Nanoflower Mn_xNi_2−xP as efficient bifunctional catalyst for hydrogen production with urea-assisted energy-saving in alkaline freshwater and seawater

Abstract

To achieve efficient and stable hydrogen production while addressing the corrosive effects of seawater on electrodes, integrating the energy-saving urea oxidation reaction (UOR) with the hydrogen evolution reaction (HER) presents a promising low-energy solution. However, developing low-cost, high-performance bifunctional electrocatalysts for both HER and UOR remains a significant challenge. In this work, we prepared bifunctional electrocatalysts featuring Mn_xNi_2−xP nanoflower structures grown on nickel foam using a simple hydrothermal phosphatization method. These catalysts demonstrated excellent performance in alkaline freshwater and seawater, with notably low overpotentials of 251 and 257 mV for HER, and 1.33 and 1.37 V for UOR. Combining its bifunctional activity in UOR and HER in a two-electrode system, an energy saving of 0.19 V potential compared to water electrolysis through water oxidation can be acquired to reach 100 mA cm⁻² current density. Moreover, the catalyst also maintains fairly stable after long-term testing, indicating its potential for efficient and energy-saving hydrogen production. Our study reveals that the synergistic interaction between Ni and Mn metals enhances the electronic structure of the electrocatalysts, significantly boosting both UOR and HER activities. Additionally, Mn doping alters the morphological structure, creating nanoflowers with abundant active sites, while nickel-iron phosphides improve the catalyst's corrosion resistance in seawater. This work provides valuable insights into the design of low-cost, stable non-precious metal electrocatalysts for seawater and freshwater splitting, combining hydrogen evolution with urea-assisted energy-saving.

Keywords

bifunctional catalyst / Mn_xNi_2−xP / seawater splitting / urea-assisted energy-saving

References

[1] Patil SJ, Chodankar NR, Hwang SK, et al. Co-metal-organic framework derived CoSe₂@MoSe₂ core-shell structure on carbon cloth as an efficient bifunctional catalyst for overall water splitting. Chem Eng J. 2022; 429:132379.

[2] Zhao D, Zhuang ZW, Cao X, et al. Atomic site electrocatalysts for water splitting, oxygen reduction and selective oxidation. Chem Soc Rev. 2020; 49(7): 2215-2264.

[3] Sahoo DP, Das KK, Mansingh S, Sultana S, Parida K. Recent progress in first row transition metal Layered double hydroxide (LDH) based electrocatalysts towards water splitting: a review with insights on synthesis. Coord Chem Rev. 2022; 469:214666.

[4] Chen J, Zhang L, Li J, et al. High-efficiency overall alkaline seawater splitting: using a nickel-iron sulfide nanosheet array as a bifunctional electrocatalyst. J Mater Chem A. 2022; 11(3): 1116-1122.

[5] Ju X, He X, Sun Y, et al. Fabrication of a hierarchical NiTe@NiFe-LDH core-shell array for high-efficiency alkaline seawater oxidation. iScience. 2023; 27(1):108736.

[6] Yangyang L, Tao Z, Jugang M, et al. Study the effect of lye flow rate, temperature, system pressure and different current density on energy consumption in catalyst test and 500W commercial alkaline water electrolysis. Mater Today Phys. 2022; 22:100606.

[7] Liu W, Niu X, Feng J, et al. Tunable heterogeneous FeCo alloy-Mo0.82N bifunctional electrocatalysts for temperature-adapted Zn-air batteries. ACS Appl Mater Interfaces. 2023; 15(12): 15344-15352.

[8] Lu Y, Zhang H, Ang EH, et al. In-situ self-catalyzed growth of bimetallic nanoparticles/carbon nanotubes: a flexible binder-free electrocatalyst for high-performance oxygen evolution reaction. Mater Today Phys. 2021; 16:100303.

[9] Song M, Yang X, Ma J, Deng X, Gao H. Tailored nanocomposite FeNiB/MnO₂/rGO@NF electrocatalyst for highly efficient and stable oxygen evolution reaction in freshwater and seawater environments. Mater Today Chem. 2024; 36:101957.

[10] Qi R, Bu H, Yang X, Song M, Ma J, Gao H. Multifunctional molybdenum-tuning porous nickel-cobalt bimetallic phosphide nanoarrays for efficient water splitting and energy-saving hydrogen production. J Colloid Interface Sci. 2023; 653: 1246-1255.

