Delving into the role of microwave curing on the strength and cement hydration features of cemented tailings backfill

Abstract

Cemented tailings backfill (CTB) comprises tailings, binders, and water and is filled into goaves to regulate the ground pressure and ensure production safety. Thus, shortening the curing time of CTB has been a popular research topic in backfill mining as it maximizes the extraction of the neighboring stopes while lowering mining-related costs. In this study, a self-made horn microwave experimental device was developed to rapidly enhance CTB’s strength property. Subsequently, the microwave-curing effects on the upper surface temperature, strength, deformation coefficient, and hydration reaction of CTB were explored through uniaxial compressive strength, X-ray diffraction, and thermogravimetric/differential thermogravimetric experiments. Experimental marks revealed that the strength property of early-aged (up to 7 d) CTB composites could be rapidly enhanced by microwave curing, except for the 7-d-cured fills with microwave curing times of 5–7 min. Moreover, the hydration reactions of CTB after 3- and 7-d curing were substantially accelerated by microwave curing. Thus, this study offers a novel method of satisfactorily increasing early-aged CTB strength and exploring its hydration mechanisms effectively.

Keywords

Cementitious mine backfill / Microwave / Curing / Mechanical property / Hydration reaction

References

[1] D. Wu, Y.L. Zhang, C. Wang, Modeling the thermal response of hydrating cemented gangue backfill with admixture of fly ash, Thermochim. Acta 623 (2016) 86-94.

[2] D. Wu, Y.L. Zhang, Y.C. Liu, Mechanical performance and ultrasonic properties of cemented gangue backfill with admixture of fly ash, Ultrasonics 64 (2016) 89-96.

[3] Q.H. Ma, G.S. Liu, X.C. Yang, L.J. Guo, Physical model investigation on effects of drainage condition and cement addition on consolidation behavior of tailings slurry within backfilled stopes, Int. J. Miner. Metall. Mater. 30 (8) (2023) 1490-1501.

[4] H.J. Lu, Y.R. Wang, D.Q. Gan, J. Wu, X.J. Wu, Numerical investigation of the mechanical behavior of the backfill-rock composite structure under triaxial compression, Int. J. Miner. Metall. Mater. 30 (5) (2023) 802-812.

[5] J.J. Li, E. Yilmaz, S. Cao, Influence of solid content, cement/tailings ratio, and curing time on rheology and strength of cemented tailings backfill, Minerals 10 (10) (2020) 922.

[6] B. Nenchev, Q. Tao, Z.H. Dong, C. Panwisawas, H.Y. Li, B. Tao, H.B. Dong, Evaluating data-driven algorithms for predicting mechanical properties with small datasets: A case study on gear steel hardenability, Int. J. Miner. Metall. Mater. 29 (4) (2022) 836-847.

[7] X.J. Deng, J.X. Zhang, B. Klein, N. Zhou, B. deWit, Experimental characterization of the influence of solid components on the rheological and mechanical properties of cemented paste backfill, Int. J. Miner. Process. 168 (2017) 116-125.

[8] F. Cihangir, B. Ercikdi, A. Kesimal, H. Deveci, F. Erdemir, Paste backfill of high-sulphide mill tailings using alkali-activated blast furnace slag: Effect of activator nature, concentration and slag properties, Miner. Eng. 83 (2015) 117-127.

[9] B. Ercikdi, A. Kesimal, F. Cihangir, H. Deveci, İ. Alp, Cemented paste backfill of sulphide-rich tailings: importance of binder type and dosage, Cem. Concr. Compos. 31 (4) (2009) 268-274.

[10] W. Sun, A.X. Wu, K.P. Hou, Y. Yang, L. Liu, Y.M. Wen, Real-time observation of meso-fracture process in backfill body during mine subsidence using X-ray CT under uniaxial compressive conditions, Constr. Build. Mater. 113 (2016) 153-162.

[11] B. Ercikdi, G. Külekci, T. Yılmaz, Utilization of granulated marble wastes and waste bricks as mineral admixture in cemented paste backfill of sulphide-rich tailings, Constr. Build. Mater. 93 (2015) 573-583.

