A simple strategy for synthesis of b-axis-oriented MFI zeolite macro-nanosheets

Abstract

Zeolite nanosheets with shortened diffusion paths and high external surface areas have drawn significant attention. This unique morphology of zeolites can endow them with reduced diffusion resistance and high accessibility of active sites, and thereby good catalytic performance. Exploring simple synthesis strategies for zeolite nanosheets is mostly desired in zeolite chemistry. Herein, MFI zeolite nanosheets with a thickness of 50-100 nm along the b-axis and a length of 1 μm along the c-axis, namely zeolite macro-nanosheets, have been successfully synthesized via the strategy of combining pre-aging and pH regulation without the use of complex templates/additives and fluorine media. Pre-aging at a relatively high temperature of 90 °C and low alkalinity for crystallization (pH = 7.0~8.5) are found to play key roles in controlling macro-nanosheet synthesis, which can promote the formation of MFI zeolite precursors and then dissociate them into smaller ones for the following oriented aggregation during hydrothermal treatment. Crystallization kinetic studies suggest that the two-dimensional crystal growth is the intrinsic behavior of zeolite crystallization under employed conditions. This synthesis strategy can be easily extended to the synthesis of heteroatom-containing MFI macro-nanosheets, such as ZSM-5 and TS-1.

Keywords

MFI zeolite / macro-nanosheets / per-aging / pH regulation / crystallization mechanism

References

[1] Wang X,Wu Q,Xiao FS.Zeolite nanosheets for catalysis.Chem Soc Rev2022;51:2431-43

[2] Chen LH,Wang Z,Xie Z.Hierarchically structured zeolites: from design to application.Chem Rev2020;120:11194-294

[3] Choi M,Kim J,Terasaki O.Stable single-unit-cell nanosheets of zeolite MFI as active and long-lived catalysts.Nature2009;461:246-9

[4] Na K,Park W,Terasaki O.Pillared MFI zeolite nanosheets of a single-unit-cell thickness.J Am Chem Soc2010;132:4169-77

[5] Xu D,Jing Z.π-π interaction of aromatic groups in amphiphilic molecules directing for single-crystalline mesostructured zeolite nanosheets.Nat Commun2014;5:4262

[6] Shen X,Ma Y.A hierarchical MFI zeolite with a two-dimensional square mesostructure.Angew Chem Int Ed Engl2018;57:724-8

[7] Lu K,Ren L.High ethylene selectivity in Methanol-to-Olefin (MTO) reaction over MOR-zeolite nanosheets.Angew Chem Int Ed Engl2020;59:6258-62

[8] Mallette AJ,Rimer JD.Synthesis strategies and design principles for nanosized and hierarchical zeolites.Nat Synth2022;1:521-34

[9] Shamzhy M,Opanasenko M,Čejka J.MWW and MFI frameworks as model layered zeolites: structures, transformations, properties, and activity.ACS Catal2021;11:2366-96

[10] Shan Z,Meng X.Designed synthesis of TS-1 crystals with controllable b-oriented length.Chem Commun2011;47:1048-50

[11] Yang J,Miao D.Enhanced aromatic selectivity by the sheet-like ZSM-5 in syngas conversion.J Energy Chem2019;35:44-8

[12] Ali B,Arslan MT,Wang H.Controlling the selectivity and deactivation of H-ZSM-5 by tuning b-axis channel length for glycerol dehydration to acrolein.J Ind Eng Chem2020;88:127-36

[13] Duan J,Wang C.Coking-resistant polyethylene upcycling modulated by zeolite micropore diffusion.J Am Chem Soc2022;144:14269-77

[14] Lv X,Song S.Boosting propane dehydrogenation by the regioselective distribution of subnanometric CoO clusters in MFI zeolite nanosheets.ACS Appl Mater Interfaces2023;15:14250-60

[15] Chen X,Cao X,Xu R.Fabrication of silicalite-1 crystals with tunable aspect ratios by microwave-assisted solvothermal synthesis.Microporous Mesoporous Mater2009;119:217-22

[16] Lupulescu AI.Tailoring silicalite-1 crystal morphology with molecular modifiers.Angew Chem Int Ed Engl2012;51:3345-9

[17] Song X,Zhang T.Controlling the morphology and titanium coordination states of TS-1 zeolites by crystal growth modifier.Inorg Chem2020;59:13201-10

[18] Zhu P,Xia F,Liu H.Alcohol-assisted synthesis of sheet-like ZSM-5 zeolites with controllable aspect ratios.Eur J Inorg Chem2023;26:e202200664

[19] Shang Z,Zhang L,Wang X.Plate-like MFI crystal growth achieved by guanidine compounds.Inorg Chem Front2022;9:2097-103

[20] Shang Z,Zhang L,Wang X.Constructing single-crystalline hierarchical plate-like ZSM-5 zeolites with short b-axis length for catalyzing MTO reactions.Inorg Chem Front2022;9:1456-66

[21] Zhang X,Xu D.Synthesis of self-pillared zeolite nanosheets by repetitive branching.Science2012;336:1684-7