[11] Yang X, Bu H, Qi R, et al. A highly efficient and long-term durable electrocatalyst for oxygen evolution in alkaline seawater by growing Ni_1.5Fe_1.5B on the NiMoO₄ nanorods. Mater Today Chem. 2023; 35:101849.

[12] Yang X, Bu H, Qi R, et al. Boosting urea-assisted water splitting over P-MoO₂@CoNiP through Mo leaching/reabsorption coupling CoNiP reconstruction. J Colloid Interface Sci. 2024; 676: 445-458.

[13] Liu F, Zhang L, Wang L, Cheng F. The electrochemical tuning of transition metal-based materials for electrocatalysis. Electrochem Energy Rev. 2021; 4(1): 146-168.

[14] Song J, Wei C, Huang Z-F, et al. A review on fundamentals for designing oxygen evolution electrocatalysts. Chem Soc Rev. 2020; 49(7): 2196-2214.

[15] Liu W, Liu W, Hou T, et al. Coupling Co-Ni phosphides for energy-saving alkaline seawater splitting. Nano Res. 2024; 17(6): 4797-4806.

[16] Khan MA, Al-Attas T, Roy S, et al. Seawater electrolysis for hydrogen production: a solution looking for a problem? Energy Environ Sci. 2021; 14(9): 4831-4839.

[17] Liu H, Shen W, Jin H, et al. High-performance alkaline seawater electrolysis with anomalous chloride promoted oxygen evolution reaction. Angew Chem Int Ed. 2023; 135(46).

[18] Guo L, Chi J, Zhu J, Cui T, Lai J, Wang L. Dual-doping NiMoO4 with multi-channel structure enable urea-assisted energy-saving H₂ production at large current density in alkaline seawater. Appl Catal, B: Environ Energy. 2022.

[19] Liu W, Que W, Yin R, et al. Ferrum-molybdenum dual incorporated cobalt oxides as efficient bifunctional anti-corrosion electrocatalyst for seawater splitting. Appl Catal, B: Environ Energy. 2023; 328:122488.

[20] Sun F, Qin J, Wang Z, et al. Energy-saving hydrogen production by chlorine-free hybrid seawater splitting coupling hydrazine degradation. Nat Commun. 2021; 12(1):4182.

[21] Tuo W, Yifei C, Huimin W, Chuanqi F, Yu D, He M. N-doped M/CoO (M=Ni, Co, and Mn) hybrid grown on nickel foam as efficient electrocatalyst for the chemical-assisted water electrolysis. Int J Hydrogen Energy. 2021.

[22] Sun H, Liu J, Kim H, et al. Ni-doped CuO nanoarrays activate urea adsorption and stabilizes reaction intermediates to achieve high-performance urea oxidation catalysts. Adv Sci. 2022; 9(34).

[23] Morales DM, Jambrec D, Kazakova MA, et al. Electrocatalytic conversion of glycerol to oxalate on Ni oxide nanoparticles-modified oxidized multiwalled carbon nanotubes. ACS Catal. 2022; 12(2): 982-992.

[24] Zhang L, Si R, Liu H, et al. Atomic layer deposited Pt-Ru dual-metal dimers and identifying their active sites for hydrogen evolution reaction. Nat Commun. 2019; 10(1):4936.

[25] Wang H-Y, Wang L, Ren J-T, Tian W-W, Sun M-L, Yuan Z-Y. Heteroatom-Induced accelerated kinetics on nickel selenide for highly efficient hydrazine-assisted water splitting and Zn-hydrazine battery. Nano-Micro Lett. 2023; 15(1):155.

[26] Ding R, Qi L, Jia M, Wang H. Correction: facile synthesis of mesoporous spinel NiCo₂O₄ nanostructures as highly efficient electrocatalysts for urea electro-oxidation. Nanoscale. 2015; 6(3): 1369-1376.

[27] Zhang J, Song X, Kang L, et al. Stabilizing efficient structures of superwetting electrocatalysts for enhanced urea oxidation reactions. Chem Catal. 2022; 2(11): 3254-3270.

