Development of AZ91/SiC surface composite by FSP: effect of vibration and process parameters on microstructure and mechanical characteristics

Abstract

A surface composite layer enhances the mechanical characteristics of a surface while retaining the properties of the base material. Friction stir processing (FSP) is a method for forming surface metal matrix composites (SMMCs) that reinforce a surface with particles. In the current study, a new method entitled friction stir vibration processing (FSVP) was applied to form SMMCs on the surface of AZ91 magnesium alloy with SiC particles as the reinforcing particles. Contrary to FSP, in FSVP, the workpiece was vibrated normal to the processing line while the tool rotated and traversed. The microstructure and mechanical properties of friction stir (FS) and friction stir vibration (FSV) processed specimens were evaluated. Additionally, the effects of vibration frequency and process parameters on different characteristics of FS and FSV processed specimens were studied. The results showed that the stir zone grains for FSV processed specimens were finer than those for FS processed specimens, and the second phase particles (SiC particles) had a more homogenous distribution in the former specimens than in the latter specimens. This was related to the effect of workpiece vibration during FSVP, which increased the material deformation and led to enhanced dynamic recrystallization and the breakdown of agglomerated SiC particles. The results indicated that the stir zone grain size decreased, and the distribution homogeneity of the SiC particles increased as vibration frequency increased. It was also observed that the stir zone grain size increased, and the mechanical properties of the processed specimens decreased as tool rotation speed increased.

Keywords

Friction stir processing (FSP) / Vibration / AZ91 magnesium alloy / Dynamic recrystallization / Microstructure / Mechanical properties

References

[1] Abbasi M, Abdollahzadeh A, Omidvar H, et al. Incorporation of SiC particles in FS welded zone of AZ31 Mg alloy to improve the mechanical properties and corrosion resistance. J Mater Res, 2016, 107: 566-572.

[2] Abdollahzadeh A, Shokuhfar A, Omidvar H, et al. Structural evaluation and mechanical properties of AZ31/SiC nano-composite produced by friction stir welding process at various welding speeds. Proc Inst Mech Eng Part L J Mater Des Appl, 2019, 233: 831-841.

[3] Abdollahzadeh A, Shokuhfar A, Cabrera JM, et al. In-situ nanocomposite in friction stir welding of 6061-T6 aluminum alloy to AZ31 magnesium alloy. J Mater Proc Technol, 2019, 263: 296-307.

[4] Abdollahzadeh A, Shokuhfar A, Cabrera JM, et al. The effect of changing chemical composition on dissimilar Mg/Al friction stir welded butt joints using zinc interlayer. J Manuf Proc, 2018, 34: 18-30.

[5] Segal VM. Engineering and commercialization of equal channel angular extrusion. Mater Sci Eng A, 2004, 386: 269-276.

[6] Edalati K, Horita Z. A review on high-pressure torsion (HPT) from 1935 to 1988. Mater Sci Eng A, 2016, 652: 325-352.

[7] Nunes LGS, Machado MLP. Simulation of the accumulative roll-bonding process through warm torsion test. J Mater Res Technol, 2018, 7: 326-330.

[8] Barati M, Abbasi M, Abedini M. The effects of friction stir processing and friction stir vibration processing on mechanical, wear and corrosion characteristics of Al6061/SiO₂ surface. J Manuf Process, 2019, 45: 491-497.

[9] Dadaei M, Omidvar H, Bagheri B, et al. The effect of SiC/Al₂O₃ particles used during FSP on mechanical properties of AZ91 magnesium alloy. J Mater Res, 2014, 105: 369-374.

[10] Zheng FY, Wu YJ, Peng LM, et al. Microstructure and mechanical properties of friction stir processed Mg-2.0Nd-0.3Zn-1.0Zr magnesium alloy. J Magnes Alloys, 2013, 1: 122-127.

[11] Chai F, Zhang D, Li Y. Effect of thermal history on microstructures and mechanical properties of AZ31 magnesium alloy prepared by friction stir processing. Materials, 2014, 7: 1573-1589.

[12] Iwaszko J, Kudla K, Fila K. Friction stir processing of the AZ91 magnesium alloy with SiC particles. Arch Mater Sci Eng, 2016, 77: 85-92.

