Effect of annealing temperature on microstructure and mechanical properties of Mg-Zn-Zr-Nd alloy with large final rolling deformation

Abstract

In this study, the Mg-3Zn-0.5Zr-χNd (χ=0, 0.6) alloys were subjected to final rolling treatment with large deformation of 50%. The impact of annealing temperatures on the microstructure and mechanical properties was investigated. The rolled Mg-3Zn-0.5Zr-0.6Nd alloy exhibited an ultimate tensile strength of 386 MPa, a yield strength of 361 MPa, and an elongation of 7.1%. Annealing at different temperatures resulted in reduced strength and obviously increased elongation for both alloys. Optimal mechanical properties for the Mg-3Zn-0.5Zr-0.6Nd alloy were achieved after annealing at 200 °C, with an ultimate tensile strength of 287 MPa, a yield strength of 235 MPa, and an elongation of 26.1%. The numerous deformed microstructures, twins, and precipitated phases in the rolled alloy could impede the deformation at room temperature and increase the work hardening rate. After annealing, a decrease in the work hardening effect and an increase in the dynamic recovery effect were obtained due to the formation of fine equiaxed grains, and the increased volume fraction of precipitated phases, which significantly improved the elongation of the alloy. Additionally, the addition of Nd element could enhance the annealing recrystallization rate, reduce the Schmid factor difference between basal and prismatic slip systems, facilitate multi-system slip initiation and improve the alloy plasticity.

Keywords

Mg-Zn-Zr-Nd alloy / large final rolling deformation / annealing temperatures / microstructures / mechanical properties

References

[[1]] Liu H-x, Li C-x, Xie J-l, et al.. Effect of Sm content on microstructure and properties of extruded Mg-6Al-2Sr alloy [J]. Journal of Central South University, 2024, 31(1): 59-71,

[[2]] Chen Y H, Gao X Y, Nie K B, et al.. Different effects of SiC dimensions on the microstructure and mechanical properties of magnesium matrix composites [J]. Materials Science and Engineering A, 2022, 847: 143273,

[[3]] Dai R-j, Deng K-k, Wang C-j, et al.. Effects of precipitates and solute atoms on the work hardening and softening behavior of Zn-rich aluminum alloy [J]. Materials Science and Engineering A, 2022, 848: 143388,

[[4]] Liu Y, Deng K-k, Zhang X-c, et al.. Investigations of PMMCs laminates with regulatable thickness ratio: Microstructure, mechanical behavior and fractural mechanism [J]. Materials Science and Engineering A, 2022, 856: 143997,

[[5]] Wen K, Li X-w, Xiong B-q, et al.. Influence of minor Sc additions on grain refinement and microstructure characteristics of a high Zn-containing Al-Zn-Mg-Cu-Zr alloy [J]. Journal of Central South University, 2022, 29(3): 780-794,

[[6]] Yang A, Nie K B, Deng K K, et al.. Microstructures and tensile properties of Mg-2Zn-0.8Sr-0.2Ca alloy extruded at relatively slow speed and low temperature [J]. Journal of Mining and Metallurgy, Section B: Metallurgy, 2022, 58(2): 203-218,

[[7]] Zhang J H, Nie K B, Deng K K, et al.. Ultrahigh strength TiC_np/Mg-2Zn-0.8Sr-0.2Ca magnesium matrix composite processed by combining multidirectional forging with extrusion [J]. Composites Communications, 2021, 27: 100847,

[[8]] Zhang J H, Nie K B, Deng K K, et al.. Effect of Nd on the microstructure and mechanical properties of Mg-3Zn-0.5Zr alloy [J]. Materials Science and Engineering A, 2022, 838: 142562,

[[9]] Zhang J-k, Wang C-j, Fan Y-d, et al.. Effect of tip content on the work hardening and softening behavior of Mg-Zn-Ca alloy [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(3): 551-560,

[[10]] Zhang L, Deng K-k, Nie K-b, et al.. Achieving strength-thermal conductivity synergy in Mg bulk system via introducing oriented graphite flakes into Mg-Zn-Ca alloy [J]. Composites Communications, 2023, 37: 101451,

[[11]] Zhang L, Deng K-k, Nie K-b, et al.. Thermal conductivity and mechanical properties of graphite/Mg composite with a super-nano CaCO₃ interfacial layer [J]. iScience, 2023, 26(4): 106505,

[[12]] Bazhenov V E, Saidov S S, Tselovalnik Y V, et al.. Comparison of castability, mechanical, and corrosion properties of Mg-Zn-Y-Zr alloys containing LPSO and W phases [J]. Transactions of Nonferrous Metals Society of China, 2021, 31(5): 1276-1290,