[28] Wang J, Sun Y, Qi Y, Wang C. Vanadium-doping and interface engineering for synergistically enhanced electrochemical overall water splitting and urea electrolysis. ACS Appl Mater Interfaces. 2021; 13(48): 57392-57402.

[29] Xu Q, Yu T, Chen J, et al. Coupling interface constructions of FeNi₃-MoO₂ heterostructures for efficient urea oxidation and hydrogen evolution reaction. ACS Appl Mater Interfaces. 2021; 13(14): 16355-16363.

[30] Xu S, Ruan X, Ganesan M, Wu J, Ravi SK, Cui X. Transition metal-based catalysts for urea oxidation reaction (UOR): catalyst design strategies, applications, and future perspectives. Adv Funct Mater. 2024; 34(18).

[31] Singh RK, Rajavelu K, Montag M, Schechter A. Advances in catalytic electrooxidation of urea: a review. Energy Technol. 2021; 9(8).

[32] Colsmann A, Leonhard T, Schulz AD, Röhm H. Comment on “ferroelectricity-free lead halide perovskites” by A. Gómez, Q. Wang, A. R. Goñi, M. Campoy-Quiles and A. Abate, Energy Environ. Sci., 2019, 12, 2537. Energy Environ Sci. 2020; 13(6): 1888-1891.

[33] Wang P, Qi J, Chen X, et al. Three-Dimensional heterostructured NiCoP@NiMn-layered double hydroxide arrays supported on Ni foam as a bifunctional electrocatalyst for overall water splitting. ACS Appl Mater Interfaces. 2020; 12(4): 4385-4395.

[34] Ahn SH, Manthiram A. Direct growth of ternary Ni-Fe-P porous nanorods onto nickel foam as a highly active, robust bi-functional electrocatalyst for overall water splitting. J Mater Chem A. 2017; 5(6): 2496-2503.

[35] Qian Z, Maosong S, Jie Z, et al. New strategy to synthesize oxygen vacancy-rich CoFe nanoneedles for overall water splitting and urea electrolysis. Chem Eng J. 2021.

[36] Yanhong W, Nannan C, Xiaoqiang D, Xinghua H, Xiaoshuang Z. Transition metal atoms M (M = Mn, Fe, Cu, Zn) doped nickel-cobalt sulfides on the Ni foam for efficient oxygen evolution reaction and urea oxidation reaction. J Alloys Compd. 2021.

[37] Wang Y, Dong Q, Du X, Zhang X. Mn-doped nickel-copper phosphides as oxygen evolution reaction electrocatalyst in alkaline seawater solution. Int J Hydrogen Energy. 2024; 69: 895-904.

[38] Lei L, Yin Z, Huang D, et al. Metallic Co and crystalline Co-Mo oxides supported on graphite felt for bifunctional electrocatalytic hydrogen evolution and urea oxidation. J Colloid Interface Sci. 2021; 612: 413-423.

[39] Huang C-J, Zhan Q-N, Xu H-M, Zhu H-R, Shuai T-Y, Li G-R. Fe-doped Ni₂P/NiSe₂ composite catalysts for urea oxidation reaction (UOR) for energy-saving hydrogen production by UOR-assisted water splitting. Inorg Chem. 2024; 63(19): 8925-8937.

[40] Yang M, Jiang Y, Qu M, et al. Strong electronic couple engineering of transition metal phosphides-oxides heterostructures as multifunctional electrocatalyst for hydrogen production. Appl Catal, B: Environ Energy. 2020; 269:118803.

[41] Zhou B, Shao Y, Li Z, Yang W, Ren X, Hao Y. Efficient energy-saving hydrogen production on binder-free electrodeposited hierarchical Ni-Mn-P@Ni-Co nanostructure. Int J Hydrogen Energy. 2023; 51: 1022-1032.

[42] Modak A, Mohan R, Rajavelu K, Cahan R, Bendikov T, Schechter A. Metal-Organic polymer-derived interconnected Fe-Ni alloy by carbon nanotubes as an advanced design of urea oxidation catalysts. ACS Appl Mater Interfaces. 2021; 13(7): 8461-8473.

[43] Ji X, Zhang Y, Ma Z, Qiu Y. Oxygen vacancy-rich Ni/NiO@NC nanosheets with Schottky heterointerface for efficient urea oxidation reaction. ChemSusChem. 2020; 13(18): 5004-5014.

