Events and reaction mechanisms during the synthesis of an Al₂O₃-TiB₂ nanocomposite via high energy ball milling

Abstract

An Al₂O₃-TiB₂ nanocomposite was successfully synthesized by the high energy ball milling of Al, B₂O₃ and TiO₂. The structures of the powdered particles formed at different milling times were evaluated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Thermodynamic calculations showed that the composite formed in two steps via highly exothermic mechanically induced self-sustaining reactions (MSRs). The composite started to form at milling times of 9–10 h but the reaction was not complete. The remaining starting materials were consumed by increasing the milling time to 15 h. The XRD patterns of the annealed powders showed that aluminum borate is one of the intermediate products and that it is consumed at higher temperatures. Heat treatment of the 6-h milled sample at 1100^°C led to a complete formation of the composite. Increasing the milling time to 15 h led to a refining of the crystallite sizes. A nanocomposite powder with a mean crystallite size of 35–40 nm was obtained after milling for 15 h.

Key words： ball milling; nanocomposite; Al₂O₃; TiB₂

Acknowledgements

The authors are grateful to the research affairs of Islamic Azad University, Saveh Branch for supporting this research.

References

1 Mayrhofer P H, Hörling A, Karlsson, Sjolen J, Mitterer C, Hultman L. Self-organized nanostructures in the Ti-Al-N system. Applied Physics Letters,2003, 83 (10): 2049–2051

2 Fahrenholtz W G, Hilmas G E, Talmy I G, Zaykoski J A.Oxidation of ultra-high temperature transition metal diboride ceramics.International Materials Reviews,2012, 57(1): 61–72

3 Volonakis G, Tsetseris L, Logothetids S. Electronic and structural properties of TiB2 bulk, surface, and nanoscale effects. Materials ScienceβandβEngineering, 2011, 176(6): 484–489

4 Hausner H H. Titanium Metallurgy, in Modern Materials, Advances in Development and Application. New York: Academic press, 1960, 225–325

5 Mollica S, Sood D K, Evans P J, Dytlewski N,Short K T. Ion beam analysis of aluminium ion implanted titanium diboride thin films. NuclearβInstruments andβMethodsβinβPhysics Research, 2002, 190(1-4): 736–741

6 Hag K Y, Yong L S, Kim H E. Oxidation behavior of titanium boride at elevated temperatures. Journal of the American Ceramic Society, 2001, 84(1): 239–241

7 Li L H, Kim H E, Kang E S. Sintering and mechanical properties of titanium diboride with aluminum nitride as a sintering aid. Journal of the European Ceramic Society, 2002, 22(6): 973–977

8 Liu G, Yan D, Zhang J. Microstructure and Mechanical Properties of Al₂O₃-TiB₂ Composites. Journal of Wuhan University of Technology, 2011, 26(4): 696–699

9 Meyers M A, Olevsky E A, Ma J, Jamet M. Combustion synthesis/densification of an Al₂O₃-TiB₂ composite. Materials Science and Engineering A, 2001, 311(1-2): 83–99

10 Merzhanov A G. History and recent development in SHS. Ceramics International, 1995, 21(5): 371–379

11 Zhu H E, Wang H Z, Ge L Q, Chen S, Wu S Q. Formation of composites fabricated by exothermic dispersion reaction in Al, B₂O₃ and TiO₂ system. Transactions of Nonferrous Metals Society of China, 2007, 17(3): 590–594

12 Sharifi M, Karimzadeh F, Enayati M H. Synthesis of titanium diboride reinforced alumina matrix nanocomposite by mechanochemical reaction of Al, B₂O₃ and TiO₂. Journal of Alloys and Compounds, 2010, 502(2): 508–512

13 Khaghani-Dehaghani M A, Ebrahimi-Kahrizsangi R, Setoudeh N, Nasiri-Tabrizi B. Mechanochemical synthesis of Al₂O₃-TiB₂ nanocomposite powder from Al, H₃BO₃ and TiO₂ mixture. Ref Met Hard Mat, 2011, 29(2): 244–249

14 Suryanarayana C, Ivanov E, Boldyrev V V. The science and technology of mechanical alloying. Materials Science and Engineering A, 2001, 304: 151–158

15 Surianarayana C. Recent developments in mechanical alloying. Reviews on Advanced Materials Science, 2011, 18(1): 203–211

16 Yadav T P, Yadav R M, Singh D P. Mechanical milling a top down approach for the synthesis of nanomaterials and nanocomposites. Journal forβNanoscienceβandβNanotechnology, 2012, 2(3): 22–48

17 Cullity B D. Elements of X-RAY Diffraction. New York: Addison-Wesely Publishing Company, 1956, 1234

18 Brandes E A, Brook G B. Smithells Metals Reference Book. London: Butterworth-Heinemann Ltd, 1992, 87–101

19 Takacs L. Self-sustaining reactions induced by ball milling. Progressβin MaterialsβScience, 2002, 47(4): 355–414

20 Takacs L, Balaz P, Torosyan AR. Ball milling-induced reduction of MoS₂ with Al. Journalβof MaterialsβScience, 2006, 41(21): 7033–7039

21 Mukhanov V A., Kurakevich O O, Solozhenko V L. On the hardness of boron (III) oxide. Journal ofβSuperhard Materials, 2008, 30(1): 71–72

22 Fajans K, Barbe S W. Properties and structures of vitreous and crystalline boron oxide. Journal of the American Chemical Society, 1952, 74(11): 2761–2768

23 Auerkari P. Mechanical and Physical Properties of Engineering Alumina Ceramics. Finland: VTT Technical Res Cen, 1996, 51–57

24 Wash R A. Electromechanical Design Handbook. New York: R R Donnelley & Sons Comp, 1999, 21–65

25 Alforda N M, Penn S J. Sintered alumina with low dielectric loss. Journal of Applied Physics, 1996, 80(10): 5895–5898

26 Ernest H N, Monte C N. Mineral reference manual. New York: Van Nostrand Reinhold, 1991,

27 Koch C C. Amorphization by mechanical alloying. Journal of Non-Crystalline Solids, 1990, 117-118(2): 670–678