A Cu-Cr alloy with nano and microscale Cr particles produced in a water-cooled copper mold

Abstract

Microstructures have profound effects on the hardness and strength of Cu-Cr alloys. The microstructures of a Cu-Cr alloy cast in a water-cooled copper mold were studied in the present work. The scanning electron microscopy (SEM) results show that there are the copper matrix saturated with chromium, spherical precipitates of chromium separated from liquid phase during cooling before the initiation of solidification, and a eutectic phase in grain boundary areas. To investigate the effect of age-hardening treatment on the microstructures and properties of the material, some samples were subsequently age-hardened in a salt bath and investigated by transmission electron microscopy (TEM). The results show that coherent precipitates with the diameter of 11 nm are detectable in the samples before and after the age-hardening stage. Of course, the volume fraction of coherent precipitates is higher after the aging process.

Keywords

copper alloys / chromium / molding / precipitation hardening / nanoparticles

References

[1] Xie M., Liu G., Lu X.Y., et al. Investigation on the Cu-Cr-RE alloys by rapid solidification. Mater. Sci. Eng. A, 2001, 304–306, 529.

[2] Zhou Z.M., Wang Y.P., Gao J., Kolbe M. Microstructure of rapidly solidified Cu-25wt% Cr alloys. Mater. Sci. Eng. A, 2005, 398, 318.

[3] Sun Z.B., Wang Y.H., Guo J. Liquid phase separation of Cu-Cr alloys during rapid cooling. Trans. Nonferrous Met. Soc. China, 2006, 16, 998.

[4] Zeng K., Hämäläinen M. Thermodynamic analysis of stable and metastable equilibria in the Cu-Cr system. Calphad, 1995, 19, 93.

[5] Jacob K.T., Prya S., Waseda Y. A thermodynamic study of liquid Cu-Cr alloys and metastable liquid immiscibility. Z. Metallkd., 2000, 91, 594.

[6] Sun Z.B., Zhang C. Microstructure of melt-spun Cu_100−x-Cr_x (x=3.4–25) ribbons. J. Alloys Compd., 2003, 361, 165.

[7] Sun Z.B., Wang Y.H., Guo J., et al. Liquid and solid phase separation during melt spinning and annealing in melt-spun Cu-Cr ribbons. Mater. Sci. Eng. A, 2007, 452–453, 411.

[8] Gao J., Wang Y.P., Zhou Z.M., Kolbe M. Phase separation in undercooled Cu-Cr melts. Mater. Sci. Eng. A, 2007, 449–451, 654.

[9] Morris M.A., Morris D.G. Microstructural refinement and associated strength of copper alloys obtained by mechanical alloying. Mater. Sci. Eng. A, 1989, 111, 115.

[10] Porter D.A., Easterling K.E. Phase Transformation in Metals and Alloys, 1992 England, Chapman and Hall, 291.

[11] Hejazi S.M.H. Effect of Cooling Rate on Chromium Solubility in Solidification Process of Cu-Cr Alloy, 2007 Kerman, Shahid Bahonar University, 53.

[12] Majidi F. Characterization of Precipitates Formed in Cu-Cr Alloy Produced by Casting in Water-Cooled Copper Mould, 2008 Kerman, Shahid Bahonar University, 43.

[13] Tenwick M.J., Davies H.A. Enhanced strength in high conductivity copper alloys. Mater. Sci. Eng., 1988, 98, 543.

[14] Hemmati M.H. Effect of Cr Content and Cooling Rate on Microstructure of Cu-Cr Alloy, 2004 Kerman, Shahid Bahonar University, 65.

[15] Elder S.P., Munitz A., Abbaschian G.J. Metal liquid immiscibility in Fe-Cu and Co-Cu alloys. Mater. Sci. Forum., 1989, 50, 137.

[16] Song X., Mahon S.W., Cochrane R.F., et al. Liquid phase separation in melt-spun Cu₇₀Co₃₀ ribbon. Mater. Lett., 1997, 31, 261.

[17] Ashby M.F., browns L.M. Diffraction contrast from spherically symmetrical coherency strains. Philos. Mag., 1963, 8, 1083.

[18] Stobrawa J., Ciura L., Rdzawski Z. Rapidly solidified strips of Cu-Cr alloys. Scripta Mater., 1996, 34, 1759.

[19] Correia J.B., Davies H.A., Sellars C.M. Strengthening in rapidly solidified age hardened Cu-Cr and Cu-Cr-Zr alloys. Acta Mater., 1997, 45, 177.