Enhancing stress relaxation resistance of high-strength Cu–1.95Be–0.24Ni (wt%) alloy via coupling control of precipitate distribution

Abstract

In this study, an optimal combination of mechanical strength, stress relaxation resistance, and conductivity was achieved in a Cu–Be alloy by controlling the precipitate distribution. The precipitation behaviors of the Cu–Be alloy aged at 360°C revealed that the size, morphology, and distribution of precipitated phases can be effectively controlled, enabling the alloy to attain a tensile strength exceeding 1043 MPa. With a reasonable proportion of precipitates, the corresponding electrical conductivity and stress relaxation resistance can reach more than 30.8% IACS and 96.7%, respectively. By correlating the morphology, size, and distribution of precipitated phases with the stress relaxation resistance of the Cu–Be alloy, kinetic equations for the stress relaxation behaviors of the alloy were established in this study. Correspondingly, the stress relaxation rates (SRR) of the alloy were predicted after different stress relaxation times.

Keywords

Cu–Be alloys / stress relaxation / precipitated phases / strength / mechanism

References

[1] Liang JY, Xie GL, Liu FX, Xue WL, Wang R, Liu XH. Optimizing the overall performance of Cu–Ni–Si alloy via controlling nanometer-lamellar discontinuous precipitation structure. Int. J. Miner. Metall. Mater., 2025, 32(4):915.

[2] Liang C, Song GX, Liang LG, Wang WL, He H, Zeng J. Microstructure–property relationship of a high strength–toughness Cr–Mo–V steel. Int. J. Miner. Metall. Mater., 2025, 32(5):1128.

[3] Zhao MJ, Jiang LH, Li CM, et al.Flow characteristics and hot workability of a typical low-alloy high-strength steel during multi-pass deformation. Int. J. Miner. Metall. Mater., 2024, 31(2):323.

[4] Liu S, Zhang P, Wang B, et al.Instrumented oscillographic study on impact toughness of an axle steel DZ2 with different tempering temperatures. Int. J. Miner. Metall. Mater., 2024, 31(7):1590.

[5] Koltygina TA, Bazhenov VE, Koltygin AV, et al.Microstructure and mechanical properties of new Mg–Zn–Y–Zr alloys with high castability and ignition resistance. Int. J. Miner. Metall. Mater., 2024, 31(12):2714.

[6] Du ZY, Shi RJ, Peng XY, Gao KW, Pang XL. Review on the design of high-strength and hydrogen-embrittlement-resistant steels. Int. J. Miner. Metall. Mater., 2024, 31(7):1572.

[7] K. Yang, H.F. Lou, Z.T. Peng, et al., Hot strain induced dynamic recrystallization, precipitation and coordinated deformation behaviors of Cu–4.3wt% Ti alloy, J. Alloy. Compd., 1022(2025), art. No. 179938.

[8] K. Yang, M.X. Guo, H. Wang, et al., Synergistically improved strength and electrical conductivity of Cu–3.3wt% Ti alloy via coupling control of dislocation and multi-scale precipitates, Mater. Sci. Eng. A, 915(2024), art. No. 147259.

[9] Wang X, Li Z, Meng XP, Xiao Z. Ultrahigh strength and improved electrical conductivity in an aging strengthened copper alloy processed by combination of equal channel angular pressing and thermomechanical treatment. J. Cent. South Univ., 2024, 31(6):1823.

[10] Kuang J, Wen W, Cheng PM, Liu G, Zhang JY, Sun J. Creep condition-oriented design of molybdenum alloys with La₂O₃ addition assisted by microstructure-based crystal plasticity modeling. J. Mater. Sci. Technol., 2025, 217: 138.

[11] K. Yang, Y.H. Wang, M.X. Guo, et al., Recent development of advanced precipitation-strengthened Cu alloys with high strength and conductivity: A review, Prog. Mater. Sci., 138(2023), art. No. 101141.

[12] B.W. Zhang, J.Y. Wang, Y.H. Meng, Z.Y. Hong, H.L. Zhao, and X.L. Dong, Double-peak age strengthening phenomenon and mechanism of Cu–Be–Ni–Co alloys, Mater. Des., 238(2024), art. No. 112678.