[44] Li X, Hu Q, Wang H, et al. Charge induced crystal distortion and morphology remodeling: formation of Mn-CoP nanowire @ Mn-CoOOH nanosheet electrocatalyst with rich edge dislocation defects. Appl Catal, B: Environ Energy. 2021; 292:120172.

[45] Wang P, Qi J, Chen X, et al. Three-Dimensional heterostructured NiCoP@NiMn-layered double hydroxide arrays supported on Ni foam as a bifunctional electrocatalyst for overall water splitting. ACS Appl Mater Interfaces. 2020; 12(4): 4385-4395.

[46] Yang SM, Tiwari SK, Zhu ZQ, et al. In situ fabrication of Mn-doped NiMoO₄ rod-like arrays as high performance OER electrocatalyst. Nanomaterials. 2023; 13(5): 827.

[47] Luo YZ, Wang P, Zhang GX, et al. Mn-doped nickel-iron phosphide heterointerface nanoflowers for efficient alkaline freshwater/seawater splitting at high current densities. Chem Eng J. 2023; 454:140061.

[48] Narasimman R, Jnanapriya G, Sujatha S, Ilangovan SA. Vertically aligned nickel-iron-phosphide nanosheets on three-dimensional porous nickel foam for overall water splitting. J Alloys Compd. 2023; 947: 947.

[49] Jin X, Li J, Xu TT, et al. Hierarchical Ni₂P@NiFe LDH heterostructural nanosheet arrays for highly efficient oxygen evolution reaction. Eur J Inorg Chem. 2021; 2021(34): 3481-3487.

[50] Jiang H, Sun MZ, Wu SL, Huang BL, Lee CS, Zhang WJ. Oxygen-Incorporated NiMoP nanotube arrays as efficient bifunctional electrocatalysts for urea-assisted energy-saving hydrogen production in alkaline electrolyte. Adv Funct Mater. 2021; 31(43).

[51] Wang T, Cao YF, Wu HM, Feng CQ, Ding Y, Mei H. N-doped M/CoO (M1/4Ni, Co, and Mn) hybrid grown on nickel foam as efficient electrocatalyst for the chemical-assisted water electrolysis. Int J Hydrogen Energy. 2022; 47(9): 5766-5778.

[52] Wu S, Wang XY, Bai JL, et al. Influence of nitrogen-doped carbon quantum dots on the electrocatalytic performance of the CoP nanoflower catalyst for OER. Langmuir. 2022; 38(37): 11210-11218.

[53] Yu JY, Chang B, Yu WQ, et al. Chromium phosphide nanoparticles embedded in porous nitrogen-/phosphorus-doped carbon as efficient electrocatalysts for a nitrogen reduction reaction. Carbon Energy. 2022; 4(2): 237-245.

[54] Wang XY, Yu X, Wu S, et al. Crystalline-amorphous interface coupling of Ni₃S₂/NiPX/NF with enhanced activity and stability for electrocatalytic oxygen evolution. ACS Appl Mater Interfaces. 2023; 15(12): 15533-15544.

[55] Wang C, Lu H, Mao Z, Yan C, Shen G, Wang X. Bimetal Schottky heterojunction boosting energy-saving hydrogen production from alkaline water via urea electrocatalysis. Adv Funct Mater. 2020; 30(21).

[56] Sinha N, Roy P. Nickel-vanadium-manganese trimetallic nitride as energy saving, efficient bifunctional electrocatalyst for alkaline water splitting via urea electrocatalysis. Inorg Chem. 2022; 62(8): 3349-3357.

[57] Lotfi N, Barati Darband G. Energy-saving electrochemical hydrogen production on dynamic hydrogen bubble-template electrodeposited Ni-Cu-Mn nano-micro dendrite. J Electrochem Soc. 2022; 169(9):096508.

[58] Yi P, Song Y, Li C, Liu R, Sun J. Heterostructured Mn-doped NiSx/NiO/Ni₃N nanoplate arrays as bifunctional electrocatalysts for energy-saving hydrogen production and urea degradation. Appl Surf Sci. 2023; 619:156789.

RIGHTS & PERMISSIONS

2025 The Author(s). EcoEnergy published by John Wiley & Sons Australia, Ltd on behalf of China Chemical Safety Association.