Optimizing diffusion kinetics of two-dimensional structures via nano-assembling towards rapid oxygen reduction electrocatalysis

Abstract

In the realm of metal-air batteries (MABs) and fuel cells (FC), managing the thickly catalytic layer of metal-nitrogen-carbon (M-N-C) catalysts is pivotal, where the design of mass transport pathways in meso- and macro-scale is essential around the active metal sites. Such arrangements are crucial to achieving adequate three-phase boundaries and timely kinetic responses during oxygen reduction reaction (ORR). Yet, when it comes to materials with low-dimensional morphologies, such as nanolayers and nanosheets, the high aspect ratios render new challenges to structure maintenance during the pore formation, usually involving templating or etching, and against the pyrolysis collapse. Herein, we have developed an in-situ nano-assembling methodology to design hierarchical porosity in M-N-C catalysts pyrolytically derived from 2D materials. By controlling the solvothermal synthesis, the 2D nonporous precursors, fusiform ZIF-L nanolayers, are taken as a particular experimental model; they can scale down into secondary monomers and restack meso- and macro-porously. After pyrolysis, the derived Fe-N-C catalysts well inherit the hierarchical morphology and thus showcase calcined micro-pores along with a spectrum of meso- and macro-pores. Advanced characterization techniques such as the spherical aberration correction electron microscopy and X-ray absorption spectrum allow us to pinpoint atomically dispersed FeN₄ motifs as the primary active sites. Notably, their upgraded accessibility exhibits a direct correlation to the performance parameters in half-cells and prototype zinc-air batteries (ZABs). This investigation heralds new pathways for the optimization of low-dimensional nanocatalysts, aiming to exploit their activity within catalytic layers to the fullest.

Keywords

Nano-assemble / low-dimension / hierarchical porosity / diffusion kinetic / oxygen reduction reaction / zinc-air battery

References

[1] Zhao Y,Huang C.Oxygen evolution/reduction reaction catalysts: from in situ monitoring and reaction mechanisms to rational design.Chem Rev2023;123:6257-358

[2] Yan L,Zhu Q.Atomically precise electrocatalysts for oxygen reduction reaction.Chem2023;9:280-342

[3] Wang S,Lan C,Ge J.Metal–nitrogen–carbon catalysts towards acidic ORR in PEMFC: fundamentals, durability challenges, and improvement strategies.Chem Synth2023;3:15

[4] Niu Y,Liu X.Engineering iron-group bimetallic nanotubes as efficient bifunctional oxygen electrocatalysts for flexible Zn–air batteries.eScience2022;2:546-56

[5] Xu C,Ka-man Au V.Recent progress of self-supported air electrodes for flexible Zn-air batteries.J Energy Chem2024;89:110-36

[6] Gottesfeld S,Page M.Anion exchange membrane fuel cells: current status and remaining challenges.J Power Source2018;375:170-84

[7] Lee SH,Chung DY.Design principle of Fe-N-C electrocatalysts: how to optimize multimodal porous structures?.J Am Chem Soc2019;141:2035-45

[8] Lu X,Wan Y.Active site engineering toward atomically dispersed M−N−C catalysts for oxygen reduction reaction.Coordin Chem Rev2023;495:215400

[9] Xu C,Wang J.Hierarchically structured Mo_1–2C/Co-encased carbon nanotubes with multi-component synergy as bifunctional oxygen electrocatalyst for rechargeable Zn-air battery.J Power Source2024;595:234063

[10] Zhao CX,Liu JN.Intrinsic electrocatalytic activity regulation of M-N-C single-atom catalysts for the oxygen reduction reaction.Angew Chem Int Ed Engl2021;60:4448-63

[11] Song W,Ding J.Review of carbon support coordination environments for single metal atom electrocatalysts (SACS).Adv Mater2024;36:e2301477

[12] Liu Y,Wang S.Hierarchical porous yolk-shell Co-N-C nanocatalysts encaged ingraphene nanopockets for high-performance Zn-air battery.Nano Res2023;16:8893-901

[13] Luo E,Liu J.Pyrolyzed M–N_x catalysts for oxygen reduction reaction: progress and prospects.Energy Environ Sci2021;14:2158-85

[14] Fu X,Jiang G.Evolution of atomic-scale dispersion of FeNx in hierarchically porous 3D air electrode to boost the interfacial electrocatalysis of oxygen reduction in PEMFC.Nano Energy2021;83:105734

[15] Fu X,Wen G.Densely accessible Fe-Nx active sites decorated mesoporous-carbon-spheres for oxygen reduction towards high performance aluminum-air flow batteries.Appl Catal B Environ2021;293:120176

[16] Yuan Y,Shi W.Optimizing oxygen redox kinetics of M-N-C electrocatalysts via an in-situ self-sacrifice template etching strategy.Chinese Chem Lett2023;34:107807

[17] Zhang Q,Fu X.Hierarchical architecture of well-aligned nanotubes supported bimetallic catalysis for efficient oxygen redox.Adv Funct Mater2022;32:2112805

[18] Huo M,Wang Y.A heteroepitaxially grown two-dimensional metal–organic framework and its derivative for the electrocatalytic oxygen reduction reaction.J Mater Chem A2022;10:10408-16

[19] Wu S,Lei G.Single-atomic iron-nitrogen 2D MOF-originated hierarchically porous carbon catalysts for enhanced oxygen reduction reaction.Chem Eng J2022;441:135849

