Reaction and characterization of crosslinking hyperbranched poly (amine-ester) with succine anhydride

Reaction and characterization of crosslinking hyperbranched poly (amine-ester) with succine anhydride

Abstract

Basing on hydroxyl terminated hyperbranched poly (amine-ester)s (HPAEs), the cross-linking reactions and preparation of ester-crosslinked HPAE films were investigated using succine anhydride (SA) as crosslink reagent. It was proved that the cross-linking reaction between HPAE and SA followed a two-step mechanism. This mechanism provides an efficient route to prepare HPAE/SA cross-linked films, in which, the precursor films were prepared by casting HPAE/SA solution at a lower temperature, and then curing the films at a higher temperature. By varying SA content, the solid HPAE/SA films with different cross-linking degrees were prepared successfully. The highest tensile strength of the cross-linked film could reach 59.60 MPa. With all water contact angle smaller than 74.3°, the crosslinked films demonstrated good hydrophilic properties.