The concept of averaging of stresses in the problems of the two-parameter fracture mechanics
Y. G. Matvienko
Izvestiya MGTU MAMI ›› 2015, Vol. 9 ›› Issue (2-4) : 85 -90.
The concept of averaging of stresses in the problems of the two-parameter fracture mechanics
The article illustrates the application of the Neuber-Novozhilov concept for averaging of stress to before tip of a crack/cutout in solving of contemporary problems of two-parameter fracture mechanics, aimed at creation of models and criteria of body limit state and search of a crack path. As a parameters of tightness strain in the vicinity of the crack tip are used nonsingular components of T-stresses of the stress field.
two-parameter fracture mechanics / crack path / cut / nonsingular T-stress
| [1] |
Матвиенко Ю.Г. Тенденции нелинейной механики разрушения в проблемах машиностроения. - М.-Ижевск: Институт компьютерных исследований, 2015, 56 с. |
| [2] |
Матвиенко Ю.Г. Модели и критерии механики разрушения. - М.: ФИЗМАТЛИТ, 2006, 328 с. |
| [3] |
Матвиенко Ю.Г. Моделирование и критерии разрушения в современных проблемах прочности, живучести и безопасности машин. Проблемы машиностроения и надежности машин. 2014. №3. C. 80-89. |
| [4] |
Матвиенко Ю.Г., Починков Р.А. Влияние несингулярных компонентов Т-напряжений на зоны пластической деформации у вершины трещины нормального отрыва. Деформация и разрушение материалов. 2012. № 3. С. 6-14. |
| [5] |
Матвиенко Ю.Г. Диаграммы трещиностойкости в связи со стеснением деформаций у вершины трещины и выреза. Заводская лаборатория. Диагностика материалов. 2008. № 10. С. 55-60. |
| [6] |
Meliani H.M., Matvienko Yu.G., Pluvinage G. Two-parameter fracture criterion (Kρ,c-Tef,c) based on notch fracture mechanics. International Journal of Fracture. 2011. Vol. 167. P. 173- 182. |
| [7] |
Matvienko, Yu.G., Shlyannikov, V.N., Boychenko, N.V. In-plane and out-of-plane constraint parameters along a three-dimensional crack-front stress field under creep loading. Fatigue and Fracture of Engineering Materials and Structures. 2013. Vol. 36. P. 14-24. |
| [8] |
Матвиенко Ю.Г. Двухпараметрическая механика разрушения в современных проблемах прочности. Проблемы машиностроения и надежности машин. 2013. №5. С. 37-46. |
| [9] |
Meliani H.M., Azari Z., Pluvinage G., Matvienko Yu.G. The effective T-stress estimation and crack paths emanating from U-notches. Engineering Fracture Mechanics. 2010. Vol. 77. P. 1682-1692. |
| [10] |
Матвиенко Ю.Г. Два подхода к учету несингулярных Т-напряжений в критериях механики разрушения тел с вырезами. Проблемы машиностроения и надежности машин. 2011. № 5. С. 104-110. |
| [11] |
Матвиенко Ю.Г. Несингулярные Т-напряжения в проблемах двухпараметрической механики разрушения. Заводская лаборатория. Диагностика материалов. 2012. № 2. C. 51-58. |
| [12] |
Матвиенко Ю.Г., Бубнов М.А., Нестеренко Г.И. Осреднение напряжений в поиске траектории трещины. Вестник научно-технического развития. 2011. № 12 (52). С. 19-24. |
| [13] |
Matvienko Yu.G. Maximum average tangential stress criterion for prediction of the crack path. International Journal of Fracture. 2012. Vol. 176. P. 113-118. |
| [14] |
Семенова М. М., Матвиенко Ю. Г. Прогнозирование траектории поверхностной трещины при контактном нагружении в условиях трения скольжения. Машиностроение и инженерное образование. 2014. № 2. С. 47-52. |
Matvienko Y.G.
/
| 〈 |
|
〉 |