Photocatalytic degradation of xanthates under visible light using heterogeneous CuO/TiO₂/montmorillonite composites

Abstract

Due to the significant demand for xanthate treatment in mineral effluents, photocatalytic techniques have emerged as one of the most promising solutions. In this study, a high-performance TiO₂/CuO/montmorillonite photocatalyst was prepared. In this configuration, TiO₂ was the classic photocatalytic material and CuO and montmorillonite were utilized to broaden the adsorption range of solar light and acted as carriers to support the photocatalyst. X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy were employed for the comprehensive characterization of the microstructure of the ternary photocatalyst. The results revealed that fine-sized TiO₂ and CuO nanoparticles were uniformly and tightly loaded on the montmorillonite layers. The photocatalytic properties of the photocatalyst were evaluated using sodium butyl xanthate as the target contaminant. For pristine TiO₂, ultraviolet (UV) light was required to effectively degrade sodium butyl xanthate. Meanwhile, the degradation reaction could be processed efficiently under visible light using the TiO₂/CuO/montmorillonite composite as the photocatalyst. Moreover, UV–visible diffuse reflectance spectroscopy, photoluminescence spectroscopy, and radical quench experiments were performed to elucidate the degradation process, and a possible degradation model and mechanism were proposed.

Keywords

TiO₂ / CuO / Montmorillonite / Visible-light photocatalysis / Xanthates

References

[1] C.S. Zhou, A. Bahr, G. Schwedt, Studies on the HPLC determination of xanthates via copper(I) xanthates and dixanthogens, Z. Anal. Chem. 334 (6) (1989) 527-533.

[2] J.Q. Yuan, S.Q. Li, Z. Ding, J. Li, A.M. Yu, S.M. Wen, S.J. Bai, Treatment technology and research progress of residual xanthate in mineral processing wastewater, Minerals 13 (3) (2023) 435.

[3] M. Jiang, M.H. Zhang, L.Z. Wang, Y.W. Fei, S. Wang, A. Núñez-Delgado, A. Bokhari, M. Race, A. Khataee, J. Jaromír Klemeš, L.B. Xing, N. Han, Photocatalytic degradation of xanthate in flotation plant tailings by TiO₂/graphene nanocomposites , Chem. Eng. J. 431 (2022) 134104.

[4] Z.Z. Bian, Y.L. Feng, H.R. Li, H. Yu, H. Wu, Adsorption-photocatalytic degradation and kinetic of sodium isobutyl xanthate using the nitrogen and cerium co-doping TiO₂-coated activated carbon , Chemosphere 263 (2021) 128254.

[5] J.Q. Yuan, Z. Ding, X. Gong, A.M. Yu, S.M. Wen, S.J. Bai, Degradation of residual xanthate in flotation tailing wastewater by activated H₂O₂ with natural ilmenite: A heterogeneous fenton-like reaction catalyzed at natural pH , Sep. Purif. Technol. 332 (2024) 125819.

[6] G.C. Molina, C.H. Cayo, M.A.S. Rodrigues, A.M. Bernardes, Sodium isopropyl xanthate degradation by advanced oxidation processes, Miner. Eng. 45 (2013) 88-93.

[7] A. Amrollahi, M. Massinaei, A. Zeraatkar Moghaddam, Removal of the residual xanthate from flotation plant tailings using bentonite modified by magnetic nanoparticles, Miner. Eng. 134 (2019) 142-155.

[8] S.H. Chen, W.Q. Gong, G.J. Mei, Q. Zhou, C.P. Bai, N. Xu, Primary biodegradation of sulfide mineral flotation collectors, Miner. Eng. 24 (8) (2011) 953-955.

[9] L. Li, M. He, Y.F. Feng, H.B. Wei, X.F. You, H. Yu, Q.B. Wang, J.X. Wang, Adsorption of xanthate from aqueous solution by multilayer graphene oxide: An experimental and molecular dynamics simulation study, Adv. Compos. Hybrid Mater. 4 (3) (2021) 725-732.

[10] C. Byrne, G. Subramanian, S.C. Pillai, Recent advances in photocatalysis for environmental applications, J. Environ. Chem. Eng. 6 (3) (2018) 3531-3555.

[11] X.G. Yang, D.W. Wang, Photocatalysis: From fundamental principles to materials and applications, ACS Appl. Energy Mater. 1 (12) (2018) 6657-6693.

[12] J. Schneider, M. Matsuoka, M. Takeuchi, J.L. Zhang, Y. Horiuchi, M. Anpo, D.W. Bahnemann, Understanding TiO₂ photocatalysis: Mechanisms and materials , Chem. Rev. 114 (19) (2014) 9919-9986.

[13] Q. Guo, C.Y. Zhou, Z.B. Ma, X.M. Yang, Fundamentals of TiO₂ photocatalysis: concepts, mechanisms, and challenges , Adv. Mater. 31 (50) (2019) 1901997.

[14] S. Peiris, H.B. de Silva, K.N. Ranasinghe, S.V. Bandara, I.R. Perera, Recent development and future prospects of TiO₂ photocatalysis , J. Chin. Chem. Soc. 68 (5) (2021) 738-769.