[[13]] Zhang Z, Zhang J-h, Xie J-s, et al.. Developing a low-alloyed fine-grained Mg alloy with high strength-ductility based on dislocation evolution and grain boundary segregation [J]. Scripta Materialia, 2022, 209: 114414,

[[14]] Yin S-q, Duan W-c, Liu W-h, et al.. Influence of specific second phases on corrosion behaviors of Mg-Zn-Gd-Zr alloys [J]. Corrosion Science, 2020, 166: 108419,

[[15]] Sun C, Liu H, Xu Z-y, et al.. Refining 18R-LPSO phase into sub-micron range by pre-kinking design and its prominent strengthening effect on Mg₉₇Y₂Zn₁ alloy [J]. Journal of Materials Science & Technology, 2024, 176: 13-24,

[[16]] Robson J D, Paa-Rai C. The interaction of grain refinement and ageing in magnesium-zinc-zirconium (ZK) alloys [J]. Acta Materialia, 2015, 95: 10-19,

[[17]] Lin X-m, Wu X-d, Cao L-f, et al.. Effect of hot deformation on the microstructure of spray-formed 7055 aluminum alloy extruded plate [J]. Journal of Central South University, 2023, 30(12): 3950-3963,

[[18]] Chen H, Tang J-w, Gong W-w, et al.. Effects of annealing treatment on the microstructure and corrosion behavior of hot rolled AZ31 Mg alloy [J]. Journal of Materials Research and Technology, 2021, 15: 4800-4812,

[[19]] Gong H, He Y-b, Zhang T, et al.. Modified constitutive behavior model of Mg-10Gd-3Y-0.4Zr alloy during high-temperature deformation process [J]. Journal of Central South University, 2023, 30(8): 2458-2471,

[[20]] Kong T, Kwak B J, Kim J, et al.. Tailoring strength-ductility balance of caliber-rolled AZ31 Mg alloy through subsequent annealing [J]. Journal of Magnesium and Alloys, 2020, 8(1): 163-171,

[[21]] Lv S-h, Ma R, Qiu X, et al.. Complex internal faults of MgZn₂ in Mg Zn binary alloy [J]. Materials Characterization, 2020, 169: 110659,

[[22]] Luo J, Yan H, Chen R-s, et al.. Effects of Gd concentration on microstructure, texture and tensile properties of Mg-Zn-Gd alloys subjected to large strain hot rolling [J]. Materials Science and Engineering A, 2014, 614: 88-95,

[[23]] Tang J-w, Chen L, Bao Y-h, et al.. Investigation on corrosion behaviors of Mg-Zn-Al-Sn-Mn alloy treated by solution and artificial aging [J]. Journal of Central South University, 2023, 30(10): 3197-3210,

[[24]] Tian A-q, Xu X-h, Sun L, et al.. Effects of interrupted ageing and asymmetric rolling on microstructures, mechanical properties, and intergranular corrosion behavior of Al-Mg-Si-Zn alloy [J]. Journal of Central South University, 2022, 29(3): 821-835,

[[25]] Srinivasan A, Ghosh C S, Srivastava V C, et al.. Microstructural and textural evolution during large strain hot rolling (LSR) of Mg-Al (AZ31) alloy [J]. Materials Science and Technology, 2007, 23(11): 1313-1320,

[[26]] Xie J-s, Zhang Z, Liu S-j, et al.. Designing new low alloyed Mg-RE alloys with high strength and ductility via high-speed extrusion [J]. International Journal of Minerals, Metallurgy and Materials, 2023, 30(1): 82-91,

[[27]] Zhao L-j, Ma L-f, Han T-z, et al.. Strength-ductility balance of Mg-1.03Ca-0.47Mn Mg alloy sheet produced by rolling and annealing [J]. Materials Letters, 2021, 287: 129288,

[[28]] Cepeda-Jiménez C M, Molina-Aldareguia J M, Pérez-Prado M T. Effect of grain size on slip activity in pure magnesium polycrystals [J]. Acta Materialia, 2015, 84: 443-456,

[[29]] Zhang Z, Zhang J-h, Xie J-s, et al.. Significantly enhanced grain boundary Zn and Ca co-segregation of dilute Mg alloy via trace Sm addition [J]. Materials Science and Engineering A, 2022, 831: 142259,

[[30]] Shi Q-x, Wang C-j, Deng K-k, et al.. Work hardening and softening behaviors of Mg-Zn-Gd-Ca alloy regulated by bimodal microstructure [J]. Journal of Alloys and Compounds, 2023, 938: 168606,

