Effects of deoxidizing degree on the pitting corrosion behavior of carbon and manganese steels

Abstract

Nine steels with different deoxidizing degrees and two comparative steels were selected. Their pitting initiation susceptibility was compared by means of potentiodynamic polarization tests in 3wt% NaCl solution. The pit propagation rate was evaluated in artificial sea water and 3wt% sea salt solution by simulating occluded corrosion cell (SOCC) test and hanging plate test, respectively. The composition of inclusions and corrosive feature were studied by scanning electron microscopy (SEM), electron probe micro-analysis (EPMA), and optical microscopy (OM). The results indicate that sulfide inclusions in steel are the sites for pit nucleation. The sulphide inclusions vary in shape from short spindle-like to long strip-like with increasing deoxidizing degree. Under the same conditions, the lower the deoxidizing degree gets, the lower the pitting initiation susceptibility becomes, and the stronger the resistance to pit propagation exhibits. For steels with different deoxidizing degrees, their pitting initiation susceptibility is mainly influenced by thermodynamic stability, while the pit propagation rate is primarily subject to the characteristics of inclusions in steel.

Keywords

carbon steel / manganese steel / pitting / deoxidization / inclusions

References

[1] Yang W., Gu J.X., Li Q.S., et al. Localized Corrosion of Metals, 1995 Beijing, Chemical Industry Press, 44.

[2] Zhang H., Chen X.Q., Chang W.S. Effect of metallurgical factors on the susceptibility to pitting initiation in steels. J. Univ. Sci. Technol. Beijing, 2008, 30(10): 1133.

[3] Kong X.D., Chen X.Q., Chang W.S., et al. Relationship between pitting initiation susceptibility and inclusions in carbon steels in artificial seawater. Acta Metall. Sin. Engl. Lett., 2001, 14(3): 157.

[4] Schmuki P., Hildebrand H., Friedrich A., et al. The composition of the boundary region of MnS inclusions in stainless steel and its relevance in triggering pitting corrosion. Corros. Sci., 2005, 47(5): 1239.

[5] Li W.S., Luo J.L. Uniformity of passive film formed on ferrite and martensite by different inorganic inhibitors. Corros. Sci., 2002, 44(8): 1695.

[6] Wang J.M., Chen X.Q., Li G.M. Susceptibility of two types of low-alloy hull steels to pit initiation. J. Univ. Sci. Technol. Beijing, 2004, 11(6): 555.

[7] Szklarska-Smialowska Z. Mechanism of pit nucleation by electrical breakdown of the passive film. Corros. Sci., 2002, 44(5): 1143.

[8] Zhang C.Y., Chen X.Q., Chen D.B. Research of pitting susceptibility in low carbon steels and mechanism of pitting initiation. J. Chin. Soc. Corros. Prot., 2001, 21(5): 265.

[9] Zhan D.P., Zhang H.S., Li S.C., Jiang Z.H. Steel deoxidation and non-metallic inclusion control using AlMnCa alloy. J. Northeast Univ. Nat. Sci., 2006, 27(10): 1118.

[10] Zhang S.J., Song B., Liu X.H., et al. Morphology, chemical compositions and size distribution of rare earth oxides in pure iron. J. Univ. Sci. Technol. Beijing, 2003, 10(2): 30.

[11] Wang J.M., Chen X.Q., Chang W.S., et al. Effect of metallurgical factors on pitting propagation process of low alloy steels. J. Harbin Inst. technol., 2006, 38(11): 1943.

[12] Chang W.S., Li G.M., Hu Y.L., et al. The effects of the RE treatment on pitting corrosion behavior of Mn-V-Ti-steels. Dev. Appl. Mater., 2008, 23(3): 70.

[13] Zheng Y.T., Zhang C.Y., Chen X.Q., et al. Effect of different deoxidization degrees in steel-making process on pitting initiation susceptibility. Corrs. Prot., 2005, 26(5): 192.

[14] G.L. Cao, G.M. Li, W.S. Chang, et al., Effect of deoxidization and inclusions on pitting behaviors of carbon steels, [in]_Proceeding of 13th Quality of Steels and Control of Inclusions, Xining, 2008, p. 192.

[15] Chen X.Q., Kong X.D., Yang S.C. Effect of sulfide inclusions on propagation of pitting in carbon steels. J. Chin. Soc. Corros. Prot., 2000, 20(2): 65.

[16] Yang X.Z., Yang W. Corrosive Electrochemical Thermodynamic Potential-pH Diagram and Application of Metals, 1991 Beijing, Chemical Industry Press, 103.

[17] Vuillemin B., Philippe X., Oltra R., et al. SVET, AFM and AES study of pitting corrosion initiated on MnS inclusions by microinjection. Corros. Sci., 2003, 45(6): 1143.

[18] Tomashov N.D. Theory of Corrosion and Protection of Metal, 1966 New York, Macmillan Press, 153.

[19] Xu T., Chang L.M., Liu J.H. Corrosion behavior of a CuCrNiAl alloy in the presence of NaCl deposit. Rare Met., 2006, 25(3): 210.

[20] Panda B., Balasubramaniam R., Dwivedi G. On the corrosion behaviour of novel high carbon rail steel in simulated cyclic wet-dry salt fog conditions. Corros. Sci., 2008, 50(6): 1684.

[21] Lin L.Y., Liu Z.C., Zhao Y.H., et al. Study on marine corrosion and antifouling behavior of copper alloys exposed to sea areas in China. Rare Met., 2000, 19(2): 96.

[22] Wang J.M. Study on Difference in Pitting Resistance between Ni-Cr and Mn Low Alloy Hull Steel, 2004 Wuhan, Naval University of Engineering, 76.