[22] Ma Y,Hu J.Design of a small organic template for synthesis of self-pillared pentasil zeolite nanosheets.J Am Chem Soc2022;144:6270-7

[23] Jain R,Linares N,Rimer JD.Spontaneous pillaring of pentasil zeolites.Adv Mater2021;33:e2100897

[24] Liu Y,Zhou T,Li H.Preparation of MFI nanosheets with distinctive microstructures via facile alkaline etching.Ind Eng Chem Res2021;60:16296-303

[25] Zhou T,Liu Y.Construction of monodispersed single-crystalline hierarchical ZSM-5 nanosheets via anisotropic etching.J Energy Chem2022;72:516-21

[26] Dai W,Tai W.Platelike MFI crystals with controlled crystal faces aspect ratio.J Am Chem Soc2021;143:1993-2004

[27] Dai W,Liu R,Guan N.Plate-like ZSM-5 zeolites as robust catalysts for the cracking of hydrocarbons.ACS Appl Mater Interfaces2022;14:11415-24

[28] Zhang L,Liu R.Design of plate-like H[Ga]MFI zeolite catalysts for high-performance methanol-to-propylene reaction.Microporous Mesoporous Mater2022;333:111767

[29] Dai W,Deng X.Synthesis and catalytic application of nanorod-like FER-type zeolites.J Mater Chem A2021;9:24922-31

[30] Wang Z,Ma Y.Transfer printing platelike MFI crystals as seeds for the preparation of silicalite-1 membranes.Microporous Mesoporous Mater2022;336:111895

[31] Hedlund J,Faisal A.Controlling diffusion resistance, selectivity and deactivation of ZSM-5 catalysts by crystal thickness and defects.J Catal2022;410:320-32

[32] Zhang J,Zhou A.Tailored synthesis of ZSM-5 nanosheets with controllable b-axis thickness and aspect ratio: strategy and growth mechanism.Chem Mater2022;34:3217-26

[33] Zhang J,Gawande K.b-Axis-oriented ZSM-5 nanosheets for efficient alkylation of benzene with methanol: synergy of acid sites and diffusion.ACS Catal2023;13:3794-805

[34] Peng Y,Wang Z.Fabrication of b-oriented MFI zeolite films under neutral conditions without the use of hydrogen fluoride.Angew Chem Int Ed Engl2015;54:5709-12

[35] Kumar S,Penn RL.A structural resolution cryo-TEM study of the early stages of MFI growth.J Am Chem Soc2008;130:17284-6

[36] Lesthaeghe D,Verstraelen T.MFI fingerprint: how pentasil-induced IR bands shift during zeolite nanogrowth.J Phys Chem C2008;112:9186-91

[37] Hsu CY,Selvin R.Rapid synthesis of MFI zeolite nanocrystals.J Phys Chem B2005;109:18804-14

[38] Shi D,Kouvatas C.Expanding the synthesis field of high-silica zeolites.Angew Chem Int Ed Engl2020;59:19576-81

[39] Qin Z,Tosheva L.Comparative study of nano-ZSM-5 catalysts synthesized in OH^- and F^- Media.Adv Funct Mater2014;24:257-64

[40] Ma Q,Ren K,Jia L.Controllable orientation growth of ZSM-5 for methanol to hydrocarbon conversion: cooperative effects of seed induction and medium pH control.Inorg Chem2022;61:13802-16

[41] Hikichi N,Naraki Y.Role of sodium cation during aging process in the synthesis of LEV-type zeolite.Microporous Mesoporous Mater2019;284:82-9

[42] Luo D,Fan D.Hydrothermal synthesis of siliceous beta zeolite by an inorganic cation-driven strategy and its crystallization mechanism.Microporous Mesoporous Mater2022;329:111557

[43] Grand J,Vicente A.One-pot synthesis of silanol-free nanosized MFI zeolite.Nat Mater2017;16:1010-5

[44] Sheng Z,Du K.Observing a zeolite nucleus (subcrystal) with a uniform framework structure and its oriented attachment without single-molecule addition.Angew Chem Int Ed Engl2021;60:13444-51

[45] Zecchina A,Spoto G.Silicalite characterization. 1. Structure, adsorptive capacity, and IR spectroscopy of the framework and hydroxyl modes.J Phys Chem1992;96:4985-90

[46] Mintova S,Vultcheva E.Crystallization kinetics of zeolite ZSM-5.Zeolites1992;12:210-5

[47] Uzcátegui D.Study of the kinetics of crystallization of zeolite MEL.Catalysis Today2005;107-8:901-5

[48] Kadja GTM,Mukti RR.A mechanistic investigation of sustainable solvent-free, seed-directed synthesis of ZSM-5 zeolites in the absence of an organic structure-directing agent.ACS Omega2021;6:925-33 PMCID:PMC7808162

[49] Xu W,Bai R,Yu J.A one-step rapid synthesis of TS-1 zeolites with highly catalytically active mononuclear TiO₆ species.J Mater Chem A2020;8:9677-83