[[31]] Zareian Z, Emamy M, Malekan M, et al.. Tailoring the mechanical properties of Mg-Zn magnesium alloy by calcium addition and hot extrusion process [J]. Materials Science and Engineering A, 2020, 774: 138929,

[[32]] Zhao H, Cheng Q-s, Zhao Y, et al.. Effect of solid solution treatment on microstructure and properties of extruded 7055 aluminum alloy [J]. Journal of Central South University, 2024, 31(1): 25-42,

[[33]] Zhang J H, Nie K B, Deng K K, et al.. Ultrahigh strength TiCnp/Mg-2Zn-0.8Sr-0.2Ca magnesium matrix composite processed by combining multidirectional forging with extrusion [J]. Composites Communications, 2021, 27: 100847,

[[34]] Zhang Z, Zhang J-h, Xie J-s, et al.. Developing a Mg alloy with ultrahigh room temperature ductility via grain boundary segregation and activation of non-basal slips [J]. International Journal of Plasticity, 2023, 162: 103548,

[[35]] Yan Z-f, Wang D-h, He X-l, et al.. Deformation behaviors and cyclic strength assessment of AZ31B magnesium alloy based on steady ratcheting effect [J]. Materials Science and Engineering A, 2018, 723: 212-220,

[[36]] Fan Y-d, Deng K-k, Wang C-j, et al.. Work hardening and softening behavior of Mg-Zn-Ca alloy influenced by deformable Ti particles [J]. Materials Science and Engineering A, 2022, 833: 142336,

[[37]] Barannikova S A, Nadezhkin M V. Kinetics of plastic deformation localization bands in polycrystalline nickel [J]. Metals, 2021, 11(9): 1440,

[[38]] Han C S, Gao H-j, Huang Y-g, et al.. Mechanism-based strain gradient crystal plasticity—II. Analysis [J]. Journal of the Mechanics and Physics of Solids, 2005, 53(5): 1204-1222,

[[39]] Zhao C-y, Li Z-y, Shi J-h, et al.. Strain hardening behavior of Mg-Y alloys after extrusion process [J]. Journal of Magnesium and Alloys, 2019, 7(4): 672-680,

[[40]] Balík J, Dobroň P, Chmelík F, et al.. Modeling of the work hardening in magnesium alloy sheets [J]. International Journal of Plasticity, 2016, 76: 166-185,

[[41]] Cai Y, Wan L, Guo Z H, et al.. Hot deformation characteristics of AZ80 magnesium alloy: Work hardening effect and processing parameter sensitivities [J]. Materials Science and Engineering A, 2017, 687: 113-122,

[[42]] Guo L-l, Chen Z-c, Gao Li. Effects of grain size, texture and twinning on mechanical properties and work-hardening behavior of AZ31 magnesium alloys [J]. Materials Science and Engineering A, 2011, 528(29–30): 8537-8545,

[[43]] Han C S, Gao H-j, Huang Y-g, et al.. Mechanism-based strain gradient crystal plasticity—II. Analysis [J]. Journal of the Mechanics and Physics of Solids, 2005, 53(5): 1204-1222,

[[44]] Yan Z-f, Wang D-h, He X-l, et al.. Deformation behaviors and cyclic strength assessment of AZ31B magnesium alloy based on steady ratcheting effect [J]. Materials Science and Engineering A, 2018, 723: 212-220,

[[45]] Song B, Yang Q-s, Zhou T, et al.. Texture control by{10–12}twinning to improve the formability of Mg alloys: A review [J]. Journal of Materials Science & Technology, 2019, 35(10): 2269-2282,

[[46]] Shen M J, Zhang M F, Ying W F. Processing, microstructure and mechanical properties of bimodal size SiCpreinforced AZ31B magnesium matrix composites [J]. Journal of Magnesium and Alloys, 2015, 3(2): 162-167,

[[47]] Barnett M R, Nave M D, Ghaderi A. Yield point elongation due to twinning in a magnesium alloy [J]. Acta Materialia, 2012, 60(4): 1433-1443,

[[48]] Zhang K, Li H, Liu J-lin. Effect of yield surface distortion on the failure prediction of Mg alloy sheets [J]. Archive of Applied Mechanics, 2021, 91(1): 151-167,

[[49]] Kim Y J, Lee J U, Kim S H, et al.. Grain size effect on twinning and annealing behaviors of rolled magnesium alloy with bimodal structure [J]. Materials Science and Engineering A, 2019, 754: 38-45,