[15] C. Hu, J. Guo, J.H. Qu, X.X. Hu, Photocatalytic degradation of pathogenic bacteria with AgI/TiO₂ under visible light irradiation , Langmuir 23 (9) (2007) 4982-4987.

[16] J.H. Sun, L.P. Qiao, S.P. Sun, G.L. Wang, Photocatalytic degradation of Orange G on nitrogen-doped TiO₂ catalysts under visible light and sunlight irradiation , J. Hazard. Mater. 155 (1-2) (2008) 312-319.

[17] W.J. Lin, X.F. Xie, X. Wang, Y. Wang, D. Segets, J. Sun, Efficient adsorption and sustainable degradation of gaseous acetaldehyde and o-xylene using rGO-TiO₂ photocatalyst , Chem. Eng. J. 349 (2018) 708-718.

[18] V. Etacheri, C. Di Valentin, J. Schneider, D. Bahnemann, S.C. Pillai, Visible-light activation of TiO₂ photocatalysts: Advances in theory and experiments , J. Photochem. Photobiol. C Photochem. Rev. 25 (2015) 1-29.

[19] C.H. Nguyen, C.C. Fu, R.S. Juang, Degradation of methylene blue and methyl orange by palladium-doped TiO₂ photocatalysis for water reuse: Efficiency and degradation pathways , J. Clean. Prod. 202 (2018) 413-427.

[20] X.F. Qu, X.H. Zhao, M.H. Liu, Z.Q. Gao, D.L. Yang, L. Shi, Y.B. Tang, H.B. Song, BiOCl/TiO₂ composite photocatalysts synthesized by the sol-gel method for enhanced visible-light catalytic activity toward methyl orange , J. Mater. Res. 35 (22) (2020) 3067-3078.

[21] S. Liu, M. Lim, R. Amal, TiO₂-coated natural zeolite: Rapid humic acid adsorption and effective photocatalytic regeneration , Chem. Eng. Sci. 105 (2014) 46-52.

[22] H.L. Yang, Y. Wu, Z.W. Zhuang, Y. Li, C. Chen, Factors affecting the catalytic performance of nano-catalysts, Chin. J. Chem. 40 (4) (2022) 515-523.

[23] C.Q. Li, Z.M. Sun, A.K. Song, X.B. Dong, S.L. Zheng, D.D. Dionysiou, Flowing nitrogen atmosphere induced rich oxygen vacancies overspread the surface of TiO₂/kaolinite composite for enhanced photocatalytic activity within broad radiation spectrum , Appl. Catal. B Environ. 236 (2018) 76-87.

[24] K. Ullah, L. Zhu, Z.D. Meng, S. Ye, Q. Sun, W.C. Oh, A facile and fast synthesis of novel composite Pt-graphene/TiO₂ with enhanced photocatalytic activity under UV/Visible light , Chem. Eng. J. 231 (2013) 76-83.

[25] H. Dzinun, M.H.D. Othman, A.F. Ismail, Photocatalytic performance of TiO₂/Clinoptilolite: Comparison study in suspension and hybrid photocatalytic membrane reactor , Chemosphere 228 (2019) 241-248.

[26] C.C. Wang, Y. Zhan, Z.Y. Wang, TiO₂, MoS₂, and TiO₂/MoS₂ heterostructures for use in organic dyes degradation , ChemistrySelect 3 (6) (2018) 1713-1718.

[27] C.C. Wang, X. Wang, W. Liu, The synthesis strategies and photocatalytic performances of TiO₂/MOFs composites: A state-of-the-art review , Chem. Eng. J. 391 (2020) 123601.

[28] Y.F. Yang, L.D. Xu, H.F. Wang, W.J. Wang, L.X. Zhang, TiO₂/graphene porous composite and its photocatalytic degradation of methylene blue , Mater. Des. 108 (2016) 632-639.

[29] B. Szczepanik, Photocatalytic degradation of organic contaminants over clay-TiO₂ nanocomposites: a review , Appl. Clay Sci. 141 (2017) 227-239.

[30] P.F. Zhou, Y.B. Shen, S.K. Zhao, G.D. Li, B.Y. Cui, D.Z. Wei, Y.S. Shen, Synthesis of clinoptilolite-supported BiOCl/TiO₂ heterojunction nanocomposites with highly-enhanced photocatalytic activity for the complete degradation of xanthates under visible light , Chem. Eng. J. 407 (2021) 126697.

[31] H. Li, Y. Yao, X. Yang, X. Zhou, R. Lei, S. He, Degradation of phenol by photocatalysis using TiO₂/montmorillonite composites under UV light , Environ. Sci. Pollut. Res. Int 29 (45) (2022) 68293-68305.

[32] Y.H. Zhang, B.J. Miao, Q.L. Chen, Z.M. Bai, Y.G. Cao, B. Davaa, Synthesis, structure, and photocatalytic activity of TiO₂-montmorillonite composites , Catalysts 12 (5) (2022) 486.

