Preparing Fe-Cr-Ni alloy by utilization of limonitic nickel laterite sinter

Abstract

In this paper, sinter samples of limonitic nickel laterite were adopted for Fe-Cr-Ni alloy preparation at lower costs. Based on the thermodynamics analysis, smelting characteristics of sinter samples of S1 (4.84 wt% Cr₂O₃) and S3 (7.72 wt% Cr₂O₃) were revealed by the optimization of smelting process parameters. When smelting durations were kept at 60 min and 90 min for S1 and S3 and smelting temperature, coke dosage and slag basicity were maintained at 1600 °C, 20 wt% and 1.0, respectively, the qualified Fe-Cr-Ni alloys containing 84%–88 wt% Fe, 5.6%–9.3 wt% Cr and 1.55%–1.70 wt% Ni were prepared with the recovery rates of Fe, Cr and Ni of over 96%, 90% and 98%, respectively. Higher Cr₂O₃ content of sinter leads to the prolongation of smelting duration, which is adverse to the reduction of coke ratio and the increase of stainless steel output. The comprehensive furnace burdens including Ni-bearing sinter and Cr-bearing pellets will be developed in the follow-up study for the more efficient preparation of high-Cr ferronickel.

Keywords

smelting characteristics / limonitic nickel laterite sinter / Fe-Cr-Ni alloy / slag-iron separation

References

[[1]] Jessy Michla J R, Nagarajan R, Krishnasamy S, et al.. Conventional and additively manufactured stainless steels: A review. Transactions of the Indian Institute of Metals, 2021, 74(6): 1261-1278, J]

[[2]] Su C, Geng Y, Zeng X-l, et al.. Uncovering the features of nickel flows in China. Resources, Conservation and Recycling, 2023, 188: 106702, J]

[[3]] Lv W, Xin Y-t, Elliott R, et al.. Drying kinetics of a Philippine nickel laterite ore by microwave heating. Mineral Processing and Extractive Metallurgy Review, 2021, 42(1): 46-52, J]

[[4]] Meshram P, Abhilash, Pandey B D. Advanced review on extraction of nickel from primary and secondary sources. Mineral Processing and Extractive Metallurgy Review, 2019, 40(3): 157-193, J]

[[5]] Elliott R, Pickles C A, Peacey J. Ferronickel particle formation during the carbothermic reduction of a limonitic laterite ore. Minerals Engineering, 2017, 100: 166-176, J]

[[6]] Da Costa G M, Couto D J F, de Castro F P M. Existence of maghemite and trevorite in nickel laterites. Mineral Processing and Extractive Metallurgy Review, 2013, 34(5): 304-319, J]

[[7]] Quintero-coronel D A, Guillin-estrada W D, Echeverri-roman J L, et al.. Large- and particle-scale energy assessment of reduction roasting of nickel laterite ore for Ferronickel production via the rotary kiln-electric furnace process. Thermal Science and Engineering Progress, 2022, 32: 101331, J]

[[8]] Rao M-j, Li G-h, Jiang T, et al.. Carbothermic reduction of nickeliferous laterite ores for nickel pig iron production in China: A review. JOM, 2013, 65(11): 1573-1583, J]

[[9]] Zhu D-q, Xue Y-x, Pan J, et al.. An investigation into the distinctive sintering performance and consolidation mechanism of limonitic laterite ore. Powder Technology, 2020, 367: 616-631, J]

[[10]] Tu Y-k, Zhang Y-b, Su Z-j, et al.. Mineralization mechanism of limonitic laterite sinter under different fuel dosage: Effect of FeO. Powder Technology, 2022, 398: 117064, J]

[[11]] Zhu D-q, Xue Y-x, Pan J, et al.. Co-benefits of CO₂ emission reduction and sintering performance improvement of limonitic laterite via hot exhaust-gas recirculation sintering. Powder Technology, 2020, 373: 727-740, J]

[[12]] Xue Y-x, Zhu D-q, Pan J, et al.. Improving sintering performance of limonitic nickel laterite and reducing carbon emissions via the pellet-sintering process. JOM, 2022, 74(4): 1807-1817, J]

[[13]] Wang S, Jiang Y, Guo Y-f, et al.. Effects of basicity and Al₂O₃ content on viscosity and crystallization behavior of super-high-alumina slag. Crystals, 2022, 12(6): 851, J]

