Fast polysulfides conversion and regulated lithium plating enabled by W₂N quantum dots for high-performance lithium sulfur batteries

Abstract

Lithium sulfur (Li-S) batteries have been regarded as one of the most promising next-generation batteries. However, the shuttle effect caused by solubility and sluggish kinetics of polysulfides on the cathode and the uneven deposition of lithium on the anode hindered its practical application seriously. Herein, we designed W₂N quantum dots (QW₂N) embedded in mesoporous carbon microspheres (MC) as catalyst (QW₂N/MC) modified on both sides of the separator. The ultrafine QW₂N associated with nitrogen vacancies provide abundant active sites to adsorb the polysulfides and induce the fast in situ conversion, which highly prevent the shuttle effect. Meanwhile, the QW₂N/MC layer on the anode side regulated the uniform deposition of lithium due to the good affinity with lithium ions. In long-term performance evaluations, the Li-S batteries achieved a reversible discharge capacity of 685.4 mAh g^-1 after 600 cycles at 1 C with a decay rate as low as 0.07% per cycle. When the sulfur loading was increased to about 7.44 mg cm^-2, it still maintained a high areal capacity of 5.97 mAh cm^-2. This study showed a novel strategy to accelerate the polysulfides conversion and regulate uniform lithium deposition simultaneously by introducing QW₂N modified separators, showing great potential in constructing high-performance Li-S batteries.

Keywords

electrocatalysis / lithium-sulfur batteries / polysulfides / quantum dots / shuttle effect

References

[1] Deng R, Wang M, Yu H, et al. Recent advances and applications toward emerging lithium-sulfur batteries: working principles and opportunities. Energy Environ Mater. 2022; 5(3): 777-799.

[2] Kim A, Oh SH, Adhikari A, Sathe BR, Kumar S, Patel R. Recent advances in modified commercial separators for lithium-sulfur batteries. J Mater Chem A. 2023; 11(15): 7833-7866.

[3] Qi M, Xie L, Han Q, Zhu L, Chen L, Cao X. An overview of the key challenges and strategies for lithium metal anodes. J Energy Storage. 2022; 47:103641.

[4] Lang S, Yu S.-H, Feng X, Krumov MR, Abruña HD. Understanding the lithium-sulfur battery redox reactions via operando confocal Raman microscopy. Nat Commun. 2022; 13(1):4811.

[5] Kim JT, Rao A, Nie H.-Y, et al. Manipulating Li₂S₂/Li₂S mixed discharge products of all-solid-state lithium sulfur batteries for improved cycle life. Nat Commun. 2023; 14(1):6404.

[6] Fujita Y, Hakari T, Sakuda A, et al. Li₂S-LiI solid solutions with ionic conductive domains for enhanced all-solid-state Li/S batteries. ACS Appl Energy Mater. 2022; 5(8): 9429-9436.

[7] Kohl M, Brückner J, Bauer I, Althues H, Kaskel S. Synthesis of highly electrochemically active Li₂S nanoparticles for lithium-sulfur-batteries. J Mater Chem A. 2015; 3(31): 16307-16312.

[8] Huang Y, Lin L, Zhang C, et al. Recent advances and strategies toward polysulfides shuttle inhibition for high-performance Li-S batteries. Adv Sci. 2022; 9(12):2106004.

[9] Li X, Chu Z, Jiang H, et al. Redistributing Li-ion flux and homogenizing Li-metal growth by N-doped hierarchically porous membranes for dendrite-free Lithium metal batteries. Energy Storage Mater. 2021; 37: 233-242.

[10] Liu S, Yu X, Yan Y, et al. Dendrite-free deposition enabled by interfacial regulation via dipole-dipole interaction in anode-free lithium metal batteries. Energy Storage Mater. 2023; 62:102959.

[11] Jin C, Huang Y, Li L, et al. A corrosion inhibiting layer to tackle the irreversible lithium loss in lithium metal batteries. Nat Commun. 2023; 14(1):8269.

[12] He X, Bresser D, Passerini S, et al. The passivity of lithium electrodes in liquid electrolytes for secondary batteries. Nat Rev Mater. 2021; 6(11): 1036-1052.

[13] Wang N, Zhang X, Ju Z, et al. Thickness-independent scalable high-performance Li-S batteries with high areal sulfur loading via electron-enriched carbon framework. Nat Commun. 2021; 12(1):4519.

[14] Wei J.-Y, Zhang X.-Q, Hou L.-P, et al. Shielding polysulfide intermediates by an organosulfur-containing solid electrolyte interphase on the lithium anode in lithium-sulfur batteries. Adv Mater. 2020; 32(37):2003012.

[15] Zou K, Jing W, Dai X, et al. A highly efficient sulfur host enabled by nitrogen/oxygen dual-doped honeycomb-like carbon for advanced lithium-sulfur batteries. Small. 2022; 18(17):2107380.

[16] He J, Chen Y, Manthiram A. Vertical Co₉S₈ hollow nanowall arrays grown on a Celgard separator as a multifunctional polysulfide barrier for high-performance Li-S batteries. Energy Environ Sci. 2018; 11(9): 2560-2568.

[17] Huang Y, Shaibani M, Gamot TD, et al. A saccharide-based binder for efficient polysulfide regulations in Li-S batteries. Nat Commun. 2021; 12(1):5375.

