Influence of a colloidal silver dioxide solution on the edge adjustment of the mineral aggregate trioxide cement for closure of perforation communications in vitro

Abstract

BACKGROUND: According to Russian and foreign literature, the probability of iatrogenic perforation of the wall of the tooth root canal is high (9.7–12.5%) during endodontic dental treatment. This is a poor prognostic sign and may subsequently result in tooth extraction. Moreover, cases without curing of mineral trioxide aggregate (MTA) cement with pronounced exudation were reported. Сurrently, the modification of domestically produced MTA cement is relevant for closing teeth root canal perforation.

AIM: This study aimed to conduct a comparative experimental microscopic study of the preservation of the marginal fit to the tooth tissues in perforation areas filled with MTA cement mixed conventionally with distilled water and a colloidal silver dioxide solution.

MATERIALS AND METHODS: Sixty teeth previously removed for medical reasons were endodontically treated after iatrogenic perforation formation in the furcation area of the roots. Two groups were formed. In the first group, MTA cement mixed with distilled water was used to close dental perforations. In the second group, MTA cement mixed with a colloidal silver dioxide solution was utilized. The groups were divided into subgroups depending on the MTA cement brand used. The teeth were placed in an automatic incubator HHD 7 LED, in which an optimal mode was created, simulating the conditions of the oral cavity (t = 37 °C, humidity 99%). The samples were placed in artificial saliva. After two months of exposing the teeth to a humid environment, the preservation and damage to the marginal fit in the perforation area of the fillings were determined under a Levenhuk 720B binocular microscope.

RESULTS: In the perforations of the 30 teeth sealed with various MTA cement types mixed with distilled water, damage of the marginal fit was found in seven (23.3 ± 7.9%) cases. Similar damage in 30 teeth with colloidal silver dioxide solution used to prepare MTA cements was detected in two (6.7 ± 4.6%) cases (p >0.050, t = 1.82).

CONCLUSION: The use of MTA cement mixed in a colloidal silver dioxide solution, in comparison with distilled water, contributes to a greater preservation of the marginal fit of the material to the walls of the root canal in an in vitro experiment.

Keywords

colloidal silver dioxide solution / adhesion to the walls of the root canal / closure of endodontic perforations / preservation of the edge fit of the material to the tooth tissues

References

[1] Farea M, Husein A, Pameijer CH. Furcation perforation. Current approaches and future perspectives. Endododontic Practice. 2018;11:25–31.

[2] Farea M., Husein A., Pameijer C.H. Furcation perforation. Current approaches and future perspectives // Endodontic Practice. 2018. N. 11. P. 25–31.

[3] Narbekova KA, Sinichkin VS, Shirshikova AA, et al. Methods of closing perforations. Mezhdunarodnyj studencheskij nauchnyj vestnik. 2018;1:17. (In Russ).

[4] Нарбекова К.А., Синичкин В.С., Ширшикова А.А., и др. Методы закрытия перфораций // Международный студенческий научный вестник. 2018. № 1. С. 17.

[5] Shorina TV. Neanalogi. Dentaltimes. 2017;36:54–56. (In Russ).

[6] Шорина Т.В. Неаналоги // Dentaltimes. 2017. № 36. С. 54–56.

[7] Slabun T. Klinicheskij sluchaj lechenija zubov s poperechnym perelomom kornja u pacienta pozhilogo vozrasta. DentArt. 2005;3:15–23. (In Russ).

[8] Слабун Т. Клинический случай лечения зубов с поперечным переломом корня у пациента пожилого возраста // ДентАрт. 2005. № 3. С. 15–23.

[9] Klimpel’ FM. Ispol’zovanie MTA dlja retrogradnogo plombirovanija v jendodontii. Kafedra. Stomatologicheskoe obrazovanie. 2015;43:62–65. (In Russ).

[10] Климпель Ф.М. Использование MTA для ретроградного пломбирования в эндодонтии // Кафедра. Стоматологическое образование. 2015. № 43. С. 62–65.

RIGHTS & PERMISSIONS

Eco-Vector