[20] Li C,Liu Y.Graphite-N modified single Fe atom sites embedded in hollow leaf-like nanosheets as air electrodes for liquid and flexible solid-state Zn-air batteries.Chem Eng J2023;477:146988

[21] Lee S,Oh M.Atypical hybrid metal-organic frameworks (MOFs): a combinative process for MOF-on-MOF growth, etching, and structure transformation.Angew Chem Int Ed Engl2020;59:1327-33

[22] Ma FX,Zhang G.Isolating Fe atoms in N-doped carbon hollow nanorods through a ZIF-phase-transition strategy for efficient oxygen reduction.Small2022;18:e2205033

[23] Malko D,Lopes T.In situ electrochemical quantification of active sites in Fe-N/C non-precious metal catalysts.Nat Commun2016;7:13285 PMCID:PMC5095514

[24] Gong M,Ali B,Kucernak A.Oxygen reduction reaction activity in non-precious single-atom (M-N/C) catalysts-contribution of metal and carbon/nitrogen framework-based sites.ACS Catal2023;13:6661-74 PMCID:PMC10204730

[25] Jerkiewicz G.Standard and reversible hydrogen electrodes: theory, design, operation, and applications.ACS Catal2020;10:8409-17

[26] Jahan M,Loh KP.Electrocatalytically active graphene-porphyrin MOF composite for oxygen reduction reaction.J Am Chem Soc2012;134:6707-13

[27] Wang J,Wang L.Suppressing thermal migration by fine-tuned metal-support interaction of iron single-atom catalyst for efficient ORR.Adv Funct Mater2023;33:2304277

[28] Wei C,Mandler D,Qiao SZ.Approaches for measuring the surface areas of metal oxide electrocatalysts for determining their intrinsic electrocatalytic activity.Chem Soc Rev2019;48:2518-34

[29] Pérez-miana M,Coronas J.Solventless synthesis of ZIF-L and ZIF-8 with hydraulic press and high temperature.Micropor Mesopor Mat2021;328:111487

[30] Bai W,Wang X,Fu Y.Transformation of ZIF-67 nanocubes to ZIF-L nanoframes.J Am Chem Soc2024;146:79-83

[31] Liu K,Lin Y.Insights into the activity of single-atom Fe-N-C catalysts for oxygen reduction reaction.Nat Commun2022;13:2075 PMCID:PMC9018836

[32] Chen G,Liu S.Highly accessible and dense surface single metal FeN₄ active sites for promoting the oxygen reduction reaction.Energy Environ Sci2022;15:2619-28

[33] Wei YS,Wang M.Fabricating dual-atom iron catalysts for efficient oxygen evolution reaction: a heteroatom modulator approach.Angew Chem Int Ed Engl2020;59:16013-22

[34] Zeng Y,Li B.Tuning the thermal activation atmosphere breaks the activity–stability trade-off of Fe–N–C oxygen reduction fuel cell catalysts.Nat Catal2023;6:1215-27

[35] Yuan Y,Yang L.Facet strain strategy of atomically dispersed Fe–N–C catalyst for efficient oxygen electrocatalysis.Adv Funct Mater2022;32:2206081

[36] Yang HB,Liu S.Atomically dispersed Ni(I) as the active site for electrochemical CO₂ reduction.Nat Energy2018;3:140-7

[37] Jia Q,Hafiz H.Experimental observation of redox-induced Fe-N switching behavior as a determinant role for oxygen reduction activity.ACS Nano2015;9:12496-505

[38] Khan IU,Ismail A.Structural transition from two-dimensional ZIF-L to three-dimensional ZIF-8 nanoparticles in aqueous room temperature synthesis with improved CO₂ adsorption.Mater Charact2018;136:407-16

[39] Thommes M,Neimark AV.Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report).Pure Appl Chem2015;87:1051-69

[40] Tian H,Zhang P.High durability of Fe-N-C single-atom catalysts with carbon vacancies toward the oxygen reduction reaction in alkaline media.Adv Mater2023;35:e2210714

[41] Zhang Y,Jiang G.Ordered mesoporous Fe₂N_x electrocatalysts with regulated nitrogen vacancy for oxygen reduction reaction and Zn-air battery.Nano Energy2023;115:108672

[42] Luo M.Multimetallic electrocatalyst stabilized by atomic ordering.Joule2019;3:9-10

[43] Ma Q,Zhu J.Stabilizing Fe-N-C catalysts as model for oxygen reduction reaction.Adv Sci2021;8:e2102209 PMCID:PMC8655191

[44] Gao Y,Jiang Y.Design principles and mechanistic understandings of non-noble-metal bifunctional electrocatalysts for zinc-air batteries.Nanomicro Lett2024;16:162 PMCID:PMC11250732

[45] Karthikeyan S,Ramakrishnan S.Heterostructured NiO/IrO₂ synergistic pair as durable trifunctional electrocatalysts towards water splitting and rechargeable zinc-air batteries: an experimental and theoretical study.Appl Catal B Environ Energy2024;355:124196

[46] Kumar K,Jaouen F.Review on the degradation mechanisms of metal-N-C catalysts for the oxygen reduction reaction in acid electrolyte: current understanding and mitigation approaches.Chem Rev2023;123:9265-326