Tuning S Doping in Porous Carbon for Enhanced Initial Coulombic Efficiency and Rate Performance for Sodium/Potassium-Ion Batteries

Abstract

Amorphous carbon has emerged as a promising anode material for sodium-ion (SIBs) and potassium-ion batteries (PIBs) due to its high specific capacity, abundant defects, and low production cost. Nevertheless, its practical application remains hindered by suboptimal rate performance and low initial Coulombic efficiency (ICE). Heteroatom doping, particularly with sulfur (S), has proven to be an effective strategy for addressing these limitations. In this study, S was successfully incorporated in a controlled amount into the amorphous porous C framework via a combination of low-temperature carbonization and a facile fumigation process. The introduction of S and the low-temperature treatment synergistically induced a higher density of structural defects, which contributed to significantly enhanced rate performance of the sulfur–carbon (S/C) composite. Furthermore, controlled S doping facilitated the formation of a thinner and more stable solid electrolyte interphase (SEI) during the initial cycling, thereby minimizing irreversible sodium consumption and leading to a substantial improvement in ICE. As an anode for SIBs, the optimized S/C composite delivers a high reversible capacity of 480 mAh g⁻¹ at 0.1 A g⁻¹ and maintains a capacity of 232.6 mAh g⁻¹ even at 5.0 A g⁻¹. Notably, an ICE of 83.1% is achieved under a current density of 0.1 A g⁻¹. When applied as the anode for PIBs, the composite exhibits a reversible capacity of 439.2 mAh g⁻¹ and an ICE of 61.2% at the same current density. This work provides a viable and scalable approach to simultaneously enhance the rate performance and ICE of amorphous C.

Keywords

amorphous porous carbon / anode materials / ICE / rate performance / sulfur doping

References

[1] C. Sun, X. Zhang, Y. An, C. Li, L. Wang, X. Zhang, X. Sun, K. Wang, H. Zhang, Y. Ma, Energy Environ. Mater. 2023, 6, e12603.

[2] Z. Yang, S. Zhao, R. Jiao, G. Hao, Y. Liu, W. He, J. Chen, G. Jia, J. Cui, S. Li, Energy Environ. Mater. 2024, 7, e12674.

[3] L. Liu, S. Li, L. Hu, X. Liang, W. Yang, X. Yang, K. Hu, C. Hou, Y. Han, S. Chou, Carbon Energy 2024, 6, e531.

[4] Z. Li, L. Ma, T. W. Surta, C. Bommier, Z. Jian, Z. Xing, W. F. Stickle, M. Dolgos, K. Amine, J. Lu, T. Wu, X. Ji, ACS Energy Lett. 2016, 1, 395.

[5] J. Ni, L. Li, J. Lu, ACS Energy Lett. 2018, 3, 1137.

[6] A. Rudola, K. Saravanan, C. W. Mason, P. Balaya, J. Mater. Chem. A 2013, 1, 2653.

[7] C. Liu, J. Alloys Compd. 2025, 1010, 177439.

[8] Y. Li, Y. S. Hu, H. Li, L. Chen, X. Huang, J. Mater. Chem. A 2016, 4, 96.

[9] W. Li, M. Zhou, H. Li, K. Wang, S. Cheng, K. Jiang, Energy Environ. Sci. 2015, 8, 2916.

[10] Q. Li, Y. Zhu, Z. Pinyi, C. Yuan, M. Chen, C. Wang, Carbon 2018, 129, 85.

[11] S. Zhong, H. Liu, D. Wei, J. Hu, H. Zhang, H. Hou, M. Peng, G. Zhang, H. Duan, Chem. Eng. J. 2020, 395, 125054.

[12] H. Zhang, T. Yang, Z. Sun, R. Li, X. Wang, Z. Chen, Nano Energy 2025, 146, 111515.

[13] Z. Duan, X. Ye, J. Chen, J. Chen, J. Li, Z. Li, J. Energy Storage 2025, 114, 115674.

[14] D. Qin, L. Wang, X. Zeng, J. Shen, F. Huang, G. Xu, M. Zhu, Z. Dai, Energy Storage Mater. 2023, 54, 498.

[15] Z. Liu, J. Zhao, H. Yao, X. He, H. Zhang, Y. Qiao, X. Wu, L. Li, S. Chou, Chem. Sci. 2024, 15, 8478.

[16] Y. Wang, M. Li, Y. Zhang, N. Zhang, Chem. Eng. J. 2024, 499, 156115.

[17] R. Yang, Y. Chen, Y. Pan, M. Kim, H. Liu, C. K. W. Lee, Y. Huang, A. Tang, F. Tu, T. Li, M. G. Li, Nat. Commun. 2025, 16, 2386.