[13] Asadi P, Faraji G, Besharati MK. Producing of AZ91/SiC composite by friction stir processing. J Adv Manuf Technol, 2010, 51: 247-260.

[14] Abbasi M, Bagheri B, Dadaei M, et al. The effect of FSP on mechanical, tribological and corrosion behavior of composite layer developed on magnesium AZ91 alloy surface. Int J Adv Manuf Technol, 2015, 77: 2051-2058.

[15] ASTM-E3-11 Standard guide for preparation of metallographic specimens. Annual Book of ASTM Standards, 2017, West Conshohocken: American Society for Testing and Materials

[16] ASTM-E8M Standard test methods for tension testing of metallic material. Annual Book of ASTM Standards, 2016, West Conshohocken: American Society for Testing and Materials

[17] ASTM-E112-13 Standard test methods for determining average grain size. Annual Book of ASTM Standards, 2017, West Conshohocken: American Society for Testing and Materials

[18] ASTM-E384-11 Standard test method for Knoop and Vickers hardness of materials. Annual Book of ASTM Standards, 2011, West Conshohocken: American Society for Testing and Materials

[19] Abbasi M, Givi M, Ramazani A. Friction stir vibration processing: a new method to improve the microstructure and mechanical properties of Al5052/SiC surface nano-composite layer. Int J Adv Manuf Technol, 2019, 100: 1463-1473.

[20] Kaibyshev R, Shipilova K, Musin F, et al. Continous dynamic recrystallization in an Al-Li-Mg-Sc alloy during equal-channel angular extrusion. Mater Sci Eng A, 2005, 396: 341-351.

[21] Darvishi Kamachali R, Steinbach I. 3D phase-field simulation of grain growth: topological analysis versus mean-field approximates. Acta Mater, 2012, 60: 2719-2728.

[22] Fouladi S, Abbasi M. The effect of friction stir vibration welding process on characteristics of SiO₂ incorporated joint. J Mater Process Technol, 2017, 243: 23-30.

[23] Hull D, Bacon DJ. Introduction to dislocations, 2011, Britain: Butterworth-Heinemann

[24] Naderi M, Abbasi M, Saeed-Akbari A. Enhanced mechanical properties of a hot-stamped advanced high-strength steel via tempering treatment. Metall Mater Trans A, 2013, 44: 1852-1861.

[25] Callister WD. Materials science and engineering: an introduction, 2003, Hoboken: Wiley

[26] Estrin YZ, Zabrodin PA, Braude IS, et al. Low temperature plastic deformation of AZ31 magnesium alloy with different microstructures. Low Temper Phys, 2010, 36: 1100-1112.

[27] Barooni O, Abbasi M, Givi M, et al. New method to improve the microstructure and mechanical properties of joint obtained using FSW. Int J Adv Manuf Technol, 2017, 93: 4371-4378.

[28] Uthaisangsuk V (2009) Microstructure based formability modeling of multiphase steels. Dissertation, IEHK, RWTH- Aachen

[29] Dieter GE, Bacon D. Mechanical and metallurgy, 1988, London: McGraw-Hill

[30] Hertzberg RW. Deformation and Fracture mechanics of engineering materials, 1996, 4 Hoboken: Wiley

[31] Bagheri B, Mahdian Rizi AA, Abbasi M, et al. Friction stir spot vibration welding: improving the microstructure and mechanical properties of Al5083 joint. Metallogr Microstruct Anal, 2019, 8: 713-725.

[32] Li YS, Zhang Y, Tao NR, et al. Effect of the Zener-Hollomon parameter on the microstructures and mechanical properties of Cu subjected to plastic deformation. Acta Mater, 2009, 57: 761-772.

[33] Chang CI, Lee CJ, Huang JC. Relationship between grain size and Zener-Holloman parameter during friction stir processing in AZ31 Mg alloys. Scr Mater, 2004, 51: 509-514.

[34] Starink MJ, Deschamps A, Wang SC. The strength of friction stir welded and friction stir processed aluminium alloys. Scr Mater, 2008, 58: 377-382.

[35] Callister WD. Materials science and engineering: an introduction, 2003, Hoboken: Wiley 153-164.