Co-Cr-Mo-Cu alloys for clinical implants with osteogenic effect by increasing bone induction, formation and development in a rabbit model

Abstract

Background: Co-Cr-Mo alloy has been widely used in clinical implants because of its excellent mechanical and anti-corrosion properties, but there is an urgent need to address its disadvantages, such as implant-related infections and implant loosening. We synthesized Co-Cr-Mo-Cu (Co-Cu) alloys with different Cu contents to modify implant performance to be suitable as a bone-compatible implant material. Methods: Microstructure, phase content and mechanical properties of the Co-Cr-Mo alloy were characterized. Histological and immunohistochemical analyses were performed after implantation in rabbits. The experimental alloy was implanted on the lateral side of the lower tibial condyle and the tibial nodule. Results: Phase content and mechanical properties revealed that the crystallographic structure and wear resistance were changed. Experimental implantation results demonstrated that osteogenic capability was markedly enhanced, ascribed to the excellent antibacterial and osseointegration capacities of Cu phases, and with the release of Cu ions. In particular, Co-Cu alloy containing 2 wt% Cu exhibited the best osteogenic performance among all samples. Conclusions: The results indicated that osteogenic performance of the Co-Cr-Mo alloy could be enhanced by adding Cu. In particular, the Co-2Cu alloy exhibited the best properties according to both immunohistochemical and histological analyses. Our study not only provides deep insight into the osteogenic effect of Cu but presents a new Co-Cu alloy for clinical implants.

Keywords

Co-Cr-Mu-Cu alloy / Cu ion / Osteogenic capability / Implantable operation / Clinical application

References

[1] Hodgson AWE, Kurz S, Virtanen S, Fervel V, Olsson COA, Mischler S. Passive and transpassive behaviour of CoCrMo in simulated biological solutions. Electrochim Acta. 2014; 49: 2167-78.

[2] Xiang DD, Wang P, Tan XP, Chandra S, Wang C, Nai MLS, et al. Anisotropic microstructure and mechanical properties of additively manufactured Co-Cr-Mo alloy using selective electron beam melting for orthopedic implants. Mater Sci Eng A Struct Mater. 2019; 765: 138270. https://doi.org/10.1016/j.msea.2019.138270.

[3] Igual Muñoz A, Casabán Julián L. Influence of electrochemical potential on the tibocorrosion behaviour of high carbon CoCrMo biomedical alloy in simulated body fluids by electrochemical impedance spectroscopy. Electrochim Acta. 2010; 55: 5428-39.

[4] Wei D, Koizumi Y, Takashima T, Nagasako M, Chiba A. Fatigue improvement of electron beam melting-fabricated biomedical co-Cr-Mo alloy by accessible heat treatment. Mater Res Lett. 2018; 6: 93-9.

[5] Shah F, Omar O, Suska F, Snis A, Matic A, Emanuelsson L, et al. Long-term osseointegration of 3D printed CoCr constructs with an interconnected open-pore architecture prepared by electron beam melting. Acta Biomater. 2016; 36: 296-309.

[6] España FA, Balla VK, Bose S, Bandyopadhyay A. Design and fabrication of CoCrMo alloy based novel structures for load bearing implants using laser engineered net shaping. Mater Sci Eng C Mater Biol Appl. 2010; 30: 50-7.

[7] Costerton JW, Stewart PS, Greenberg EP. Bacterial biofilms: a common cause of persistent infections. Science. 1999; 284: 1318-22.

[8] Ribeiro M, Monteiro FJ, Ferraz MP. Infection of orthopedic implants with emphasis on bacterial adhesion process and techniques used in studying bacterial-material interactions. Biomat ter. 2012; 2: 176-94.

[9] Jie K, Deng P, Cao H, Feng W, Chen J, Zeng Y. Prosthesis design of animal models of periprosthetic joint infection following total knee arthroplasty: a systematic review. PLoS One. 2019; 14: e0223402. https://doi.org/10.1371/journal.pone.0223402.

[10] Ren L, Ma Z, Li M, Zhang Y, Liu W, Liao Z, et al. Antibacterial properties of Ti-6Al-4V-xCu alloys. J Mater Sci Technol. 2014; 30: 699-705.

[11] Zhang E, Li F, Wang H, Liu J, Wang C, Li M, et al. A new antibacterial titanium-copper sintered alloy: preparation and antibacterial property. Mater Sci Eng C Mater Biol Appl. 2013; 33: 4280-7.