[18] Z. Tang, R. Zhang, H. Wang, S. Zhou, Z. Pan, Y. Huang, D. Sun, Y. Tang, X. Ji, K. Amine, M. Shao, Nat. Commun. 2023, 14, 6024.

[19] Z. Hu, P. Gao, S. Ju, Y. Li, T. Zhang, C. Lu, T. Huang, P. Liu, Y. Lv, M. Guo, W. Zhang, W. Teng, G. Xia, S. Zhu, D. Sun, X. Yu, Nat. Commun. 2025, 16, 3979.

[20] M. Thommes, K. Kaneko, A. V. Neimark, J. P. Olivier, F. Rodriguez-Reinoso, J. Rouquerol, K. S. W. Sing, Pure Appl. Chem. 2015, 87, 1051.

[21] H. J. Shin, S.-W. Park, S. Park, D.-W. Kim, Adv. Sci. 2023, 10, 2205424.

[22] W. Liu, T. Shi, F. Liu, C. Yang, F. Qiao, K. Han, C. Han, J. Meng, X. Wang, Nano 2024, 14, 550.

[23] A. Sadezky, H. Muckenhuber, H. Grothe, R. Niessner, U. Poschl, Carbon 2005, 43, 1731.

[24] J. Zhao, X.-X. He, W.-H. Lai, Z. Yang, X.-H. Liu, L. Li, Y. Qiao, Y. Xiao, L. Li, X. Wu, S.-L. Chou, Adv. Energy Mater. 2023, 13, 2300444.

[25] Z. Li, Y. Chen, Z. Jian, H. Jiang, J. J. Razink, W. F. Stickle, J. C. Neuefeind, X. Ji, Chem. Mater. 2018, 30, 4536.

[26] L. Zhao, S. Sun, J. Lin, L. Zhong, L. Chen, J. Guo, J. Yin, H. N. Alshareef, X. Qiu, W. Zhang, Nano-Micro Lett. 2023, 15, 41.

[27] B. Cao, S. Gao, Y. Ma, D. Zhang, Z. Guo, M. Du, Z. Xin, C. Zhou, H. Liu, J. Colloid Interface Sci. 2024, 661, 598.

[28] S. W. Lee, N. Yabuuchi, B. M. Gallant, S. Chen, B.-S. Kim, P. T. Hammond, Y. Shao-Horn, Nat. Nanotechnol. 2010, 5, 531.

[29] D. Qiu, B. Zhang, T. Zhang, T. Shen, Z. Zhao, Y. Hou, ACS Nano 2022, 16, 21443.

[30] J. Meng, G. Jia, H. Yang, M. Wang, Front. Chem. 2022, 10, 986541.

[31] J. S. Kim, T. H. Hwang, B. G. Kim, J. Min, J. W. Choi, Adv. Funct. Mater. 2014, 24, 5359.

[32] X. Feng, Y. Li, M. Zhang, Y. Li, Y. Gong, M. Liu, Y. Bai, C. Wu, ACS Appl. Mater. Interfaces 2022, 14, 50992.

[33] P. Komen, L. Ngamwongwan, S. Jungthawan, A. Junkaew, S. Suthirakun, ACS Appl. Mater. Interfaces 2021, 13, 57306.

[34] E. Hao, W. Liu, S. Liu, Y. Zhang, H. Wang, S. Chen, F. Cheng, S. Zhao, H. Yang, J. Mater. Chem. A 2017, 5, 2204.

[35] X. Zhang, G. Zhu, M. Wang, J. Li, T. Lu, L. Pan, Carbon 2017, 116, 686.

[36] W. Liu, X. Wu, F. Wang, Z. Wu, Chem. Commun. 2025, 61, 4236.

[37] Y. Qu, M. Guo, X. Wang, C. Yuan, J. Alloys Compd. 2019, 791, 874.

[38] X. Wang, S. Wang, K. Shen, S. He, X. Hou, F. Chen, J. Mater. Chem. A 2020, 8, 4007.

[39] Q. Zhao, Y. Meng, L. Yang, X. He, B. He, Y. Liu, D. Xiao, J. Colloid Interface Sci. 2019, 551, 61.

[40] W. Cha, I. Y. Kim, J. M. Lee, S. Kim, K. Ramadass, K. Gopalakrishnan, S. Premkumar, S. Umapathy, A. Vinu, ACS Appl. Mater. Interfaces 2019, 11, 27192.

