Constructing Atomically Dispersed Bimetallic Electrocatalyst by a Topologically Confined Pre-Anchoring Strategy for Enhanced Oxygen Reduction Reaction and Zn-Air Battery

Abstract

The development of atomically dispersed multi-metallic catalysts is imperative for tailoring catalytic performance and elucidating structure–activity relationships. However, synthesizing such precisely engineered architectures while maintaining atomic dispersion of distinct metal centers remains a formidable challenge due to thermodynamic instability and synthetic complexity. We herein propose a topological confinement pre-anchoring strategy via pre-anchoring spatially resolved Zn/Fe dual-metal sources in a structurally engineered metal–organic framework precursor to synthesize atomically dispersed ZnFe bimetallic single-atom catalysts. Extended X-ray absorption fine structure measurements and X-ray absorption near-edge structure reveal that the atomically dispersed Zn/Fe metal sites and electronic redistribution in ZnFe bimetallic single-atom catalysts. The ultrahigh surface area, hierarchical pore, and synergistic effect between Zn/Fe can greatly favor the exposure of the active site, mass transport, and improvement of intrinsic activity. Consequently, the ZnFe bimetallic single-atom catalyst demonstrates superior oxygen reduction reaction performance, achieving a half-wave potential of 0.86 V and delivering a kinetic current density of 10.1 mA cm⁻² at 0.85 V versus RHE in 0.1 M KOH electrolyte. These metrics not only surpass those of commercial Pt/C, but also rival the highest-performing catalysts reported to date. The Zn-air battery built with ZnFe bimetallic single-atom catalyst exhibits high power density (278.5 mW cm⁻²) and specific discharging capacities (657 mAh g⁻¹). This work provides a new design pathway for constructing atomically dispersed multi-metal electrocatalysts for high-performance energy-related applications.

Keywords

bimetallic single atom catalyst / metal–organic frameworks / oxygen reduction reaction / Zn-air battery

References

[1] A. Kulkarni, S. Siahrostami, A. Patel, J. K. Norskov, Chem. Rev. 2018, 118, 2302.

[2] X. X. Wang, M. T. Swihart, G. Wu, Nat. Catal. 2019, 2, 578.

[3] M. M. Liu, L. L. Wang, K. N. Zhao, S. S. Shi, Q. S. Shao, L. Zhang, X. L. Sun, Y. F. Zhao, J. J. Zhang, Energy Environ. Sci. 2019, 12, 2890.

[4] X. L. Tian, X. F. Lu, B. Y. Xia, X. W. Lou, Joule 2020, 4, 45.

[5] Y. Gao, B. Z. Liu, D. S. Wang, Adv. Mater. 2023, 35, 2209654.

[6] C. Bai, S. Li, K. Ji, M. Wang, D. Kong, Energy Mater. 2023, 3, 300041.

[7] D. Zhang, X. Zhang, X. Li, C. Feng, Y. Chu, C. Chen, Z. Kou, Energy Mater. 2025, 5, 500014.

[8] X. C. Yan, Y. Jia, X. D. Yao, Chem. Soc. Rev. 2018, 47, 7628.

[9] X. Q. Wang, Z. J. Li, Y. T. Qu, T. W. Yuan, W. Y. Wang, Y. Wu, Y. D. Li, Chem-Us 2019, 5, 1486.

[10] M. H. Shao, Q. W. Chang, J. P. Dodelet, R. Chenitz, Chem. Rev. 2016, 116, 3594.

[11] X. Wang, M. H. Yu, X. L. Feng, Escience 2023, 3, 100141.

[12] Y. G. Zhao, D. P. A. Saseendran, C. Huang, C. A. Triana, W. R. Marks, H. Chen, H. Zhao, G. R. Patzke, Chem. Rev. 2023, 123, 6257.

[13] S. C. Wang, M. Y. Zhang, X. Q. Mu, S. L. Liu, D. S. Wang, Z. H. Dai, Energy Environ. Sci. 2024, 17, 4847.

[14] Y. Wang, J. Mao, X. G. Meng, L. Yu, D. H. Deng, X. H. Bao, Chem. Rev. 2019, 119, 1806.

[15] L. Jiao, G. Wan, R. Zhang, H. Zhou, S. H. Yu, H. L. Jiang, Angew. Chem. Int. Ed. 2018, 57, 8525.

[16] Y. S. Wei, M. Zhang, R. Q. Zou, Q. Xu, Chem. Rev. 2020, 120, 12089.

[17] Y. X. Wang, H. Y. Su, Y. H. He, L. G. Li, S. Q. Zhu, H. Shen, P. F. Xie, X. B. Fu, G. Y. Zhou, C. Feng, D. K. Zhao, F. Xiao, X. J. Zhu, Y. C. Zeng, M. H. Shao, S. W. Chen, G. Wu, J. Zeng, C. Wang, Chem. Rev. 2020, 120, 12217.

[18] D. Zhao, Z. W. Zhuang, X. Cao, C. Zhang, Q. Peng, C. Chen, Y. D. Li, Chem. Soc. Rev. 2020, 49, 2215.

