Decarburization rate of RH refining for ultra low carbon steel

Abstract

The decarburization behaviors of ultra low carbon steel in a 210-t RH vacuum degasser were investigated under practical operating conditions. According to the apparent decarburization rate constant (K _C) calculated by the carbon content in the samples taken from the hot melt in a ladle at an interval of 1–2 min, it is observed that the total decarburization reaction period in RH can be divided into the quick decarburization period and the stagnant decarburization period, which is quite different from the traditional one with three stages. In this study, the average apparent decarburization rate constant during the quick decarburization period is 0.306 min⁻¹, and that of the stagnant period is 0.072 min⁻¹. Increasing the initial carbon content and enhancing the exhausting capacity can increase the apparent decarburization rate constant in the quick decarburization period. The decarburization reaction comes into the stagnant decarburization period when the carbon content in molten steel is less than 14×10⁻⁶ after 10 min of decarburization.

Keywords

refining / decarburization / ultra low carbon steel / degassing

References

[1] Higuchi Y., Ikenaga H., Shirota Y. Effect of [C], [O] and pressure on RH vacuum decarburization. Tetsu-to-Hagane, 1998, 84(10): 21.

[2] S.C. Kang, K.C. Kim, J.M. Park, et al., Improvement of decarburization capacity of RH degasser by revamping at Kwangyang Works, POSCO, [in] Proceeding of Steelmaking Conference, Pittsburgh, 2000, p.99.

[3] Kishimoto Y., Yamaguchi K., Sakuraya T., et al. Decarburization reaction in ultra-low carbon iron melt under reduced pressure. ISIJ Int., 1993, 33(3): 391.

[4] Harashima K., Mizoguchi S., Matsuo M., et al. Rates of nitrogen and carbon removal from liquid iron in low content region under reduced pressures. ISIJ Int., 1992, 32(1): 111.

[5] M. Yano, S. Kitamura, K. Harashima, et al., Improvement of RH refining technology for the production of ultra low carbon and low nitrogen steel, [in] Proceeding of Steelmaking Conference, Chicago, 1994, p.117.

[6] Higashi K. Investigation of decarburization in RH-reactor and its operation improvement. CAMP-ISIJ, 1990, 3(1): 168.

[7] Inoue S., Furuno Y., Usui T., et al. Acceleration of decarburization in RH vacuum degassing process. ISIJ Int., 1992, 32(1): 120.

[8] Kato Y., Fujii T., Suetsugu S., et al. Effect of geometry of vacuum vessel on decarburization rate and final carbon content in RH degasser. Tetsu-to-Hagane, 1993, 79(11): 32.

[9] Kuwabara T., Umezawa K., Mori K., et al. Investigation of decarburization behavior in RH-reactor and its operation improvement. Trans. Iron Steel Inst. Jpn., 1988, 28, 305.

[10] Takahashi M., Matsumoto H., Saito T. Mechanism of decarburization in RH degasser. ISIJ Int., 1995, 35(12): 1452.

[11] Yamaguchi K., Kishimoto Y., Sakuraya T., et al. Effect of refining conditions for ultra low carbon steel on decarburization reaction in RH degasser. ISIJ Int., 1992, 32(1): 126.

[12] S.R. Balajee and W.J. Krajcik, Raw material and process improvements to produce low impurity steels at Inland’s No.4 BOF shop, [in] Proceeding Steelmaking Conference, Detroit, 1990, p.95.

[13] Hahn F.J., Haastert H.P., Bading W., Decker B. Application of the RH process to the production of ultra-low-carbon steels at Thyssen Stahl AG. Iron Steelmaker, 1990, 17(3): 43.

[14] H. Didier, S.R. Huberet, S. Francois, et al., Kinetics of vacuum decarburization of ultra low carbon steels, [in] Proceeding Steelmaking Conference, Maryland, 2001, p.601.

[15] Zhang F.S., Zhu W.J., Xu D., et al. Deep decarbonization and deep denitrification simultaneously by RH-KTB process. Steelmaking, 2007, 23(1): 14.