[12] B. Lothenbach, F. Winnefeld, C. Alder, E. Wieland, P. Lunk, Effect of temperature on the pore solution, microstructure and hydration products of Portland cement pastes, Cem. Concr. Res. 37 (4) (2007) 483-491.

[13] E. Yilmaz, T. Belem, B. Bussière, M. Mbonimpa, M. Benzaazoua, Curing time effect on consolidation behaviour of cemented paste backfill containing different cement types and contents, Constr. Build. Mater. 75 (2015) 99-111.

[14] S. Wang, X.P. Song, M.L. Wei, W. Liu, X.J. Wang, Y.X. Ke, T.J. Tao, Strength characteristics and microstructure evolution of cemented tailings backfill with rice straw ash as an alternative binder, Constr. Build. Mater. 297 (2021) 123780.

[15] S. Cao, E. Yilmaz, W.D. Song, Fiber type effect on strength, toughness and microstructure of early age cemented tailings backfill, Constr. Build. Mater. 223 (2019) 44-54.

[16] J.J. Li, S. Cao, E. Yilmaz, Y.P. Liu, Compressive fatigue behavior and failure evolution of additive fiber-reinforced cemented tailings composites, Int. J. Miner. Metall. Mater. 29 (2) (2022) 345-355.

[17] Q.Y. Xie, J.P. Li, Y.F. Zhao, Effects of air temperature and precipitation on soil moisture on the Qinghai-Tibet Plateau during the 2015 growing season, Adv. Meteorol. 2020 (2020) 4918945.

[18] C. Hou, W.C. Zhu, B.X. Yan, K. Guan, J.F. Du, The effects of temperature and binder content on the behavior of frozen cemented tailings backfill at early ages, Constr. Build. Mater. 239 (2020) 117752.

[19] M. Fall, M. Pokharel, Coupled effects of sulphate and temperature on the strength development of cemented tailings backfills: Portland cement-paste backfill, Cem. Concr. Compos. 32 (10) (2010) 819-828.

[20] A. Hasan, W.K. Ting, Temperature effect on Mohr-Coulomb’s effective strength parameters of paste backfill, Front. Mater. 8 (2022) 794089.

[21] B. Han, S.Y. Zhang, W. Sun, Impact of temperature on the strength development of the tailing-waste rock backfill of a gold mine, Adv. Civ. Eng. 2019 (2019) 4379606.

[22] B.W. Wang, Q.L. Li, R.Z. Wang, D.Z. Wang, P.B. Dong, Mechanical strength and hydration exothermic behavior of cemented paste backfill with early-strength agent under low temperature, Int. J. Min. Reclam. Environ. 36 (10) (2022) 710-723.

[23] X.Q. Wu, J. Dong, M.S. Tang, Microwave curing technique in concrete manufacture, Cem. Concr. Res. 17 (2) (1987) 205-210.

[24] C.K.Y. Leung, T. Pheeraphan, Microwave curing of Portland cement concrete: experimental results and feasibility for practical applications, Constr. Build. Mater. 9 (2) (1995) 67-73.

[25] C.K.Y. Leung, T. Pheeraphan, Determination of optimal process for microwave curing of concrete, Cem. Concr. Res. 27 (3) (1997) 463-472.

[26] C.Y. Bai, Y. Deng, Q. Zhou, G. Deng, T.T. Yang, Y.Y. Yang, Effect of different curing methods on the preparation of carbonized high-titanium slag based geopolymers, Constr. Build. Mater. 342 (2022) 128023.

[27] J.W. Tan, J.M. Cai, L.C. Huang, Q.N. Yang, M.J. Mao, J.B. Li, Feasibility of using microwave curing to enhance the compressive strength of mixed recycled aggregate powder based geopolymer, Constr. Build. Mater. 262 (2020) 120897.

[28] Y.N. Kong, P.M. Wang, S.H. Liu, Microwave pre-curing of Portland cement-steel slag powder composite for its hydration properties, Constr. Build. Mater. 189 (2018) 1093-1104.