[13] W.W. Zhang, Z.H. Zhao, J.H. Fang, et al., Evolution and strengthening mechanism of metastable precipitates in Cu–2.0wt% Be alloy, J. Alloy. Compd., 857(2021), art. No. 157601.

[14] S.H. Zhao, J. Feng, Y.M. Zhang, et al., Mechanism of Cr enhancement on stress relaxation resistance in Cu–Ni–Co–Si–Mg alloys, J. Alloy. Compd., 1017(2025), art. No. 178978.

[15] M.X. Zhang, H.W. Song, W. Guo, et al., Study on stress relaxation behavior and mechanism of typical high strength and elasticity copper alloy, Mater. Today Commun., 44(2025), art. No. 112077.

[16] W. Jin, H.F. Huang, S.S. Fu, et al., Effect of temperature on stress relaxation behavior of pure copper with continuous fiber crystal structure, Mater. Sci. Eng. A, 929(2025), art. No. 148138.

[17] J. Feng, Y.M. Zhang, Y.J. Zhou, et al., The influences of Cr and Mn on the strength, electrical conductivity, and stress relaxation properties of Cu–Ni–Si–Co–Mg alloys, Mater. Today Commun., 42(2025), art. No. 111328.

[18] Z.H. Zhang, H.T. Liu, Y.X. Hua, et al., Effect of trace grain boundary segregation element bismuth on stress relaxation behavior of copper, Mater. Sci. Eng. A, 912(2024), art. No. 147006.

[19] Zhang YM, Yang YP, Wang YL, et al.Study of the stress relaxation resistance and microstructural evolution of a Cu–Ni–Si alloy strip. J. Mater. Res. Technol., 2024, 33: 3264.

[20] S.S. Xiao, Q. Lei, Y.Q. Liang, X. Li, and C. Chen, Effect of trace alloying elements on stress relaxation properties of high strength and high conductivity C19160 alloy, Mater. Sci. Eng. A, 908(2024), art. No. 146947.

[21] Y.Q. Shan, Y.M. Zhang, C.M. Zhang, et al., Study on the microstructure and mechanism of stress relaxation behavior of Cu–Ni–Si alloy by two-stage rolling deformation, Mater. Sci. Eng. A, 908(2024), art. No. 146946.

[22] Wang GJ, Liu HT, Song KX, et al.Aging process and strengthening mechanism of Cu–Cr–Ni alloy with superior stress relaxation resistance. J. Mater. Res. Technol., 2022, 19: 3579.

[23] L. Huang, Z.S. Cui, X.P. Meng, X. Li, X.F. Sheng, and Q. Lei, Effect of trace alloying elements on the stress relaxation properties of high strength Cu–Ti alloys, Mater. Sci. Eng. A, 846(2022), art. No. 143281.

[24] Y.Q. Sun, L.J. Peng, G.J. Huang, et al., Effect of Mg on the stress relaxation resistance of Cu–Cr alloys, Mater. Sci. Eng. A, 799(2021), art. No. 140144.

[25] Meng YH, Zhang BW, Wang JY, et al.Effects of Ni content and heat treatment on the properties, microstructures, and precipitates of Cu–0.2wt% Be–xwt% Ni alloys. Materials, 2024, 17(4):816.

[26] Wang Z, Li J, Zhang Y, et al.Comparison of the mechanical properties and microstructures of QB2.0 and C17200 alloys. Materials, 2022, 15(7):2570.

[27] Rotem A, Shechtman D, Rosen A. Correlation among microstructure, strength, and electrical conductivity of Cu–Ni–Be alloy. Metall. Trans. A, 1988, 19(9):2279.

[28] Chakrabarti DJ, Laughlin DE, Tanner LE. The Be–Cu (beryllium–copper) system. Bull. Alloy Phase Diagr., 1987, 8(3):269.

[29] Xie GL, Wang QS, Mi XJ, Xiong BQ, Peng LJ. The precipitation behavior and strengthening of a Cu–2.0wt% Be alloy. Mater. Sci. Eng. A, 2012, 558: 326.