[[14]] Kumar V, Patil D, Mrunmaya K P, et al.. Impact of sinter basicity and alumina on softening melting behavior in blast furnace. Transactions of the Indian Institute of Metals, 2020, 73(2): 365-375, J]

[[15]] Zhang X-f, Jiang T, Xue X-x, et al.. Influence of MgO/Al₂O₃ ratio on viscosity of blast furnace slag with high Al₂O₃ content. Steel Research International, 2016, 87(1): 87-94, J]

[[16]] Yan Z, Lv X, Zhang J, et al.. Influence of MgO, Al₂O₃ and CaO/SiO₂ on the viscosity of blast furnace type slag with high Al₂O₃ and 5 wt% TiO₂. Canadian Metallurgical Quarterly, 2016, 55(2): 186-194, J]

[[17]] Murthy Y R, Tripathy S K, Kumar C R. Chrome ore beneficiation challenges & opportunities – A review. Minerals Engineering, 2011, 24(5): 375-380, J]

[[18]] Li S-n, Li J-l, Yu Y, et al.. Effect of Cr₂O₃ on physicochemical properties of CaO-SiO₂-Fe_tO slags during BOF smelting process of chromium-bearing iron. Metals, 2022, 12(7): 1110, J]

[[19]] Xue Y-x, Zhu D-q, Guo Z-q, et al.. Achieving efficient utilization of limonitic nickel laterite and CO₂ emission reduction through multi-force field sintering process. Journal of Iron and Steel Research International, 2022, 29(11): 1734-1747, J]

[[20]] Xue Y-x, Zhu D-q, Pan J, et al.. An investigation into the co-sintering process of limonitic nickel laterite and low-grade chromite via multi-force fields. Journal of Materials Research and Technology, 2021, 12(2): 1816-1831, J]

[[21]] Wright S, Zhang L, Sun S, et al.. Viscosity of a CaO-MgO-Al₂O₃-SiO₂ melt containing spinel particles at 1646 K. Metallurgical and Materials Transactions B, 2000, 31(1): 97-104, J]

[[22]] Nakamoto M, Kiyose A, Tanaka T, et al.. Evaluation of the surface tension of ternary silicate melts containing Al₂O₃, CaO, FeO, MgO or MnO. ISIJ International, 2007, 47(1): 38-43, J]

[[23]] Roscoe R. The viscosity of suspensions of rigid spheres. British Journal of Applied Physics, 1952, 3(8): 267-269, J]

[[24]] Hundermark R J, Nelson L R. Considerations for scale-up of ferronickel electric smelting furnaces. JOM, 2017, 69(2): 335-342, J]

[[25]] Bhaskar K L, Bhoi B. Iron and nickel enrichment in low grade chromite overburden to produce ferronickel alloys. Transactions of the Indian Institute of Metals, 2021, 74(6): 1321-1332, J]

[[26]] Bao J-w, Chu M-s, Liu Z-g, et al.. Evolution behavior and mechanism of iron carbon agglomerates under simulated blast furnace smelting conditions. Journal of Iron and Steel Research International, 2023, 30(9): 1714-1731, J]

[[27]] Park J G, Eom H S, Huh W W, et al.. A study in the thermodynamic behavior of nickel in the MgO-SiO₂-FeO slag system. Steel Research International, 2011, 82(4): 415-421, J]

[[28]] Chen Y-f, Lv X-m, Pang Z-d, et al.. Effect of basicity and Al₂O₃ on viscosity of ferronickel smelting slag. Journal of Iron and Steel Research International, 2020, 27(12): 1400-1406, J]

[[29]] Gan L, Lai C-bin. A general viscosity model for molten blast furnace slag. Metallurgical and Materials Transactions B, 2014, 45(3): 875-888, J]

[[30]] Shankar A, Görnerup M, Lahiri A K, et al.. Estimation of viscosity for blast furnace type slags. Ironmaking & Steelmaking, 2007, 34(6): 477-481, J]

[[31]] Yao L, Ren S, Wang X-q, et al.. Effect of Al₂O₃, MgO, and CaO/SiO₂ on viscosity of high alumina blast furnace slag. Steel Research International, 2016, 87(2): 241-249, J]