[29] P.S. Mangat, K. Grigoriadis, S. Abubakri, Microwave curing parameters of in situ concrete repairs , Constr. Build. Mater. 112 (2016) 856-866.

[30] D. Wu, W. Sun, S. Liu, C.L. Qu, Effect of microwave heating on thermo-mechanical behavior of cemented tailings backfill, Constr. Build. Mater. 266 (2021) 121180.

[31] W. Sun, D. Wu, H.B. Liu, C.L. Qu, Thermal, mechanical and ultrasonic properties of cemented tailings backfill subjected to microwave radiation, Constr. Build. Mater. 313 (2021) 125535.

[32] W. Sun, D. Wu, W.Y. Xu, L.F. Ma, J. Cao, J.G. Chen, Coupled electromagnetic heat transfer model for cemented tailings backfill cured by microwave energy, Constr. Build. Mater. 342 (2022) 128014.

[33] Y.F. Sun, S.G. Hu, P. Zhang, K. Elmaadawy, Y. Ke, J.H. Li, M.Y. Li, J.P. Hu, B.C. Liu, J.K. Yang, S. Liang, K.K. Xiao, H.J. Hou, Microwave enhanced solidification/stabilization of lead slag with fly ash based geopolymer, J. Clean. Prod. 272 (2020) 122957.

[34] D.Q. Gan, H.B. Li, C. Chen, H.J. Lu, Y.Z. Zhang, An experimental study on strength characteristics and hydration mechanism of cemented ultra-fine tailings backfill, Front. Mater. 8 (2021) 723878.

[35] B.L. Xiao, Z.J. Wen, S.J. Miao, Q. Gao, Utilization of steel slag for cemented tailings backfill: hydration, strength, pore structure, and cost analysis, Case Stud. Constr. Mater. 15 (2021) e00621.

[36] J.R. Zheng, X.X. Sun, L.J. Guo, S.M. Zhang, J.Y. Chen, Strength and hydration products of cemented paste backfill from sulphide-rich tailings using reactive MgO-activated slag as a binder, Constr. Build. Mater. 203 (2019) 111-119.

[37] Y.F. Hu, S.H. Yin, K.Q. Li, B. Han, B. Zhang, Formation mechanism and thermal decomposition properties of hydration products of superfine tailings cemented paste backfill, Arab. J. Chem. 16 (8) (2023) 104977.

[38] G.J. Zhu, W.C. Zhu, Y. Fu, B.X. Yan, H.Q. Jiang, Effects of chloride salts on strength, hydration, and microstructure of cemented tailings backfill with one-part alkali-activated slag, Constr. Build. Mater. 374 (2023) 130965.

[39] P. Rattanadecho, N. Makul, A. Pichaicherd, P. Chanamai, B. Rungroungdouyboon, A novel rapid microwave-thermal process for accelerated curing of concrete: prototype design, optimal process and experimental investigations, Constr. Build. Mater. 123 (2016) 768-784.

[40] N. Makul, Utilization of microwave-accelerated heating and dewatering in low-pressure conditions to accelerated-cure Type-I cement paste for early-age compressive strength development, J. Build. Eng. 26 (2019) 100920.

[41] M.S. El-Feky, M. Kohail, A.M. El-Tair, M.I. Serag, Effect of microwave curing as compared with conventional regimes on the performance of alkali activated slag pastes, Constr. Build. Mater. 233 (2020) 117268.

[42] W. Xia, E.L. Bai, S. Lu, J.Y. Xu, H. Huang, Optimal design and experimental study of horn antenna in pavement microwave deicing technology, Cold Reg. Sci. Technol. 205 (2023) 103695.

[43] G. Mayhew-Ridgers, J.W. Odendaal, J. Joubert, Improved diffraction model and numerical validation for horn antenna gain calculations, Int. J. RF Microw. Comput. Aided Eng. 19 (6) (2009) 701-711.

[44] N. Abdul-Hussain, M. Fall, Unsaturated hydraulic properties of cemented tailings backfill that contains sodium silicate, Eng. Geol. 123 (4) (2011) 288-301.