[33] T.B.T. Dao, T.T.L. Ha, T. Do Nguyen, H.N. Le, C.N. Ha-Thuc, T.M.L. Nguyen, P. Perre, D.M. Nguyen, Effectiveness of photocatalysis of MMT-supported TiO₂ and TiO₂ nanotubes for rhodamine B degradation , Chemosphere 280 (2021) 130802.

[34] L.L. Yuan, D.D. Huang, W.N. Guo, Q.X. Yang, J. Yu, TiO₂/montmorillonite nanocomposite for removal of organic pollutant , Appl. Clay Sci. 53 (2) (2011) 272-278.

[35] K.E. Onwuka, K. Achilike, K.S. Eze, N.E. Enenwa, Montmorillonite clay enhanced TiO₂ nanoparticle for photocatalytic degradation of organic pollutants: Mini review , Int. J. Pharm. Sci. 1 (1) (2021) 33-38.

[36] K.K. Hu, L. E, D. Zhao, Y.J. Li, W. Zhao, H. Rong, Characteristics and performance of rutile/anatase/brookite TiO₂ and TiO₂-Ti₂O₃(H₂O)₂(C₂O₄)·H₂O multiphase mixed crystal for the catalytic degradation of emerging contaminants , CrystEngComm 22 (6) (2020) 1086-1095.

[37] H.F. Xu, G. Li, G. Zhu, K.R. Zhu, S.W. Jin, Enhanced photocatalytic degradation of rutile/anatase TiO₂ heterojunction nanoflowers , Catal. Commun. 62 (2015) 52-56.

[38] S. Bagheri, N.M. Julkapli, Mixed-phase TiO₂ photocatalysis: correlation between phase composition and photodecomposition of water pollutants , Rev. Inorg. Chem. 37 (1) (2017) 11-28.

[39] V. Likodimos, A. Chrysi, M. Calamiotou, C. Fernández-Rodríguez, J.M. Doña-Rodríguez, D.D. Dionysiou, P. Falaras, Microstructure and charge trapping assessment in highly reactive mixed phase TiO₂ photocatalysts , Appl. Catal. B Environ. 192 (2016) 242-252.

[40] M.E. Bustos, F. Hevia, S. Fuentes, A.I. Martínez, R.A. Zárate, A novel route for the preparation of self-assembled CuO hierarchical nanostructures by hydrothermal processing at high pressure, Mater. Lett. 297 (2021) 129936.

[41] W.B. Liu, X.Y. Peng, W.G. Liu, K.L. Tong, Y.B. Shen, Q. Zhao, S.K. Zhao, W.H. Sun, Novel polyhydroxy cationic collector N-(2,3-propanediol)-N-dodecylamine: Synthesis and flotation performance to hematite and quartz, Int. J. Min. Sci. Technol. 33 (1) (2023) 115-122.

[42] P.F. Zhou, Y.B. Shen, S.K. Zhao, J.Z. Bai, C. Han, W.G. Liu, D.Z. Wei, Facile synthesis of clinoptilolite-supported Ag/TiO₂ nanocomposites for visible-light degradation of xanthates , J. Taiwan Inst. Chem. Eng. 122 (2021) 231-240.

[43] J. Liu, J. Jin, Z. Deng, S.Z. Huang, Z.Y. Hu, L. Wang, C. Wang, L.H. Chen, Y. Li, G. Van Tendeloo, B.L. Su, Tailoring CuO nanostructures for enhanced photocatalytic property, J. Colloid Interface Sci. 384 (1) (2012) 1-9.

[44] S. Harish, J. Archana, M. Sabarinathan, M. Navaneethan, K.D. Nisha, S. Ponnusamy, C. Muthamizhchelvan, H. Ikeda, D.K. Aswal, Y. Hayakawa, Controlled structural and compositional characteristic of visible light active ZnO/CuO photocatalyst for the degradation of organic pollutant, Appl. Surf. Sci. 418 (2017) 103-112.

[45] P. Apopei, C. Catrinescu, C. Teodosiu, S. Royer, Mixed-phase TiO₂ photocatalysts: crystalline phase isolation and reconstruction, characterization and photocatalytic activity in the oxidation of 4-chlorophenol from aqueous effluents , Appl. Catal. B Environ. 160-161 (2014) 374-382.

[46] S.K. Zhao, Y.B. Shen, P.F. Zhou, J. Zhang, W. Zhang, X.X. Chen, D.Z. Wei, P. Fang, Y.S. Shen, Highly selective NO₂ sensor based on p-type nanocrystalline NiO thin films prepared by sol-gel dip coating , Ceram. Int. 44 (1) (2018) 753-759.

[47] J.H. Lee, J.H. Kim, S.S. Kim, CuO-TiO₂ p-n core-shell nanowires: sensing mechanism and p/n sensing-type transition , Appl. Surf. Sci. 448 (2018) 489-497.

[48] Y.J. Wang, Q.S. Wang, X.Y. Zhan, F.M. Wang, M. Safdar, J. He, Visible light driven type II heterostructures and their enhanced photocatalysis properties: a review, Nanoscale 5 (18) (2013) 8326-8339.