[18] Tong Z, Huang L, Liu H, et al. Defective graphitic carbon nitride modified separators with efficient polysulfide traps and catalytic sites for fast and reliable sulfur electrochemistry. Adv Funct Mater. 2021; 31(11):2010455.

[19] Li J, Dai L, Wang Z, et al. Cellulose nanofiber separator for suppressing shuttle effect and Li dendrite formation in lithium-sulfur batteries. J Energy Chem. 2022; 67: 736-744.

[20] Wang G, Yu M, Feng X. Carbon materials for ion-intercalation involved rechargeable battery technologies. Chem Soc Rev. 2021; 50(4): 2388-2443.

[21] Ma F, Chen Z, Srinivas K, et al. NbN quantum dots anchored hollow carbon nanorods as efficient polysulfide immobilizer and lithium stabilizer for Li-S full batteries. J Energy Chem. 2024; 88: 260-271.

[22] Zhang X, Ma F, Srinivas K, et al. Fe₃N@N-doped graphene as a lithiophilic interlayer for highly stable lithium metal batteries. Energy Storage Mater. 2022; 45: 656-666.

[23] Liu Q, Wu Y, Li D, et al. Dilute alloying to implant activation centers in nitride electrocatalysts for lithium-sulfur batteries. Adv Mater. 2023; 35(7):2209233.

[24] Liu R, Liu W, Bu Y, et al. Conductive porous laminated vanadium nitride as carbon-free hosts for high-loading sulfur cathodes in lithium-sulfur batteries. ACS Nano. 2020; 14(12): 17308-17320.

[25] Yang J.-L, Cai D.-Q, Lin Q, et al. Regulating the Li₂S deposition by grain boundaries in metal nitrides for stable lithium-sulfur batteries. Nano Energy. 2022; 91:106669.

[26] Ma F, Zhang X, Sriniva K, et al. NbN nanodot decorated N-doped graphene as a multifunctional interlayer for high-performance lithium-sulfur batteries. J Mater Chem A. 2022; 10(15): 8578-8590.

[27] Yang M, Liu P, Qu Z, et al. Nitrogen-vacancy-regulated Mo₂N quantum dots electrocatalyst enables fast polysulfides redox for high-energy-density lithium-sulfur batteries. Nano Energy. 2022; 104:107922.

[28] Zeng P, Su B, Wang X, et al. In situ reconstruction of electrocatalysts for lithium-sulfur batteries: progress and prospects. Adv Funct Mater. 2023; 33(33):2301743.

[29] Ma F, Yu B, Zhang X, et al. WN_0.67-Embedded N-doped Graphene-Nanosheet Interlayer as efficient polysulfide catalyst and absorbant for High-Performance Lithium-Sulfur batteries. Chem Eng J. 2022; 431:133439.

[30] Ma F, Chen Z, Srinivas K, et al. VN quantum dots anchored N-doped carbon nanosheets as bifunctional interlayer for high-performance lithium-metal and lithium-sulfur batteries. Chem Eng J. 2023; 459:141526.

[31] Ma F, Srinivas K, Zhang X, et al. Mo₂N quantum dots decorated N-doped graphene nanosheets as dual-functional interlayer for dendrite-free and shuttle-free lithium-sulfur batteries. Adv Funct Mater. 2022; 32(40):2206113.

[32] Dan Z, Liang W, Gong X, et al. Substitutional doping engineering toward W₂N nanorod for hydrogen evolution reaction at high current density. ACS Mater Lett. 2022; 4(7): 1374-1380.

[33] Chu S, Yu M, Liu B, et al. WO_3-x@W₂N heterogeneous nanorods cross-linked in carbon nanosheets for electrochemical potassium storage. Chem Eng J. 2022; 435:135188.

[34] Seenivasan S, Im H, Lim T, Han JW, Seo J. Schottky switch derived by metallic W₅N₄ | catalyst junction: switch-on to enhance catalytic activity and durability in water splitting reaction. Appl Catal B Environ. 2024; 340:123233.

[35] Huang Z, Yang B, Zhou Y, et al. Tungsten nitride/tungsten oxide nanosheets for enhanced oxynitride intermediate adsorption and hydrogenation in nitrate electroreduction to ammonia. ACS Nano. 2023; 17(24): 25091-25100.

[36] Hong Z, Xu Z, Wu Z, et al. Construction of core-shell Co-NC@W₂N Schottky heterojunctions for high-efficiency hydrogen evolution reaction. Appl Surf Sci. 2023; 608:155159.

[37] Wang Y, Pu Y, Yuan L, et al. Synergistic effect of WN/Mo₂C embedded in bioderived carbon nanofibers: a rational design of a shuttle inhibitor and an electrocatalyst for lithium-sulfur batteries. ACS Appl Mater Interfaces. 2022; 14(16): 18578-18588.

[38] Lei T, Chen W, Huang J, et al. Multi-functional layered WS₂ nanosheets for enhancing the performance of lithium-sulfur batteries. Adv Energy Mater. 2017; 7(4):1601843.

[39] Zhang X, Chen Y, Ma F, et al. Regulating Li uniform deposition by lithiophilic interlayer as Li-ion redistributor for highly stable lithium metal batteries. Chem Eng J. 2022; 436:134945.

RIGHTS & PERMISSIONS

2024 The Author(s). EcoEnergy published by John Wiley & Sons Australia, Ltd on behalf of China Chemical Safety Association.