[30] Bonfield W, Edwards BC. Micro-yielding in a precipitation hardening Cu 1.81wt% Be 0.28wt% Co alloy. J. Mater. Sci., 1975, 10(3):493.

[31] Rioja RJ, Laughlin DE. The sequence of precipitation in Cu–2wt% Be alloys. Acta Metall., 1980, 28(9):1301.

[32] Wilkes P, Jackson MM. An electron-microscope study of precipitation in Cu–Be alloys. Met. Sci. J., 1969, 3(1):130.

[33] Geisler AH, Mallery JH, Steigert FE. On the mechanism of precipitation in copper–beryllium alloys. JOM, 1952, 4(3):307.

[34] Yamamoto S, Matsui M, Murakami Y. Electron microscopic observation on the precipitation sequence in Cu–Be alloys. Trans. JIM, 1971, 12(3):159.

[35] Henmi Z, Nagai T. Mechanism of precipitation hardening in Cu–Be alloys. Trans. JIM, 1969, 10(3):166.

[36] X.X. Huang, G.L. Xie, X.H. Liu, H.D. Fu, L. Shao, and Z.F. Hao, The influence of precipitation transformation on Young’s modulus and strengthening mechanism of a Cu–Be binary alloy, Mater. Sci. Eng. A, 772(2020), art. No. 138592.

[37] Zhang HT, Jiang YB, Xie JX, Li YH, Yue LJ. Precipitation behavior, microstructure and properties of aged Cu–1.7wt% Be alloy. J. Alloy. Compd., 2019, 773: 1121.

[38] Tang YC, Kang YL, Yue LJ, Jiao XL. Mechanical properties optimization of a Cu–Be–Co–Ni alloy by precipitation design. J. Alloy. Compd., 2017, 695: 613.

[39] M. Hariram, D. Theerath, P. Chakravarthy, and R.A. Kumar, Influence of cold work on aging response of C17200–beryllium copper alloy C17200, Mater. Today Proc., 4(2017), No. 10, art. No. 11188.

[40] Watanabe C, Hibino M, Monzen R, SeiichiroTsuchiya K. Effects of natural aging on age-hardening behavior of Cu–Be–Co and Cu–Ti alloys processed by high-pressure torsion. Mater. Trans., 2016, 57(9):1471.

[41] Tang YC, Kang YL, Yue LJ, Jiao XL. The effect of aging process on the microstructure and mechanical properties of a Cu–Be–Co–Ni alloy. Mater. Des., 2015, 85: 332.

[42] Monzen R, Okawara S, Watanabe C. Stress-assisted nucleation and growth of γ″ and γ′ precipitates in a Cu–1.2w% Be–0.1wt% Co alloy aged at 320°C. Philos. Mag., 2012, 92(14):1826.

[43] Yagmur L, Duygulu O, Aydemir B. Investigation of metastable γ′ precipitate using HRTEM in aged Cu–Be alloy. Mater. Sci. Eng. A, 2011, 528(12):4147.

[44] Behjati P, Dastjerdi HV, Mahdavi R. Influence of ageing process on sound velocity in C17200 copper–beryllium alloy. J. Alloy. Compd., 2010, 505(2):739.

[45] Watanabe C, Sakai T, Monzen R. Misfit strains of precipitated phases and dimensional changes in Cu–Be alloys. Philos. Mag., 2008, 88(9):1401.

[46] Monzen R, Seo T, Sakai T, Watanabe C. Precipitation processes in a Cu–0.9mass% Be single crystal. Mater. Trans., 2006, 47(12):2925.

[47] Yang K, Wang MM, Guo MX, et al.Improved hot workability of Cu–3.18wt% Ti alloy via cooperative control of dynamic recrystallization and precipitation. J. Mater. Sci., 2025, 60(14):6307.

[48] K. Yang, M.X. Guo, H. Wang, et al., Synergistical effects of Mg microalloying, deformation, and aging on the strength and electrical conductivity of Cu–3.3W% Ti alloy, Adv. Eng. Mater., 27(2025), No. 1, art. No. 2401917.

Rights & permissions

University of Science and Technology Beijing