The research of thermal capacity of submicrocrystalline powder materials on the basis of nickel aluminide

Abstract

The paper examines the influence of compacting pressure on the thermal capacity of macrocrystalline and submicrocrystalline powder composition on the basis of nickel aluminide in the wide range of temperatures. It was found that the compacting pressure in the large-dispersed powder mixtures Ni50 Al50 actuates inttermetallides Ni2Al3, NiAl3 according liquid-phase mechanisms at Т ~ 0,85 Tпл, and in fine-dispersed powder mixtures it intensifies the generation of intermetallides according to the solid-phase reaction mechanisms at Т ~ 0,77 Tпл. The obtained results may be used for the analysis of physical and mechanical features of nano-materials, obtained from by gas condensation in the inert atmosphere.

Keywords

physical and mechanical features of nano-materials / thermal capacity of submicrocrystalline powder composition

References

[1] Гекузин Я.Е. Диффузионная зона. М. Наука, 1979, 344 с.

[2] Богданов В.В., Кибец В.И., Парицкая Л.Н., Пузанов А.А., Сорокина Е.П., Чеканов М.И. Влияние малых гидростатических давлений на диффузионное фазообразования в дисперсных многослойных системах. ФММ, 1993, N11/12, С. 27-6.

[3] Поварова К.Б., Проскурин В.Б., Левин В.П., Николаев А.Г., Казанская Ю.K., Фиров А.И. Влияние механического легирования на характер формирования интерметаллидной фазы в системе Ni-A1 при реакционном спекании. Металлы, N4, 1994 г. с.67-75.

RIGHTS & PERMISSIONS

Levin V.P.