[12] Liu J, Li F, Liu C, Wang H, Ren B, Yang K, et al. Effect of cu content on the antibacterial activity of titanium-copper sintered alloys. Mater Sci Eng C Mater Biol Appl. 2014; 35: 392-400.

[13] Ren L, Wong HM, Yan CH, Yeung KWK, Yang K. Osteogenic ability of Cu-bearing stainless steel. J Biomed Mater Res B Appl Biomater. 2015; 103: 1433-44.

[14] Li M, Nan L, Xu D, Ren G, Yang K. Antibacterial performance of a cu-bearing stainless steel against microorganisms in tap water. J Mater Sci Technol. 2015; 31: 243-51.

[15] Xu R, Zhao M, Zhao Y, Liu L, Liu C, Gao C, et al. Improved biodegradation resistance by grain refinement of novel antibacterial ZK30-cu alloys produced via selective laser melting. Mater Lett. 2019; 237: 253-7.

[16] Hu X, Neoh KG, Zhang J, Kang ET. Bacterial and osteoblast behavior on titanium, cobalt-chromiumalloy and stainless steel treatedwith alkali and heat: a comparative study for potential orthopedic applications. J Colloid Interface Sci. 2014; 417: 410-9.

[17] Pullisaar H, Reseland JE, Haugen HJ, Brinchmann JE, Østrup E. Simvastatin coating of TiO2 scaffold induces osteogenic differentiation of human adipose tissue-derived mesenchymal stem cells. Biochem Bioph Res Commun. 2014; 447: 139-4.

[18] Zhang E, Liu C. A new antibacterial Co-Cr-Mo-Cu alloy: preparation, biocorrosion, mechanical and antibacterial property. Mater Sci Eng C Mater Biol Appl. 2016; 69: 134-43.

[19] International Organization for Standardization.Implants for surgery-metallic materials-Part 4. Cobalt-chromium-molybdenum casting alloy ISO 5832-4:1996(E). 1996; Available at: https://www.iso.org/standard/23050.html.

[20] Tajima K, Yamakawa M, Katagiri T, Sasaki H. Immunohistochemical detection of bone morphogenetic protein-2 and transforming growth factor beta-1 in tracheopathia osteochondroplastica. Virchows Arch. 1997; 431: 359-63.

[21] Zou Y, Dong Y, Meng Q, Zhao Y, Li N. Incorporation of a skeletal muscle-specific enhancer in the regulatory region of Igf1 upregulates IGF1 expression and induces skeletal muscle hypertrophy. Sci Rep. 2018; 8: 2781. https://doi.org/10.1038/s41598-018-21122-5.

[22] Exposto CR, Oz U, Westgate PM, Huja SS. Influence of miniscrew diameter and loading conditions on static and dynamic assessments of bone-implant contact: an animal study. Orthod Craniofac Res. 2019; 22: 96-100.

[23] Rutten S, Nolte PA, Korstjens CM, van Duin MA, Klein-Nulend J. Low-intensity pulsed ultrasound increases bone volume, osteoid thickness and mineral apposition rate in the area of fracture healing in patients with a delayed union of the osteotomized fibula. Bone. 2008; 43: 348-54.

[24] Bilouk S, Broussous L, Nogueira RP, Ivanova V, Pernel C. Electrochemical behavior of copper and cobalt in post-etch cleaning solutions. Microelectron Eng. 2009; 86: 2038-44.

[25] Ren Z, Eppell S, Collins S, Ernst F. Co-Cr-Mo alloys: improved wear resistance through low-temperature gas-phase nitro-carburization. Surf Coat Technol. 2019; 378: 124943. https://doi.org/10.1016/j.surfcoat.2019.124943.

[26] Béreš M, Silva CC, Sarvezuk PWC, Wu L, Antunes LHM, Jardini AL, et al. Mechanical and phase transformation behaviour of biomedical Co-Cr-Mo alloy fabricated by direct metal laser sintering. Mater Sci Eng A Struct Mater. 2018; 714: 36-42.

[27] Smith RAA, Murali S, Rai B, Lu X, Lim ZXH, Lee JJL, et al. Minimum structural requirements for BMP-2-binding of heparin oligosaccharides. Biomaterials. 2018; 184: 41-55.

