Structure and properties of polymer modified TiO pillared montmorillonite

Abstract

With the aim of improving the microstructures and properties of TiO₂ pillared montmorillonite (MMT), a long-chain polymer (polyoxypropylenediamine, PPO-D 2000) was used as a template to synthesize composite pillared MMT. The materials were characterized by X-ray powder diffraction (XRD), Fourier transform infrared (FT-IR) spectrophotometer, Fourier Raman (FT-Raman) spectrophotometer, thermo-gravimeter/differential thermo-gravimeter (TG/DSC), transmission electron microscopy (TEM), and Brunauer-Emmett-Teller (BET) methods. The results show that as compared to low-molecular weight surfactant, this polymer significantly expanded the interlayer spacing and thus more TiO₂ could be intercalated into MMT. The specific surface area of polymer/TiO₂ pillared MMT was increased by 13% with comparison to TiO₂ pillared MMT and rose to 241.52 m²/g. Both the pore diameter and volume are doubled, and thus the pore structure is optimized markedly. The investigation on the photo-catalytic degradation of methyl orange in aqueous solution show that the modulation of polymer molecules raise the adsorption content of montmorillonite and improve the photo-catalytic activity. Therefore, this process provides a novel alternative to design and prepare the advanced eco-catalytic materials with high adsorption capacity and photo-catalytic activity.

Keywords

null