), 2005 West Conshohocken, Pennsylvania, American Society for Testing Materials

[2] ASTM D6521-08. Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV), 2005 West Conshohocken, Pennsylvania, American Society for Testing Materials

[3] Siddiqui M.N., Ali M.F. Studies on the aging behavior of the Arabian asphalts. Fuel, 1999, 78, 1005.

[4] G.C. Page, K.H. Murphy, and B.E. Ruth, Asphalt binder hardening: causes and effects, [in]_Proceedings of the Association of Asphalt Paving Technologists, 1985, p.140.

[5] Ruan Y.H., Davison R.R., Glover C.J. The effect of long-term oxidation on the rheological properties of polymer modified asphalts. Fuel, 2003, 82, 1763.

[6] Cheng D.X., Little D.N., Lytton R.L., Holste J.C. Moisture damage evaluation of asphalt mixtures by considering both moisture diffusion and repeated-load conditions. Transp. Res. Rec., 2003, 1832, 42.

[7] Caro S., Masad E., Bhasin A., Little D.N. Moisture susceptibility of asphalt mixtures: Part I. Mechanisms. Int. J. Pavement Eng., 2008, 9, 89.

[8] Kringos N., Scarpas A., Copeland A., Youtcheff J. Modeling of combined physical-mechanical moisture-induced damage in asphaltic mixes, part II: moisture susceptibility parameters. Int. J. Pavement Eng., 2008, 9, 129.

[9] Chindaprasirt P., Hatanaka S., Mishima N., Yuasa Y., Chareerat T. Effects of binder strength and aggregate size on the compressive strength and void ratio of porous concrete. Int. J. Miner. Metall. Mater., 2009, 16(6): 714.

[10] Bhasin A., Masad E., Little D., Lytton R. Limits on adhesive bond energy for improved resistance of hot-mix asphalt to moisture damage. Transp. Res. Rec., 2006, 1970, 3.

[11] Chen X.W., Huang B.S. Evaluation of moisture damage in hot mix asphalt using simple performance and superpave indirect tensile tests. Constr. Build. Mater., 2008, 22, 1950.

[12] Caro S., Masad E., Bhasin A., Little D. Micromechanical modeling of the influence of material properties on moisture-induced damage in asphalt mixtures. Constr. Build. Mater., 2010, 24, 1184.

[13] Kassem E., Masad E., Bulut R., Lytton R. Measurements of moisture suction and diffusion coefficient in hot-mix asphalt and their relationships to moisture damage. Transp. Res. Rec., 2006, 1970, 45.

[14] Li T.X., Yang W.W., Zhu W.Y. Component transformation mechanism of mesoporous composite materials studied by FTIR spectroscopy and X-ray diffraction. J. Univ. Sci. Technol. Beijing, 2009, 31(6): 739.

[15] Codrin D. Characterization of Aged Polymer Modified Asphalt Pavements for Recycling Purposes, 2005 Baton Rouge, Louisiana State University, 177.

[16] Gao J., Li X.G., Zhao Q.L., Bao J.P. Effects of artificial weathering on the structure and mechanical properties of thermoplastic elastomer SBS. J. Univ. Sci. Technol. Beijing, 2008, 30(2): 157.