[28] Cheng ZA, Alba-Perez A, Gonzalez-Garcia C, Donnelly H, Llopis-Hernandez V, Jayawarna V, et al. High efficiency BMP-2 coatings: nanoscale coatings for ultralow dose BMP-2-driven regeneration of critical-sized bone defects. Adv Sci. 2019; 6: 1970009. https://doi.org/10.1002/advs.201970009.

[29] Inai K, Norris RA, Hoffman S, Markwald RR, Sugi Y. BMP-2 induces cell migration and periostin expression during atrioventricular valvulogenesis. Dev Biol. 2008; 315: 383-96.

[30] Rabiee A, Krüger M, Ardenkjær-Larsen J, Kahn CR, Emanuelli B. Distinct signalling properties of insulin receptor substrate (IRS)-1 and IRS-2 in mediating insulin/IGF-1 action. Cell Signal. 2018; 47: 1-15.

[31] Moore DR, McKay BR, Tarnopolsky MA, Parise G. Blunted satellite cell response is associated with dysregulated IGF-1 expression after exercise with age. Eur J Appl Physiol. 2018; 118: 2225-31.

[32] Bätz J, Messer-Hannemann P, Lampe F, Klein A, Püschel K, Morlock MM, et al. Effect of cavity preparation and bone mineral density on bone-interface densification and bone-implant contact during press-fit implantation of hip stems. J Orthop Res. 2019; 37: 1580-9.

[33] Bernhardt R, Kuhlisch E, Schulz MC, Eckelt U, Stadlinger B. Comparison of bone-implant contact and bone-implant volume between 2D-histological sections and 3D-SRμCT slices. Eur Cell Mater. 2012; 23: 237-47.

[34] Oest ME, Franken V, Kuchera T, Strauss J, Damron TA. Long-term loss of osteoclasts and unopposed cortical mineral apposition following limited field irradiation. J Orthop Res. 2015; 33: 334-42.

[35] Isaacson BM, Potter BK, Bloebaum RD, Epperson RT, Kawaguchi B, Swanson TM, et al. Determining the mineral apposition rate of heterotopie ossification in military healthcare system patients after total joint replacement: a case series. Bone Tissue Regen Insights 2016; 7:BTRI.S38041. https://doi.org/10.4137/BTRI.S38041.

[36] Kawai M, Kataoka Y, Sonobe J, Yamamoto H, Maruyama H, Yamamoto T, et al. Analysis of mineral apposition rates during alveolar bone regeneration over three weeks following transfer of BMP-2/7 gene via in vivo electroporation. Eur J Histochem. 2018; 62: 2947. https://doi:10.4081/ejh.2018.2947.

[37] Ram S.Allotropic phase transformations in HCP, FCC and BCC metastable structures in co-nanoparticles. Mater Sci Eng A Struct Mater. 2001; 304: 923-7.

[38] Childress JR, Chien CL. Reentrant magnetic behavior in fcc Co-Cu alloys. Phys Rev B. 1991; 43: 8089. https://doi.org/10.1103/PhysRevB.43.8089.

[39] Yamanaka K, Mori M, Chiba A. Effects of nitrogen addition on microstructure and mechanical behavior of biomedical Co-Cr-Mo alloys. J Mech Behav Biomed Mater. 2014; 29: 417-26.

[40] Li Y, Yamashita Y, Tang N, Liu B, Kurosu S, Matsumoto H, et al. Influence of carbon and nitrogen addition on microstructure and hot deformation behavior of biomedical Co-Cr-Mo alloy. Mater Chem Phys. 2012; 135: 849-54.

[41] Yamanaka K, Mori M, Chiba A. Effects of carbon concentration on microstructure and mechanical properties of as-cast nickel-free co-28Cr-9W-based dental alloys. Mater Sci Eng C Mater Biol Appl. 2014; 40: 127-34.

[42] Bettini E, Eriksson T, Boström M, Leygraf C, Pan J. Influence of metal carbides on dissolution behavior of biomedical CoCrMo alloy: SEM, TEM and AFM studies. Electrochim Acta. 2011; 56: 9413-9.

[43] Matković T, Matković P, Malina J. Effects of Ni and Mo on the microstructure and some other properties of Co-Cr dental alloys. J Alloys Compd. 2004; 366: 293-7.

[44] Issa Y, Brunton P, Waters CM, Watts DC. Cytotoxicity of metal ions to human oligodendroglial cells and human gingival fibroblasts assessed bymitochondrial dehydrogenase activity. Dent Mater. 2008; 24: 281-7.