[19] H. Li, F. Pan, C. Qin, T. Wang, K.-J. Chen, Adv. Energy Mater. 2023, 13, 2301378.

[20] S. Kment, A. Bakandritsos, I. Tantis, H. Kmentová, Y. P. Zuo, O. Henrotte, A. Naldoni, M. Otyepka, R. S. Varma, R. Zboril, Chem. Rev. 2024, 124, 11767.

[21] D. C. Zhong, Y. N. Gong, C. Zhang, T. B. Lu, Chem. Soc. Rev. 2023, 52, 3170.

[22] P. Rao, X. Han, H. Sun, F. Wang, Y. Liang, J. Li, D. Wu, X. Shi, Z. Kang, Z. Miao, P. Deng, X. Tian, Angew. Chem. Int. Ed. 2025, 64, e202415223.

[23] M. M. Tong, F. F. Sun, Y. Xie, Y. Wang, Y. Q. Yang, C. G. Tian, L. Wang, H. G. Fu, Angew. Chem. Int. Ed. 2021, 60, 14005.

[24] Q. Q. Zhang, J. Q. Guan, Adv. Funct. Mater. 2020, 30, 202000768.

[25] D. W. Liu, K. Srinivas, X. Chen, F. Ma, X. J. Zhang, X. Q. Wang, B. Wang, Y. F. Chen, J. Colloid Interface Sci. 2022, 624, 680.

[26] W. X. Xu, R. Zeng, M. Rebarchik, A. Posada-Borbón, H. Q. Li, C. J. Pollock, M. Mavrikakis, H. D. Abruña, J. Am. Chem. Soc. 2024, 146, 2593.

[27] H. Liu, P. Zhu, D. Yang, C. K. Zhong, J. L. Li, X. Liang, L. G. Wang, H. Yin, D. S. Wang, Y. D. Li, J. Am. Chem. Soc. 2024, 146, 2132.

[28] M. Liu, N. Li, S. Cao, X. Wang, X. Lu, L. Kong, Y. Xu, X.-H. Bu, Adv. Mater. 2022, 34, 2107421.

[29] Z. Wang, X. Y. Jin, R. J. Xu, Z. B. Yang, S. D. Ma, T. Yan, C. Zhu, J. Fang, Y. P. Liu, S. J. Hwang, Z. J. Pan, H. J. Fan, ACS Nano 2023, 17, 8622.

[30] Y. S. Wei, L. Sun, M. Wang, J. Hong, L. Zou, H. Liu, Y. Wang, M. Zhang, Z. Liu, Y. Li, S. Horike, K. Suenaga, Q. Xu, Angew. Chem. Int. Ed. 2020, 59, 16013.

[31] Y. Wang, Z. Li, P. Zhang, Y. Pan, Y. Zhang, Q. Cai, S. R. P. Silva, J. Liu, G. Zhang, X. Sun, Nano Energy 2021, 87, 106147.

[32] S. J. Lyle, R. W. Flaig, K. E. Cordova, O. M. Yaghi, J. Chem. Educ. 2018, 95, 1512.

[33] W. Zhu, L. Zhang, S. Liu, A. Li, X. Yuan, C. Hu, G. Zhang, W. Deng, K. Zang, J. Luo, Y. Zhu, M. Gu, Z.-J. Zhao, J. Gong, Angew. Chem. Int. Ed. 2020, 59, 12664.

[34] F. Yang, P. Song, X. Liu, B. Mei, W. Xing, Z. Jiang, L. Gu, W. Xu, Angew. Chem. Int. Ed. 2018, 57, 12303.

[35] Z. P. Zhang, J. T. Sun, F. Wang, L. M. Dai, Angew. Chem. Int. Ed. 2018, 57, 9038.

[36] Q. Yang, C.-C. Yang, C.-H. Lin, H.-L. Jiang, Angew. Chem. Int. Ed. 2019, 58, 3511.

[37] J. Li, S. Chen, N. Yang, M. Deng, S. Ibraheem, J. Deng, J. Li, L. Li, Z. Wei, Angew. Chem. Int. Ed. 2019, 58, 7035.

[38] Y. P. Ku, K. Ehelebe, A. Hutzler, M. Bierling, T. Böhm, A. Zitolo, M. Vorokhta, N. Bibent, F. D. Speck, D. Seeberger, I. Khalakhan, K. J. J. Mayrhofer, S. Thiele, F. Jaouen, S. Cherevko, J. Am. Chem. Soc. 2022, 144, 9753.

[39] X. Cao, C. Zhu, Q. Hong, X. Chen, K. Wang, Y. Shen, S. Liu, Y. Zhang, Angew. Chem. Int. Ed. 2023, 62, e202302463.

[40] Y. Chen, S. Ji, Y. Wang, J. Dong, W. Chen, Z. Li, R. Shen, L. Zheng, Z. Zhuang, D. Wang, Y. Li, Angew. Chem. Int. Ed. 2017, 56, 6937.

RIGHTS & PERMISSIONS

2025 The Author(s). Energy & Environmental Materials published by John Wiley & Sons Australia, Ltd on behalf of Zhengzhou University.