[41] G. Zhao, G. Zou, H. Hou, P. Ge, X. Cao, X. Ji, J. Mater. Chem. A 2017, 5, 24353.

[42] Y. Li, B. Ni, X. Li, X. Wang, D. Zhang, Q. Zhao, J. Li, T. Lu, W. Mai, L. Pan, Nano-Micro Lett. 2019, 11, 60.

[43] J. Yang, X. Zhou, D. Wu, X. Zhao, Z. Zhou, Adv. Mater. 2017, 29, 1604108.

[44] C. Bommier, W. Luo, W.-Y. Gao, A. Greaney, S. Ma, X. Ji, Carbon 2014, 76, 165.

[45] Z. Chen, J. Liao, W. Li, Y. Song, C. Chen, J. Yang, Z. Xu, T. Feng, M. Wu, Appl. Surf. Sci. 2020, 506, 144909.

[46] L. Chen, M. Chen, Q. Meng, J. Zhang, G. Feng, X. Ai, Y. Cao, Z. Chen, Angew. Chem. Int. Ed. 2024, 63, e202407717.

[47] T. He, Q. An, M. Zhang, N. Kang, D. Kong, H. Song, S. Wu, Y. Wang, J. Hu, D. Zhang, K. Lv, S. Huang, ACS Nano 2024, 18, 5672.

[48] Z. Lu, H. Yang, Y. Guo, H. Lin, P. Shan, S. Wu, P. He, Y. Yang, Q.-H. Yang, H. Zhou, Nat. Commun. 2024, 15, 3497.

[49] H. Fang, Y. Huang, W. Hu, Z. Song, X. Wei, J. Geng, Z. Jiang, H. Qu, J. Chen, F. Li, Angew. Chem. Int. Ed. 2024, 63, e202400539.

[50] Z. Lu, C. Geng, H. Yang, P. He, S. Wu, Q.-H. Yang, H. Zhou, Proc. Natl Acad. Sci. USA 2022, 119, e2210203119.

[51] G. Maresca, A. Petrongari, S. Brutti, G. B. Appetecchi, ChemSusChem 2023, 16, e202300840.

[52] J. He, A. Bhargav, L. Su, H. Charalambous, A. Manthiram, Nat. Commun. 2023, 14, 6568.

[53] C. Wang, Z. Sun, Y. Liu, L. Liu, X. Yin, Q. Hou, J. Fan, J. Yan, R. Yuan, M. Zheng, Q. Dong, Nat. Commun. 2024, 15, 6292.

[54] Z. Chen, X. Wu, Z. Sun, J. Pan, J. Han, Y. Wang, H. Liu, Y. Shen, J. Li, D.-L. Peng, Q. Zhang, Adv. Energy Mater. 2024, 14, 2400132.

[55] Q. Xu, S. Tang, N. Li, Y. Wang, X. Zhao, X. Zhang, S. Geng, B. Yuan, S. Wang, Z. Ouyang, M. Liao, L. Ma, M. Shang, Y. Sun, H. Peng, H. Sun, Nat. Commun. 2025, 16, 1946.

[56] M. Mense, M. M. Bela, S. P. Kühn, I. Cekic-Laskovic, M. Börner, S. Wiemers-Meyer, M. Winter, S. Nowak, Commun. Chem. 2025, 8, 31.

[57] C. Qiu, A. Kumar, D. Qiu, M. Tabish, J. Zhang, Z. Jiang, A. Li, G. Yasin, X. Chen, H. Song, J. Mater. Chem. A 2023, 11, 22187.

[58] M. Song, Z. Yi, R. Xu, J. Chen, J. Cheng, Z. Wang, Q. Liu, Q. Guo, L. Xie, C. Chen, Energy Storage Mater. 2022, 51, 620.

[59] E. O. Eren, C. Esen, E. Scoppola, Z. Song, E. Senokos, H. Zschiesche, D. Cruz, I. Lauermann, N. V. Tarakina, B. Kumru, M. Antonietti, P. Giusto, Adv. Sci. 2024, 11, 2310196.

[60] Nagmani, S. Manna, S. Puravankara, Chem. Commun. 2024, 60, 3071.

[61] X. Gao, X. Dong, Z. Xing, S. Jamila, H. Hong, H. Jiang, J. Zhang, Z. Ju, Nanoscale 2023, 15, 1568.

[62] W. Li, X. Lu, B. W. Biney, J. Li, Y. Yan, K. Chen, J. Colloid Interface Sci. 2025, 677, 312.

Rights & permissions

2026 The Author(s). Energy & Environmental Materials published by John Wiley & Sons Australia, Ltd on behalf of Zhengzhou University.