Influence of Nd and Y additions on the corrosion behaviour of extruded Mg-Zn-Zr alloys

Abstract

To improve the corrosion resistance of wrought magnesium alloys through rare earth (RE) additions, the corrosion behaviour of Mg-5Zn-0.3Zr-xNd (x=0, 1, and 2; wt%) and Mg-5Zn-0.3Zr-2Nd-yY (y=0.5 and 1; wt%) alloys in a 5wt% NaCl solution was investigated using immersion test and electrochemical measurements. The results of immersion test show that Mg-5Zn-0.3Zr-2Nd alloy exhibits the best corrosion resistance among the tested alloys. Electrochemical measurements show that secondary phases in RE-containing Mg-5Zn-0.3Zr alloys behave as less noble cathodes in micro-galvanic corrosion and suppress the cathodic process. The additions of Nd and Y into Mg-5Zn-0.3Zr alloy also improve the compactness of the corrosion product film and are beneficial to the corrosion resistance.

Keywords

magnesium alloys / corrosion resistance / rare earth additions / electrochemical properties / neodymium / yttrium

References

[1] Chang J.W., Guo X.W., Fu P.H., et al. Effect of heat treatment on corrosion and electrochemical behaviour of Mg-3Nd-0.2Zn-0.4Zr (wt.%) alloy. Electrochim. Acta, 2007, 52(9): 3160.

[2] Chang J.W., Peng L.M., Guo X.W., et al. Comparison of the corrosion behaviour in 5% NaCl solution of Mg alloys NZ30K and AZ91D. J. Appl. Electrochem., 2008, 38(2): 207.

[3] Peng L.M., Chang J.W., Guo X.W., et al. Influence of heat treatment and microstructure on the corrosion of magnesium alloy Mg-10Gd-3Y-0.4Zr. J. Appl. Electrochem., 2009, 39(6): 913.

[4] Neil W.C., Forsyth M., Howlett P.C., et al. Corrosion of magnesium alloy ZE41: the of microstructural features. Corros. Sci, 2009, 51(2): 387.

[5] Zhao M.C., Liu M., Song G.L., Atrens A. Influence of pH and chloride ion concentration on the corrosion of Mg alloy ZE41. Corros. Sci., 2008, 50(11): 3168.

[6] Liu N., Wang J., Wang L., et al. Electrochemical corrosion behavior of Mg-5Al-0.4Mn-xNd in NaCl solution. Corros. Sci., 2009, 51(6): 1328.

[7] Zhang J., Wang J., Qiu X., et al. Effect of Nd on the microstructure, mechanical properties and corrosion behavior of die-cast Mg-4Al-based alloy. J. Alloys Compd., 2008, 464(1–2): 556.

[8] Song Y.L., Liu Y.H., Yu S.R., et al. Effect of neodymium on microstructure and corrosion resistance of AZ91 magnesium alloy. J. Mater. Sci., 2007, 42(12): 4435.

[9] Liu W., Cao F., Chang L., et al. Effect of rare earth element Ce and La on corrosion behavior of AM60 magnesium alloy. Corros. Sci., 2009, 51(6): 1334.

[10] Izumi S., Yamasaki M., Kawamura Y. Relation between corrosion behavior and microstructure of Mg-Zn-Y alloys prepared by rapid solidification at various cooling rates. Corros. Sci., 2009, 51(2): 395.

[11] Li Q., Wang Q., Wang Y., et al. Effect of Nd and Y addition on microstructure and mechanical properties of as-cast Mg-Zn-Zr alloy. J. Alloys Compd., 2007, 427(1–2): 115.

[12] Song G., Atrens A. Understanding magnesium corrosion-a framework for improved alloy performance. Adv. Eng. Mater., 2003, 5(12): 837.

[13] Baril G., Pébère N. Corrosion of pure magnesium in aerated and deaerated sodium sulphate solutions. Corros. Sci., 2001, 43(3): 471.

[14] Yao H.B., Li Y., Wee A.T.S., et al. Correlation between the corrosion behavior and corrosion films formed on the surfaces of Mg_82−xNi₁₈Nd_x(x=0, 5, and 15) amorphous alloys. Appl. Surf. Sci, 2001, 173(1–2): 54.