Assessment of deterioration in RHA-concrete due to magnesium sulphate attack

Abstract

The assessment of magnesium sulphate attack on concretes containing rice husk ash (RHA, 20wt% of the cementitious materials) with various average particle sizes was investigated. The total cementitious materials were 390 kg and the water-to-binder ratio (W/B) was 0.53 for all mixtures. Specimens were initially cured in water for 7 d and then immersed in the 3wt% magnesium sulphate solution for up to 111 d of exposure. The specimens were subjected to drying-wetting cycles to accelerate sulphate attack. In addition to the visual monitoring of the specimens, the concrete specimens were subsequently tested for compressive strength, dynamic modulus of elasticity, and length and mass changes. The results show that the specimens exposed to sulphate attack exhibit higher strength and dynamic modulus than those kept in water. The length change is negligible and can be attributed to the normal swelling of concrete. On the other hand, concretes suffers mass loss and surface spalling and softening; the fine RHA-concrete results in a better resistance. For the accelerated sulphate attack method used in this study, mass change and visual monitoring are recommended for assessing the deterioration degree and the effectiveness of supplementary cementitious materials to resist sulphate attack.

Keywords

concretes / pozzolan / ettringite / rice husk ash (RHA) / magnesium sulphate

References

[1] Shehata M.H., Adhikari G., Radomski S. Long-term durability of blended cement against sulfate attack. ACI Mater. J., 2008, 105(6): 594.

[2] Wee T.H., Suryavanshi A.K., Wong S.F., Anisur-Rahman A.K.M. Sulfate resistance of concrete containing mineral admixtures. ACI Mater. J., 2000, 97(5): 536.

[3] Cohen M.D., Bentur A. Durability of Portland cement-silica fume pastes in magnesium sulfate and sodium sulfate solutions. ACI Mater. J., 1987, 85(3): 148.

[4] Santhanam M., Cohen M.D., Olek J. Sulfate attack research—whither now?. Cem. Concr. Res., 2001, 31, 845.

[5] FAO, World Paddy Production for 2008, Food and Agriculture Organization of the United Nations, 2008, p.2.

[6] Chandrasekhar S., Satyanarayana K.G., Pramada P.N., et al. Review processing, properties and applications of reactive silica from rice husk—An overview. J. Mater. Sci., 2003, 38, 3159.

[7] D.V. Reddy and B.S. Marcelina, Marine durability characteristics of rice husk ash-modified reinforced concrete, [in] Proceedings of the 4th LACCET International Latin American and Caribbean Conference for Engineering and Technology, Puerto Rico, 2006, p.134.

[8] Zhang M.H., Malhotra V.M. High-performance concrete incorporating rice husk ash as a supplementary cementing materials. ACI Mater. J., 1996, 93(6): 629.

[9] Talend D. The Best-Kept Secret to High-Performance Concrete, 1997 Boston, The Aberdeen Group, 3.

[10] H.B. Mahmud, Strength property of rice husk ash concrete, [in] The 5th CANMET/ACI International Conference on Fly Ash, Silica Fume, Slag and Natural Pozzolans in Concrete, Milwaukee, 1995, p.11.

[11] Neville A.M. Properties of Concrete, 2005 4th ed. Essex, Pearson Education Ltd.

[12] Ganesan K., Rajagopal K., Thangavel K. Rice husk ash blended cement: Assessment of optimal level of replacement for strength and permeability properties of concrete. Constr. Build. Mater., 2008, 22(8): 1675.

[13] Hekal E.E., Kishar E., Mostafa H. Magnesium sulfate attack on hardened blended cement pastes under different circumstances. Cem. Concr. Res., 2002, 32, 1421.

[14] Cohen M.D., Mather B. Sulfate attack on concrete—Research needs. ACI Mater. J., 1991, 88(1): 62.

[15] Kalousek G.L., Benton E.J. Mechanism of seawater attack on cement paste. J. Am. Concr. Inst., 1970, 67(2): 187.

[16] Zhang Z., Olek J., Diamond S. Studies on delayed ettringite formation in early-age, heat-cured mortars I. Expansion measurements, changes in dynamic modulus of elasticity, and mass gains. Cem. Concr. Res., 2002, 32, 1729.

[17] Polivka M., Brown E.H. Influence of various factors on sulfate resistance of concrete containing pozzolans. Proc. Am. Soc. Test. Mater., 1959, 58, 1077.