Two-step gate-recess process combining selective wet-etching and digital wet-etching for InAlAs/InGaAs InP-based HEMTs

Abstract

A two-step gate-recess process combining high selective wet-etching and non-selective digital wet-etching techniques has been proposed for InAlAs/InGaAs InP-based high electron mobility transistors (HEMTs). High etching-selectivity ratio of InGaAs to InAlAs material larger than 100 is achieved by using mixture solution of succinic acid and hydrogen peroxide (H2O2). Selective wet-etching is validated in the gate-recess process of InAlAs/InGaAs InP-based HEMTs, which proceeds and automatically stops at the InAlAs barrier layer. The non-selective digital wet-etching process is developed using a separately controlled oxidation/de-oxidation technique, and during each digital etching cycle 1.2 nm InAlAs material is removed. The two-step gate-recess etching technique has been successfully incorporated into device fabrication. Digital wet-etching is repeated for two cycles with about 3 nm InAlAs barrier layer being etched off. InP-based HEMTs have demonstrated superior extrinsic transconductance and RF characteristics to devices fabricated during only the selective gate-recess etching process because of the smaller gate to channel distance.

Keywords

High electron mobility transistors (HEMTs) / Gate-recess / Digital wet-etching / Selective wet-etching

References

[1] Cao,X., Thoms, S., Macintyre,D. , , 2004. Fabrication and performance of 50 nm T-gates for InP high electron mobility transistors.Microelectron. Eng., 73-74:818-821.

[2] Deal,W.R., Mei,X.B., Leong,K., , 2011a. THz monolithic integrated circuits using InP high electron mobility transistors.IEEE Trans. Terah. Sci. Technol., 1(1):25–32.

[3] Deal,W.R., Leong, K., Radisic,V. , , 2011b. Low noise amplification at 0.67 THz using 30 nm InP HEMTs.IEEE Microw. Wirel. Compon. Lett., 21(7):368–370.

[4] Deal,W.R., Leong, K., Zamora,A. , , 2014. Recent progress in scaling InP HEMT TMIC technology to 850 GHz.IEEE MTT-S Int. Microwave Symp., p.1–3.

[5] Leong,K., Mei,X.B., Yoshida,W. , , 2015. A 0.85 THz low noise amplifier using InP HEMT transistors.IEEE Microw. Wirel. Compon. Lett., 25(6):397–399.

[6] Mei,X.B., Yoshida, W., Lange,M. , , 2015. First demonstration of amplification at 1 THz using 25-nm InP high electron mobility transistor process.IEEE Electr. Dev. Lett., 36(4):327–329.

[7] Reck,T., Zemora, A., Schlecht,E. , , 2016. A 230 GHz MMIC-based sideband separating receiver.IEEE Trans. Terah. Sci. Technol., 6(1):141–147.

[8] Rodwell,M.J.W., 2014. 50-500 GHz wireless: transistors, ICs, and system design.German Microwave Conf., p.1–4.

[9] Varonen,M., Reeves, R., Kangaslahti,P. , , 2016. An MMIC low-noise amplifier design technique.IEEE Trans. Microw. Theory Techn., 64(3):826–835.

[10] Zhong,Y.H., Wang,X.T., Su,Y.B., , 2012a. Impact of the lateral width of the gate recess on the DC and RF characteristics of InAlAs/InGaAs HEMTs.J. Semicond., 33(5):61–65.

[11] Zhong,Y.H., Wang,X.T., Su,Y.B., , 2012b. An 88 nm gate-length In0.53Ga0.47As/In0.52Al0.48As InP-based HEMT with fmax of 201 GHz.J. Semicond., 33(7):39–42.

[12] Zhong,Y.H., Li,K.K., Li,X.J., , 2015. A W-band high-gain and low-noise amplifier MMIC using InPbased HEMTs.J Infrar. Millim. Waves, 34(6):668–672 (in Chinese).

RIGHTS & PERMISSIONS

Zhejiang University and Springer-Verlag GmbH Germany