High speed steel produced by spray forming

Abstract

In this paper, ASP2030 (A30) high speed steel (HSS) was produced by spray forming and the microstructure was studied by optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron probe microanalysis (EPMA) and X-ray diffraction (XRD). The spray formed A30 (SF A30) steel exhibited a very uniform and fine microstructure consisting of martensite, retained austenite and uniformly distributed network carbides. Microstructure refining can be explained in terms of the rapid solidification of spray forming. M₂C, MC and M₆C type carbides were found in the as-sprayed A30 HSS by XRD and TEM. A uniform distribution of carbides was obtained after forging and annealing. The microstructure properties of SF A30 steel indicate that spray forming can be considered as a cost-effective route for the production of A30 steels and other highly alloyed steels.

Keywords

Spray forming / High speed steel (HSS) / Microstructure / Carbides / Property

References

[1] Moon HK, Lee KB, Kwon H. Influences of Co addition and austenitizing temperature on secondary hardening and impact fracture behavior in P/M high speed steels of W-Mo-Cr-V(-Co) system. Mater Sci Eng A, 2008, 474: 328-334.

[2] Mesquita RA, Barbosa CA. Spray forming high speed steel—properties and processing. Mater Sci Eng A, 2004, 383: 87-95.

[3] Zhou B, Shen Y, Chen J, Cui ZS. Breakdown behavior of eutectic carbides in high speed steel during hot compression. J Iron Steel Res Int, 2011, 18: 41-48.

[4] Hetzner DW. Refining carbide size distributions in M1 high speed steel by processing and alloying. Mater Charact, 2001, 46: 175-182.

[5] Wronski AS, Wright CS, Bolton JD, Bienvenu Y, Jeandin M, Smith AB. PM HSS for aerospace automotive and cutting tool applications. Met Powder Rep, 1991, 46(50–51): 53-55.

[6] Grant PS. Spray forming. Prog Mater Sci, 1995, 39: 497-545.

[7] Rodenburg C, Krzyzanowski M, Beynon JH, Rainforth WM. Hot workability of spray-formed AISI M3:2 high-speed steel. Mater Sci Eng A, 2004, 386: 420-427.

[8] Schulz A, Uhlenwinkel V, Escher C, Kohlmann R, Kulmburg A, Montero MC, Rabitsch R, Schützenhöfer W, Stocchi D, Viale D. Opportunities and challenges of spray forming high-alloyed steels. Mater Sci Eng A, 2008, 477: 69-79.

[9] Bhargava AK, Tiwari AN. Effect of rapid solidification and heat treatment on D2 steel. Int J Rapid Solidif, 1992, 7: 51-66.

[10] Zhang JG. Research in spray forming technology and its applications in metallurgy. J Mater Process Technol, 2003, 138: 357-360.

[11] Zhang JG, Xu HB, Shi HS, Wu JS, Sun DS. Microstructure and properties of spray formed Cr₁₂MoV steel for rolls. J Mater Process Technol, 2003, 111: 79-84.

[12] Ikawa Y, Itami T, Kumagai K, Kawashima Y, Leatham AG, Coombs JS. Spray deposition method and its application to the production of mill rolls. ISIJ Int, 1990, 30: 756-763.

[13] Lee ES, Park WJ, Baik KH, Ahn S. Different carbide types and their effect on bend properties of a spray-formed high speed steel. Scr Mater, 1998, 39: 1133-1138.

[14] Zhang Y, Zhang GQ, Li Z, Li ZD, Yuan H, Xu WY, Liu N, Tian SF. Analysis of twin-nozzle-scanning spray forming process and spray formed high speed steel (HSS). J Iron Steel Res Int, 2007, 14: 7-10.

[15] Yan F, Xu Z, Shi HS, Fan JF. Microstructure of the spray formed Vanadis 4 steel and its ultrafine structure. Mater Charact, 2008, 59: 592-597.

[16] Cui CS, Fritsching U, Schulz A, Tinscher R, Bauckhage K, Mayr P. Spray forming of homogeneous 100Cr6 bearing steel billets. J Mater Process Technol, 2005, 168: 496-504.

[17] Yu FX, Cui JZ, Ranganathan S, Dwarakadasa ES. Fundamental differences between spray forming and other semisolid processes. Mater Sci Eng A, 2001, 304–306: 621-626.

[18] Wei SZ, Zhu JH, Xu LJ. Research on wear resistance of high speed steel with high vanadium content. Mater Sci Eng A, 2005, 404: 138-145.

[19] Zhou H, Wang JG, Jia SS, Keisaku OGI. Solidified microstructures and phases of high speed steels containing different V and C content. Acta Metall Sin, 1997, 33: 838-843.

[20] Luan YK, Song NN, Bai YL, Kang XH, Li DZ. Effect of solidification rate on the morphology and distribution of eutectic carbides in centrifugal casting high-speed steel rolls. J Mater Process Technol, 2010, 210: 536-541.

[21] Lee ES, Park WJ, Jung JY. Solidification microstructure and M₂C carbide decomposition in a spray-formed high-speed steel. Metall Mater Trans, 1998, 29A: 1395-1404.

[22] Xu Q, Lavernia EJ. Microstructure evolution during the initial stages of spray atomization and deposition. Scr Mater, 1999, 41: 535-540.

[23] Pan FS, Wang WQ, Tang AT. Phase transformation refinement of coarse primary carbides in M2 high speed steel. Prog Nat Sci, 2011, 21: 180-186.

[24] Večko Pirtovšek T, Kugler G, Godec M, Terčelj M. Microstructural characterization during the hot deformation of 1.17C-11.3Cr-1.48V-2.24W-1.35Mo ledeburitic tool steel. Mater Charact, 2011, 62: 189-197.

[25] Meurling F, Melander A, Tidesten M, Westin L. Influence of carbide and inclusion contents on the fatigue properties of high speed steels and tool steels. Int J Fatigue, 2001, 23: 215-224.