Microstructural evolution and mechanical properties of aging high nitrogen austenitic stainless steels

Abstract

The microstructural evolution of 18Cr18Mn2Mo0.77N high nitrogen austenitic stainless steel in aging treatment was investigated by optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results show that hexagonal intergranular and cellular Cr₂N with a=0.478 nm and c=0.444 nm and body-centered cubic intermetallic χ phase with a=0.892 nm precipitate gradually in the isothermal aging treatment. The matrix nitrogen depletion due to the intergranular Cr₂N precipitation induces the decay of Vickers hardness, and the formation of cellular Cr₂N and χ phase causes the increase in the values. The impact toughness presents a monotonic decrease and SEM morphologies show the leading brittle intergranular fracture. The tensile strength and elongation deteriorate obviously except for the sample aged for 1 h in yield strength. Stress concentration occurs when the matrix dislocations pile up at the precipitation and matrix interfaces, and the interfacial dislocations may become precursors to the misfit dislocations, which can form small cleavage steps and accelerate the formation of cracks.

Keywords

microstructural evolution / aging / mechanical properties / austenitic stainless steel / secondary phase

References

[1] Marshal P. Austenitic Stainless Steels: Microstructure and Properties, 1984 New York, Elsevier Applied Science Publishers, 1.

[2] Li H.B., Jiang Z.H., Zhang Z.R., et al. Intergranular corrosion behavior of high nitrogen austenitic stainless steel. Int. J. Miner. Metall. Mater., 2009, 16(6): 654.

[3] Li H.B., Jiang Z.H., Yang Y., et al. Pitting corrosion and crevice corrosion behaviors of high nitrogen austenitic stainless steels. Int. J. Miner. Metall. Mater., 2009, 16(5): 517.

[4] Li H.B., Jiang Z.H., Cao Y., et al. Fabrication of high nitrogen austenitic stainless steels with excellent mechanical and pitting corrosion properties. Int. J. Miner. Metall. Mater., 2009, 16(4): 387.

[5] Mudali U.K., Raj B. High Nitrogen Steels and Stainless Steels, 2004 Pangbourne, Alpha Science International Ltd., 133.

[6] M.O. Speidel, Properties and applications of high nitrogen steels, [in] Proceedings of the 1st International High Nitrogen Steels, London, 1989, p.92.

[7] Simmons J.W. Overview: High-nitrogen alloying of stainless steels. Mater. Sci. Eng. A, 1996, 207(2): 159.

[8] Katada Y., Sagara M., Kobayashi Y. Fabrication of high strength high nitrogen stainless steel with excellent corrosion resistance and its mechanical properties. Mater. Manuf. Process., 2004, 19(1): 19.

[9] Simmons J.W., Atteredige D.G., Eawers J.C. Sensitization of high-nitrogen austenitic stainless steels by dichromium nitride precipitation. Corrosion, 1994, 50(7): 491.

[10] Ogawa M., Hiraoka K., Katada Y., et al. Chromium nitride precipitation behavior in weld heat-affected zone of high nitrogen stainless steel. ISIJ Int., 2002, 42(12): 1391.

[11] Tsuchiyama T., Hirakawa N., Nakada N., et al. Decomposition of austenite in Fe-25Cr-1N alloy produced by solution nitriding. Mater. Sci. Forum, 2007, 539–543(5): 4950.

[12] Lee T.H., Kim S.J., Jung Y.C. Crystallographic details of precipitates in Fe-22Cr-21Ni-6Mo-(N) superaustenitic stainless steels aged at 900°C. Metall. Mater. Trans. A, 2000, 31(7): 1713.

[13] Knutsen R.D., Lang C.L., Basson J.A. Discontinuous cellular precipitation in a Cr-Mn-N steel with niobium and vanadium additions. Acta Mater., 2004, 52(8): 2407.

[14] Lee T.H., Kim S.J. Phase identification in an isothermally aged austenitic 22Cr-21Ni-6Mo-N stainless steel. Scripta Mater., 1998, 39(7): 951.

[15] Lee T.H., Oh C.S., Lee C.G., et al. Precipitation characteristics of the second phases in high-nitrogen austenitic 18Cr-18Mn-2Mo-0.9N steel during isothermal aging. Met. Mater. Int., 2004, 10(3): 231.

[16] Kikuchi M., Kajihara M., Choi S.K. Cellular precipitation involving both substitutional and interstitial solutes: cellular precipitation of Cr₂N in Cr-Ni austenitic steels. Mater. Sci. Eng. A, 1991, 146(1–2): 131.

[17] Santhi Srinivas N.C., Pendase R., Gouthama, et al. Initial stages of discontinuous precipitation in high nitrogen austenitic stainless steels. Trans. Indian Inst. Met., 2002, 55(4): 247.

[18] Li H.B., Jiang Z.H., Zhang Z.R., et al. Mechanical properties of nickel free high nitrogen austenitic stainless steels. J. Iron Steel Res. Int., 2007, 14(Suppl.1): 330.

[19] Li H.B., Jiang Z.H., Zhang Z.R., et al. Effect of grain size on mechanical properties of nickel-free high nitrogen austenitic stainless steel. J. Iron Steel Res. Int., 2007, 16(1): 58.

[20] Li H.B., Jiang Z.H., Shen M.H., et al. High nitrogen austenitic stainless steels manufactured by nitrogen gas alloying and adding nitrided ferroalloys. J. Iron Steel Res. Int., 2007, 14(3): 64.

[21] Srinivas N.C. S., Kutumbarao V.V. On the discontinuous precipitation of Cr₂N in Cr-Mn-N austenitic stainless steels. Scripta Mater., 1997, 37(3): 285.

[22] Kasper J.S. The ordering of atoms in the chi-phase of the iron-chromium-molybdenum system. Acta Metall., 1954, 2(3): 456.

[23] Vanderschaeve F., Taillard R., Foct J. Discontinuous precipitation of Cr₂N in a high nitrogen, chromium-manganese austenitic stainless steel. J. Mater. Sci., 1995, 30(23): 6035.

[24] Simmons J.W., Covino B.S., Hauk J.A., et al. Effect of nitride (Cr₂N) precipitation on the mechanical, corrosion and wear properties of austenitic stainless steels. ISIJ Int., 1996, 36(7): 846.

[25] O. Storz, A. Ibach, and M. Pohl, Morphology of σ-phase and its effects on the mechanical properties of duplex steels, [in] Proceedings of Duplex 2007 International Conference, Grado, 2007, p.95.

[26] Maruyama K., Suzuki G., Kim H.Y., et al. Saturation of yield stress and embrittlement in fine lamellar TiAl alloy. Mater. Sci. Eng. A, 2002, 329–331(6): 190.